CN103740185A - 一种新型无规共聚聚丙烯涂覆料 - Google Patents
一种新型无规共聚聚丙烯涂覆料 Download PDFInfo
- Publication number
- CN103740185A CN103740185A CN201410016952.2A CN201410016952A CN103740185A CN 103740185 A CN103740185 A CN 103740185A CN 201410016952 A CN201410016952 A CN 201410016952A CN 103740185 A CN103740185 A CN 103740185A
- Authority
- CN
- China
- Prior art keywords
- coating material
- atactic copolymerized
- copolymerized polypropene
- masterbatch
- novel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种新型无规共聚聚丙烯涂覆料,其原料组分包括母料和辅料,辅料的质量为母料质量的10%~20%;母料包括质量比为2-3的无规共聚聚丙烯和均聚聚丙烯;辅料包括线性低密度聚乙烯和高压低密度聚乙烯。本发明新型无规共聚聚丙烯涂覆料通过选择均聚和共聚两种高熔指母料及适合的聚乙烯辅料进行混配,加工出了环保(无需使用化学降解剂)、机械性能高(如剥离强度、冲击强度)、制备简易的涂覆料;同时,使用该种方法制备的涂膜的外观漂亮,晶莹剔透。
Description
技术领域
本发明涉及一种新型无规共聚聚丙烯涂覆料。
背景技术
编织袋/纸塑袋/薄膜符合用涂覆级聚丙烯,是通过挤出涂覆机均匀的涂覆在包装袋/膜内外侧的关键材料,该层涂膜能够起到粘结及防潮、防水的作用。涂覆后的包装袋/膜,其使用性能和外观会大大提高。国内目前涂覆料多使用在普通化学原料包装袋、水泥编织袋、日用生活品包装袋(如洗衣粉袋、大米袋等)以及高档印花编织布上。
目前,生产涂覆料技术以降解法为主。降解法制备涂覆料是将降解剂掺混在低熔指(多为2~3g/10min)均聚粉料里,再通过螺杆挤出机熔融造粒,造粒后的原料熔指高达30~40g/10min,甚至更高。化学降解的目的是为了提高熔指,提升流动性,使分子量分布变窄,满足涂覆机牵引转动时挤出膜的机械性能。造粒后,一般还要掺混一定比例的高压低密度聚乙烯(LDPE)和其他粘性树脂(如松脂),有的还以接枝马来酸酐等粘性物来增加粘结性,以增加剥离强度。其掺混比例视涂覆机机头温度而定,一般温度越高掺混量越多。此种方法制备的涂覆料能满足大多数情况下的使用。但由于使用了化学降解剂,存在气味大且涂覆时易破膜和与基材的粘结性较差、易脱膜的缺点;且增加LDPE的量又会增加成本。
发明内容
本发明的目的是提供一种新型无规共聚聚丙烯涂覆料。
为解决上述技术问题,本发明所采用的技术方案如下:
一种新型无规共聚聚丙烯涂覆料,其原料组分包括母料和辅料,辅料的质量为母料质量的10%~20%;母料包括质量比为2-3的无规共聚聚丙烯和均聚聚丙烯;辅料包括线性低密度聚乙烯和高压低密度聚乙烯。
上述涂覆料通过选择均聚和共聚两种母料及适合的聚乙烯辅料进行混配,加工出了环保、机械性能高(如剥离强度、冲击强度)的涂覆料,且降低了成本。
上述涂覆料整体分子量分布窄,提高了流动性和减少了涂膜颈缩现象。辅料的选择能够协调整体分子量分布,增强了膜的强度和剥离力,制备时,用简单的物理掺混的方法使涂覆料整体分子量变窄,避免了复杂的化学降解带来的问题,上述各母料和辅料的混合使用产生了意想不到的协同效应。使用时,只要将各组分混匀、熔融挤出涂覆即可。
线性低密度聚乙烯和高压低密度聚乙烯的质量比为1.5~2.5。这样可进一步提高涂覆料的均匀性、粘结性和机械性能,同时提高所得涂覆料的亮度。
无规共聚聚丙烯粉料的熔指为35±5g/10min;均聚聚丙烯粉料的熔指为45±5g/10min。这样可进一步保证涂覆料的机械强度。
无规共聚聚丙烯中含有质量含量为无规共聚聚丙烯总质量的3~5%的乙烯。上述由于有3~5%的乙烯分子无规的键合在聚丙烯大分子链上,使得共聚聚丙烯的粘性提高,耐冲击性提高,成本降低,无规共聚聚丙烯的制备可参照申请号为200810196008的中国专利申请。均聚聚丙烯为间歇式均聚聚丙烯生产工艺。上述技术方案弥补了目前没有共聚涂覆料产品的空白。
