CN103740346B - 堵漏增韧剂 - Google Patents

堵漏增韧剂 Download PDF

Info

Publication number
CN103740346B
CN103740346B CN201310748439.8A CN201310748439A CN103740346B CN 103740346 B CN103740346 B CN 103740346B CN 201310748439 A CN201310748439 A CN 201310748439A CN 103740346 B CN103740346 B CN 103740346B
Authority
CN
China
Prior art keywords
leak stopping
content
toughner
component
high polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310748439.8A
Other languages
English (en)
Other versions
CN103740346A (zh
Inventor
隋跃华
关芳
张建阔
韩立国
罗剑波
张景红
唐东
张延喜
张伟
王希玲
韩博
张晓军
李强
张振红
孔得峰
刘洋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGYING TAIER PETROLEUM TECHNOLOGY Co Ltd
Original Assignee
DONGYING TAIER PETROLEUM TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGYING TAIER PETROLEUM TECHNOLOGY Co Ltd filed Critical DONGYING TAIER PETROLEUM TECHNOLOGY Co Ltd
Priority to CN201310748439.8A priority Critical patent/CN103740346B/zh
Publication of CN103740346A publication Critical patent/CN103740346A/zh
Application granted granted Critical
Publication of CN103740346B publication Critical patent/CN103740346B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种堵漏增韧剂，其组份及含量，含量为重量份：聚丙烯纤维5-12、橡胶颗粒20-30、高分子聚丙烯酰胺1-5、增韧尼龙2-8、石棉段2-8、植物纤维5-12、氢氧化钙4-7、聚阴离子纤维素PAC-HV0.1-0.4。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入捏合机中，混合搅拌均匀，粉碎成0.05mm-1mm的颗粒状制品。本发明具有原料来源广泛、无毒无污染、施工工艺简便、流变性能好、成柱性能好、韧性强不易脆性脱落，堵漏后起下钻过程中不易破裂和脆性裂缝，堵漏成功率高等特点，广泛在石油、地质钻探中低压破碎地层、大裂缝、大溶洞、地下河、以及严重亏空地层的承压堵漏工程中应用。

