CN103740339A - 堵漏填充剂 - Google Patents

堵漏填充剂 Download PDF

Info

Publication number
CN103740339A
CN103740339A CN201310748437.9A CN201310748437A CN103740339A CN 103740339 A CN103740339 A CN 103740339A CN 201310748437 A CN201310748437 A CN 201310748437A CN 103740339 A CN103740339 A CN 103740339A
Authority
CN
China
Prior art keywords
parts
plugging
powder
content
leak stopping
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310748437.9A
Other languages
English (en)
Inventor
隋跃华
关芳
刘光法
曹树生
郭京华
肖新磊
赵忠亮
丁海峰
杨军义
唐东
杨兴福
方国俊
卢康华
高峰
刘振娜
刘密密
张晓军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGYING TAIER PETROLEUM TECHNOLOGY Co Ltd
Original Assignee
DONGYING TAIER PETROLEUM TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGYING TAIER PETROLEUM TECHNOLOGY Co Ltd filed Critical DONGYING TAIER PETROLEUM TECHNOLOGY Co Ltd
Priority to CN201310748437.9A priority Critical patent/CN103740339A/zh
Publication of CN103740339A publication Critical patent/CN103740339A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种TRS-DFJC型填充剂，其组成及含量为重量份：石英粉10-15；硅酸钙10-20；油溶树脂15-25；淀粉1-3；橡胶粒20-30；沥青粉10-15；碳酸钙20-30；生物聚合物0.1-0.3；上述物质按其组份及含量，常温常压下，以常规配制方法依次加入溶器中，混合搅拌均匀，待其干燥，粉碎成0.05mm–0.8mm的颗粒状制品。本发明具有原料来源广泛，工艺科学简单、施工安全、填充效果好、封堵率高、堵漏成功率高的特点，广泛在石油、地质钻探工艺中应用，特别适应在裂缝性硬地层及溶洞型地层中应用。

