CN103755199A - 用于水泥和混凝土的工业废渣微粉激发剂及其使用方法 - Google Patents

用于水泥和混凝土的工业废渣微粉激发剂及其使用方法 Download PDF

Info

Publication number
CN103755199A
CN103755199A CN201310705965.6A CN201310705965A CN103755199A CN 103755199 A CN103755199 A CN 103755199A CN 201310705965 A CN201310705965 A CN 201310705965A CN 103755199 A CN103755199 A CN 103755199A
Authority
CN
China
Prior art keywords
exciting agent
cement
micro mist
concrete
residue micro
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310705965.6A
Other languages
English (en)
Inventor
陈广言
盛广宏
马孟臣
张芳
周晨辉
丁陈来
饶磊
张耀辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Magang Group Holding Co Ltd
Maanshan Iron and Steel Co Ltd
Original Assignee
Magang Group Holding Co Ltd
Maanshan Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Magang Group Holding Co Ltd, Maanshan Iron and Steel Co Ltd filed Critical Magang Group Holding Co Ltd
Priority to CN201310705965.6A priority Critical patent/CN103755199A/zh
Publication of CN103755199A publication Critical patent/CN103755199A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种用于水泥和混凝土的工业废渣微粉激发剂，按总质量分数100%计，由下列组分组成：有机胺1.2%～2.6%，可溶性钙盐40%～75%，硫酸盐19.8%～33%，尿素0～25%。将本发明激发剂混合粉磨后按重量百分比1～3%掺入工业废渣微粉中，可以提高掺工业废渣（如矿渣、粉煤灰）的水泥的3d强度15－30%，28d强度提高10－20%。

Description

用于水泥和混凝土的工业废渣微粉激发剂及其使用方法
技术领域
本发明属建材领域，尤其涉及用于水泥和混凝土的工业废渣微粉激发剂。
背景技术
很多工业固废的活性并不高，为了促进工业固废在水泥混凝土以及其他建材中的应用，提高其活性，增加其在水泥混凝土中的掺量非常有必要，因此可以通过掺加少量的活性激发剂来提高其潜在活性的发挥。现有的用于工业废渣的活性激发剂多数含有大量氯盐、碱，而氯盐对钢筋混凝土具有非常严重的危害性，限制了利用范围，因而在水泥的国家标准中对其含量进行了严格限制，而碱的存在也可能会产生碱集料反应而对混凝土的耐久性产生影响，因而碱的含量不宜太高。如CN201210017077.0公开的发明专利中使用的激发剂为纯碱、元明粉、泡花碱等，使用了大量的碱，CN201010575247中公开了一种用于提高早期强度的激发剂，其使用的主要是氯化钙。
发明内容
为克服现有技术的缺陷，本发明提供一种无氯且碱含量较低的用于水泥和混凝土的工业废渣微粉激发剂及其使用方法。
为解决上述技术问题，本发明提供一种用于水泥和混凝土的工业废渣微粉激发剂，按总质量分数100%计，由下列组分组成：有机胺1.2%～2.6%，可溶性钙盐40%～75%，硫酸盐19.8%～33%，尿素0～25%。
所述有机胺为三乙醇胺、二乙二胺、三聚腈胺、三异丙醇胺中的一种或二种的混合。
所述可溶性钙盐为无水硝酸钙或甲酸钙中的一种或二种混合。
所述硫酸盐为硫酸钠或硫酸钾或硫铝酸钾，优选硫酸钠。
本发明还提供一种用于水泥和混凝土的工业废渣微粉激发剂的使用方法，将上述的用于水泥和混凝土的工业废渣微粉激发剂混合粉磨后按重量百分比1～3%掺入工业废渣微粉中（所述激发剂与工业废渣微粉的比例为1-3:100），以提高其活性。
通过掺加本发明激发剂可以提高掺工业废渣（如矿渣、粉煤灰）的水泥的3d强度15－30%，28d强度提高10－20%。
具体实施方式
通过掺加本发明激发剂可以显著提高废渣的早期和后期强度，具体例如下：
实例1：
组分及比例：三乙醇胺1.2%，无水硝酸钙59%，尿素20%，硫酸钠19.8%。
上述组分按比例进行充分混合粉磨至80um筛余小于20%，制备得到本发明激发剂，掺入矿粉、粉煤灰中1.0%，可以提高3d强度15～30%，28d强度可以提高10～20%。
实例2：
组分及比例：三乙醇胺2.6%，硝酸钙65%，硫酸钠32.4%。
上述组分按比例进行充分混合粉磨至80um筛余小于20%，制备得到本发明激发剂，掺入矿粉、粉煤灰中1.5%，可以提高3d强度20～30%，28d强度可以提高10～20%。
实例3：
组分及比例：三聚腈胺2%，硝酸钙73.5%，硫酸钠，24.5%。
上述组分按比例进行充分混合粉磨至80um筛余小于20%，制备得到本发明激发剂，掺入矿粉、粉煤灰中2.5%，可以提高3d强度20～30%，28d强度可以提高10～20%。
实例4：
组分及比例：三聚腈胺2.6%，甲酸钙65%，硫酸钠32.4%。
上述组分按比例进行充分混合粉磨至80um筛余小于20%，制备得到本发明激发剂，掺入矿粉、粉煤灰中2.5%，可以提高3d强度20～30%，28d强度可以提高10～20%。
实例5：
组分及比例：三乙醇胺2.4%，甲酸钙65%，硫酸钠，32.6%
上述组分按比例进行充分混合粉磨至80um筛余小于20%，制备得到本发明激发剂，掺入矿粉、粉煤灰中3%，可以提高3d强度20～30%，28d强度可以提高10～20%。

Claims (6)

1.一种用于水泥和混凝土的工业废渣微粉激发剂，其特征在于，按总质量分数100%计，由下列组分组成：有机胺1.2%～2.6%，可溶性钙盐40%～75%，硫酸盐19.8%～33%，尿素0～25%。
2.如权利要求1所述的用于水泥和混凝土的工业废渣微粉激发剂，其特征在于，所述有机胺为三乙醇胺、二乙二胺、三聚腈胺、三异丙醇胺中的一种或二种的混合。
3.如权利要求1所述的用于水泥和混凝土的工业废渣微粉激发剂，其特征在于，所述可溶性钙盐为无水硝酸钙或甲酸钙中的一种或二种混合。
4.如权利要求1所述的用于水泥和混凝土的工业废渣微粉激发剂，其特征在于，所述硫酸盐为硫酸钠或硫酸钾或硫铝酸钾。
5.如权利要求4所述的用于水泥和混凝土的工业废渣微粉激发剂，其特征在于，所述硫酸盐为硫酸钠。
6.一种用于水泥和混凝土的工业废渣微粉激发剂的使用方法，其特征在于，将权利要求1所述的用于水泥和混凝土的工业废渣微粉激发剂混合粉磨后按重量百分比1～3%掺入工业废渣微粉中，以提高其活性。
CN201310705965.6A 2013-12-19 2013-12-19 用于水泥和混凝土的工业废渣微粉激发剂及其使用方法 Pending CN103755199A (zh)