上述新型无规共聚聚丙烯涂覆料,其原料组分还包括抗氧剂1010、抗氧剂168和硬脂酸钙,抗氧剂1010的质量含量为母料和辅料质量和的2~5‰;抗氧剂168的质量含量为母料和辅料质量和的2~5‰;硬脂酸钙的质量含量为母料和辅料质量和的2~5‰。
抗氧剂1010、抗氧剂168和硬脂酸钙掺混在造粒前的无规共聚聚丙烯中。
无规共聚聚丙烯在造粒前在粉料里分别掺混上述比例的助剂抗氧剂1010,抗氧剂168及硬脂酸钙,加入捏合锅,经过在捏合锅里捏合3分钟左右,再放料至锥形锅,经过锥形锅搅拌15分钟,出料包装。均聚聚丙烯无需掺混助剂。这样保证造粒时无规共聚聚丙烯的降解可以忽略。均聚聚丙烯经过造粒后大幅度的降解,分子量分布变窄,与无规共聚聚丙烯掺混后有效补充无规共聚聚丙烯的分子量分布宽的问题,提高了涂膜的整体流动性。
造粒后,无规共聚聚丙烯粒料的熔指为35±5g/10min;均聚聚丙烯粒料的熔指为125±5g/10min。
在生产母料时按照要求投料,上述未提及的工艺参照现有技术;在造粒时,控制好各段螺杆温度。
无规共聚聚丙烯造粒和均聚聚丙烯造粒时,螺杆挤出机进料段的温度为170-190℃,混炼段的温度为210-230℃,压力段的温度为205-215℃,出料段的温度为180-190℃。
本发明未提及的技术均为现有技术。
本发明新型无规共聚聚丙烯涂覆料通过选择均聚和共聚两种高熔指母料及适合的聚乙烯辅料进行混配,加工出了环保(无需使用化学降解剂)、机械性能高(如剥离强度、冲击强度)、制备方法简单易操作的涂覆料;同时,使用该种方法制备的涂膜的外观漂亮,晶莹剔透。
具体实施方式
为了更好地理解本发明,下面结合实施例进一步阐明本发明的内容,但本发明的内容不仅仅局限于下面的实施例。
实施例1
(1)母料A粉料,为金陵塑胶化工有限公司间歇式无规共聚聚丙烯,牌号:R300;
母料B粉料,牌号为金陵塑胶化工有限公司间歇式聚丙烯,牌号:450。
(2)母料A掺混助剂量:
抗氧剂1010:3‰;抗氧剂168:3‰;硬脂酸钙:4‰,用量为相对母料和辅料质量和的千分比。
母料A粒料的制备:在粉料里分别掺混上述比例的助剂抗氧剂1010,抗氧剂168及硬脂酸钙,加入捏合锅,经过在捏合锅里捏合3分钟左右,再放料至锥形锅,经过锥形锅搅拌15分钟,出料造粒。母料B粒料的制备为由母料B粉料直接造粒,即得。
(3)母料A和母料B造粒时,65机螺杆各段温度℃均为:
一区 二区 三区 四区 五区 六区 七区 八区 九区
170 190 210 220 225 215 205 190 180
(4)母料A粒料熔指:35±5g/10min母料B粒料熔指:125±5g/10min
(5)新型无规共聚聚丙烯涂覆料的配比如下:
母料A(粒料):100kg 母料B(粒料):35kg
线型聚乙烯7042(粒料):10kg 高压聚乙烯1C7A(粒料):5kg
新型无规共聚聚丙烯涂覆料使用时,将各物料混匀、熔融挤出涂覆即可,实施例中未提到的技术均参照现有技术即可。
上述实施例中所得涂覆料检测性能如表1:
表1
Claims (7)
1.一种新型无规共聚聚丙烯涂覆料,其特征在于:其原料组分包括母料和辅料,辅料的质量为母料质量的10%~20%;母料包括质量比为2-3的无规共聚聚丙烯和均聚聚丙烯;辅料包括线性低密度聚乙烯和高压低密度聚乙烯。
2.如权利要求1所述的新型无规共聚聚丙烯涂覆料,其特征在于:线性低密度聚乙烯和高压低密度聚乙烯的质量比为1.5~2.5。
3.如权利要求1或2所述的新型无规共聚聚丙烯涂覆料,其特征在于:无规共聚聚丙烯粉料的熔指为35±5g/10min;均聚聚丙烯粉料的熔指为45±5g/10min。
4.如权利要求1或2所述的新型无规共聚聚丙烯涂覆料,其特征在于:无规共聚聚丙烯中含有质量含量为无规共聚聚丙烯总质量的3~5%的乙烯。
5.如权利要求1或2所述的新型无规共聚聚丙烯涂覆料,其特征在于:其原料组分还包括抗氧剂1010、抗氧剂168和硬脂酸钙,抗氧剂1010的质量含量为母料和辅料质量和的2~5‰;抗氧剂168的质量含量为母料和辅料质量和的2~5‰;硬脂酸钙的质量含量为母料和辅料质量和的2~5‰。
6.如权利要求5所述的新型无规共聚聚丙烯涂覆料,其特征在于:抗氧剂1010、抗氧剂168和硬脂酸钙掺混在造粒前的无规共聚聚丙烯中。
7.如权利要求6所述的新型无规共聚聚丙烯涂覆料,其特征在于:无规共聚聚丙烯造粒和均聚聚丙烯造粒时,螺杆挤出机进料段的温度为170-190℃,混炼段的温度为210-230℃,压力段的温度为205-215℃,出料段的温度为180-190℃。