Description

堵漏填充剂
技术领域
本发明涉及钻井堵漏剂，特别涉及一种堵漏填充剂。
背景技术
　   石油钻井中采用的常规堵漏剂,一般采用核桃壳、贝壳粉、云母、谷壳等作为堵漏填充剂，这些堵漏填充剂为石油钻井作业发挥了作用，但同时存在着如下缺点或不足：①填充剂完全靠物理填充进行封堵，填充效果差，没有凝结性；②这些填充剂用量大，容易封口，当填充剂量少时起不到填充作用，在漏失裂缝通道不易滞留；量大时难以配浆，流动性差，在漏失裂缝通道内极易封口，填充封堵效果差，不能进入漏层深部；③加大填充剂的量时，堵漏浆有时虽然进入裂缝及通道深部，但因堵漏浆不具有凝结性，当开泵循环压力激动时又发生复漏，造成反复堵漏，堵漏效果差；④堵漏材料耗费量大，堵漏时间长，堵漏费用高；⑤填充剂性能单一，靠物理堵塞，易发生重复漏失；⑥这些填充剂复配应用对付渗透性漏失有微小的封堵效果，堵漏施工易堵泵，不好上水，易损坏泵件，导致不能连续施工，达不到堵漏效果，极易造成井下事故。
发明内容
本发明的目的是提供一种堵漏填充剂，采用不同粒径、不同性能的多种材料组合，具有良好的流动性和可泵性，悬浮携带能力强，进入漏失通道中，易滞流，经过井下温度压力作用后填充封堵效果好，具有一定的凝结性，施工安全快速，可复配在不同性能的堵漏配方中应用。有效地克服或避免上述现有技术中存在的缺点或不足。
本发明所述的堵漏填充剂 ，其组成及含量，含量为重量份：
石英粉10-15；硅酸钙10-20；油溶树脂  15-25；淀粉 1-3；橡胶粒 20-30；沥青粉10-15；碳酸钙  20-30；生物聚合物  0.1-0.3； 
配制方法：将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入溶器中，混合搅拌均匀，待其干燥，粉碎或过筛成粒径为0.05mm – 0.8mm的粉末状制品。
其中，所述XC生物聚合物为钻井液用黄原胶。  
本发明与现有桥堵剂相比较具有如下优点或有益效果：
1、具有很好的填充能力，既有物理填充作用又有化学凝结作用，填充封堵能力强；
2、进入不同类型裂缝、孔隙中有很好的滞流特性，具有很强的填充支撑能力；
3、悬浮携带能力强，易进入不同类型的裂缝、孔隙及通道中，填充能力强，封堵成功率高。
4、具有很好的流动性能易泵入，对泵件无损害，可连续施工，达到填充封堵目的。
5、配伍性能好，可与其他堵漏剂相匹配，可提高堵漏浆的协同效应。
6、使用范围广，可适用在裂缝、孔隙地层及灰岩、泥岩、砂岩、泥砂岩煤层等地层，有显著的填充封堵堵漏效果。
7、无毒、对环境无污染， 施工快速操作安全，不会造成井下复杂事故。
具体实施方式
一种堵漏填充剂，其组成及含量，含量为重量份：石英10-15；硅酸钙  10-20；油溶树脂15-25；淀粉1-3；橡胶粒20-30；沥青粉10-15；碳酸钙20-30；生物聚合物0.1-0.3。            
配制方法：将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入溶器中，混合搅拌均匀，待其干燥，粉碎或过筛成粒径为0.05mm – 0.8mm的粉末状制品。XC生物聚合物为钻井液用黄原胶。
使用时，在堵漏钻井液中加入堵漏钻井液总量的2%-15%本发明的堵漏填充剂。
下面给出具体实施例：
第1例
石英粉10；硅酸钙10；油溶树脂 15；淀粉 1；橡胶粒 20；沥青粉10；碳酸钙  20；XC生物聚合物  0.1。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入溶器中，混合搅拌均匀，待其干燥，粉碎或过筛成粒径为0.05mm – 0.8mm的粉末状制品。XC生物聚合物为钻井液用黄原胶。
使用时，在堵漏钻井液中加入堵漏钻井液总量2%的本发明的堵漏填充剂。
第2 例
石英粉12；硅酸钙14；油溶树脂  18；淀粉 1.5；橡胶粒 24；沥青粉12；碳酸钙  24；XC生物聚合物  0.15。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入溶器中，混合搅拌均匀，待其干燥，粉碎或过筛成粒径为0.05mm – 0.8mm的粉末状制品。XC生物聚合物为钻井液用黄原胶。
使用时，在堵漏钻井液中加入堵漏钻井液总量8%的本发明的堵漏填充剂。
第3例
石英粉15；硅酸钙20；油溶树脂25；淀粉3；橡胶粒30；沥青粉15；碳酸钙30；XC生物聚合物0.3。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入溶器中，混合搅拌均匀，待其干燥，粉碎或过筛成粒径为0.05mm – 0.8mm的粉末状制品。XC生物聚合物为钻井液用黄原胶。
使用时，在堵漏钻井液中加入堵漏钻井液总量15%的本发明的堵漏填充剂。
第4例
石英粉14；硅酸钙18；油溶树脂 22；淀粉 2；橡胶粒 26；沥青粉14；碳酸钙26；XC生物聚合物  0.2。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入溶器中，混合搅拌均匀，待其干燥，粉碎或过筛成粒径为0.05mm – 0.8mm的粉末状制品。XC生物聚合物为钻井液用黄原胶。
使用时，在堵漏钻井液中加入堵漏钻井液总量12%的本发明的堵漏填充剂。
第1例、第2例、第3例为实施例，第4例为比较例，在现场使用中具有很好的堵漏效果。

Claims (2)

1.一种堵漏填充剂，其组成及含量，含量为重量份： 
石英粉                                 10-15；
硅酸钙                                 10-20；
油溶树脂                              15-25；
淀粉                                   1-3；
橡胶粒                                 20-30
沥青粉                                10-15
碳酸钙                                20-30
XC生物聚合物                          0.1-0.3
配制方法：将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入溶器中，混合搅拌均匀，待其干燥，粉碎或过筛成粒径为0.05mm – 0.8mm的粉末状制品。
2.根据权利要求1所述的堵漏填充剂，其特征在于所述XC生物聚合物为钻井液用黄原胶。
CN201310748437.9A 2013-12-31 2013-12-31 堵漏填充剂 Pending CN103740339A (zh)