Description

堵漏增韧剂
技术领域
本发明涉及钻井堵漏增韧剂，特别涉及一种堵漏增韧剂。
背景技术
石油钻井中，大型恶性井漏如：大裂缝、大溶洞、地层放空、地下暗河、地层严重亏空等复杂地层以及破碎薄弱地层时，一般使用核桃壳、锯末、聚合物堵漏剂、非渗透封堵剂、凝胶等材料作为堵漏增韧剂，上述物质在一般情况下能起堵漏作用，但其存在着如下的缺点和不足：①脆性高韧性差,抗压强度低,堵漏稳定性差；②堵漏后柱塞易脆性脱落，极易造成井下复杂情况及卡钻事故；③堵漏效果不明显,而且消耗大量堵漏材料及堵漏时间长；③大裂缝、大溶洞地层、严重亏空地层难以解决封堵后与井壁胶结性能；④破碎地层堵漏后地层与堵漏剂胶结无韧性，多次反复堵漏的现象时有发生，堵漏效果差，影响钻探速度。
发明内容
本发明的目的是提供一种堵漏增韧剂，采用聚丙烯纤维、橡胶颗粒、高分子聚丙烯酰、氧化钙等多种具有粘弹性的颗粒材料，组合配制成堵漏增韧剂，该增韧剂与其它桥堵剂配合，在地层漏失通道中形成网状结构,从而形成封堵漏失通道的基本骨架,堵漏增韧剂中的粗颗粒在通过网状结构时产生“架桥”,“架桥”后,漏失通道由大变小,由小变微,形成有效堆积,堵住漏失通道，从而形成韧性强的凝固体，有效地克服或避免上述现有技术中存在的缺点或不足。
本发明所述的堵漏增韧剂，其组份及含量，含量为重量份：
聚丙烯纤维5-12、橡胶颗粒20-30、高分子聚丙烯酰胺1-5、增韧尼龙2-8、塑料小球2-5、石棉段2-8、植物纤维5-12、氢氧化钙4-7；聚阴离子纤维素PAC-HV0.1-0.4。
配制方法：上述物质按其组份及含量，常温常压下，以常规配制方法依次加入捏合机中，混合搅拌均匀，粉碎成0.05mm-1mm的颗粒状制品。
其中，所述橡胶颗粒的粒径为0.1mm-1mm。所述高分子聚丙烯酰胺的分子量为1200万—2000万。所述植物纤维为10-200目的玉米秸秆。
1、具有很好的增韧性能，可显著提高堵漏浆的抗折强度，
2、可避免堵漏后形成物的脆性变形，增加其抗压强度和抗拉强度。
3、在堵漏浆中，可提高网状结构及连接性，从而提高破碎、薄弱地层及大裂缝、大通道漏失地层的承压连接韧性能力。
4.在不同堵漏体系中，易与系列堵漏剂形成纤维网架桥，达到滞留、拉筋、堆积、填充、加固的目的，具有很好的增韧封堵效果
5、施工安全，极易泵入，堵漏成功率高
6、无毒、无污染，特别适合不同压力地层、大裂缝、大溶洞、地下河、严重亏空地层以及碎地层的承压堵漏施工。
具体实施方式
一种堵漏增韧剂，其组份及含量，含量为重量份：
聚丙烯纤维5-12、橡胶颗粒20-30、高分子聚丙烯酰胺1-5、增韧尼龙2-8、塑料小球2-5、石棉段2-8、植物纤维5-12、氢氧化钙4-7；聚阴离子纤维素PAC-HV0.1-0.4。
配制方法：上述物质按其组份及含量，常温常压下，以常规配制方法依次加入捏合机中，混合搅拌均匀，粉碎成0.05mm-1mm的颗粒状制品。橡胶颗粒的粒径为0.1mm-1mm。高分子聚丙烯酰胺的分子量为1200万—2000万。植物纤维为10-200目的玉米秸秆。
使用时，在堵漏钻井液中加入堵漏钻井液总量2﹪-15﹪的本发明的堵漏增韧剂。
下面给出具体实施例：
第1例
聚丙烯纤维5、橡胶颗粒20、高分子聚丙烯酰胺1、增韧尼龙2、石棉段2、植物纤维5、氢氧化钙4；聚阴离子纤维素PAC-HV0.1。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入捏合机中，混合搅拌均匀，粉碎成0.05mm的颗粒状制品。橡胶颗粒的粒径为0.1mm。高分子聚丙烯酰胺的分子量为1200万。植物纤维为10目的玉米秸秆。
在堵漏钻井液中加入堵漏钻井液总量2﹪的本发明的堵漏增韧剂。
第2例
聚丙烯纤维7、橡胶颗粒23、高分子聚丙烯酰胺2、增韧尼龙4、石棉段4、植物纤维7；氢氧化钙5；聚阴离子纤维素PAC-HV0.2。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入捏合机中，混合搅拌均匀，粉碎成0.08mm的颗粒状制品。橡胶颗粒的粒径为0.6mm。高分子聚丙烯酰胺的分子量为1500万。植物纤维为120目的玉米秸秆。
使用时，在堵漏钻井液中加入堵漏钻井液总量总量8﹪的本发明的堵漏增韧剂。
第3例
聚丙烯纤维12、橡胶颗粒30、高分子聚丙烯酰胺5、增韧尼龙8、塑料小球5、石棉段8、植物纤维12；氢氧化钙7；聚阴离子纤维素PAC-HV0.4。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入捏合机中，混合搅拌均匀，粉碎成0.08mm的颗粒状制品。橡胶颗粒的粒径为0.6mm。高分子聚丙烯酰胺的分子量为2000万。植物纤维为200目的玉米秸秆。使用时，在堵漏钻井液中加入堵漏钻井液总量15﹪的本发明的堵漏增韧剂。
第4例
聚丙烯纤维10、橡胶颗粒26、高分子聚丙烯酰胺4、增韧尼龙6、塑料小球4、石棉段6、植物纤维10；氢氧化钙6；聚阴离子纤维素PAC-HV0.3。将上述物质按其组份及含量，常温常压下，以常规配制方法依次加入捏合机中，混合搅拌均匀，粉碎成0.5mm的颗粒状制品。橡胶颗粒的粒径为0.5mm。高分子聚丙烯酰胺的分子量为1800万。植物纤维为100目的玉米秸秆。
使用时，在堵漏钻井液中加入堵漏钻井液总量12﹪的本发明的堵漏增韧剂。
第1例、第2例、第3例为实施例，第4例为比较例，在现场试用中具有很好的堵漏效果。

Claims (1)

1.一种堵漏增韧剂，其组份及含量，含量为重量份：
聚丙烯纤维5-12
橡胶颗粒20-30
高分子聚丙烯酰胺1-5
增韧尼龙2-8
石棉段2-8
植物纤维5-12
氢氧化钙4-7
聚阴离子纤维素PAC-HV0.1-0.4；
所述橡胶颗粒的粒径为0.1mm-1mm；所述高分子聚丙烯酰胺的分子量为1200万—2000万；所述植物纤维为10-200目的玉米秸秆；
配制方法：上述物质按其组份及含量，常温常压下，以常规配制方法依次加入捏合机中，混合搅拌均匀，粉碎成0.05mm-1mm的颗粒状制品。
CN201310748439.8A 2013-12-31 2013-12-31 堵漏增韧剂 Active CN103740346B (zh)