CN103740076A - 一种高光泽无卤阻燃pc/abs合金材料及其制备方法 - Google Patents

一种高光泽无卤阻燃pc/abs合金材料及其制备方法 Download PDF

Info

Publication number
CN103740076A
CN103740076A CN201310733811.8A CN201310733811A CN103740076A CN 103740076 A CN103740076 A CN 103740076A CN 201310733811 A CN201310733811 A CN 201310733811A CN 103740076 A CN103740076 A CN 103740076A
Authority
CN
China
Prior art keywords
free flame
halogen
alloy material
flame retardant
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310733811.8A
Other languages
English (en)
Inventor
赵成方
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO DADU NEW MATERIAL SCIENCE & TECHNOLOGY Co Ltd
Original Assignee
QINGDAO DADU NEW MATERIAL SCIENCE & TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO DADU NEW MATERIAL SCIENCE & TECHNOLOGY Co Ltd filed Critical QINGDAO DADU NEW MATERIAL SCIENCE & TECHNOLOGY Co Ltd
Priority to CN201310733811.8A priority Critical patent/CN103740076A/zh
Publication of CN103740076A publication Critical patent/CN103740076A/zh
Pending legal-status Critical Current

Abstract

本发明涉及塑料改性技术领域，特别是涉及一种高光泽无卤阻燃PC/ABS合金材料及其制备方法；该材料主要由如下质量份的组分组成：PC树脂65～80，ABS树脂10-20，相容剂3-8，无卤阻燃剂5-15，抗滴落剂0.1-0.3；该材料的制备方法包括混合、挤出、造粒步骤；本发明提供的材料具有外观好、使用安全的性能，能够广泛应用于家电领域。

Description

一种高光泽无卤阻燃PC/ABS合金材料及其制备方法
技术领域
本发明涉及塑料改性技术领域，特别是涉及一种高光泽无卤阻燃PC/ABS合金材料及其制备方法。
背景技术
    目前，人们对高光泽塑料产品的要求主要集中在外观感好、质轻等特点，但随着经济的发展以及人们对防火安全意识的提高，对塑料产品的阻燃性能和使用成本的要求越来越高。随着消费者个性化需求的日益提高，以及降低系统成本的迫切要求，电子电器行业的生产厂商面临着严峻的挑战：家电所等所用材料不仅要更加环保，而且材料在安全性和加工性能等方面应该符合更严苛的应用标准。
    阻燃改性大多采用卤系阻燃剂与锑化合物的协效系统，材料在燃烧或热裂解（甚至高温加工）时形成有毒化合物，腐蚀性气体和大量烟尘，对人体和环境危害很大。2006年7月1日，欧盟《关于在电气电子设备中限制使用某些有害物质指令》正式生效，规定部分含溴阻燃剂不能使用在工程塑料的产品上。低碳、环保”理念已经深入人心，越来越多的消费者在选择使用无卤素电子产品。无毒、环保、无卤阻燃逐渐替代有卤阻燃成为国际上阻燃产品发展的方向，成为各国开发的重点。目前，中国工业上所用的阻燃产品近80%为含卤阻燃。中国必须大力发展无卤阻燃产品才能适应国际市场的发展趋势。
发明内容
     为解决上述问题，本发明的目的在于提供一种高光泽无卤阻燃PC/ABS合金材料，使其具有外观好、使用安全的性能，能够广泛应用于家电领域；本发明的另一目的在于提供该材料的制备方法。
 本发明的技术方案为：一种高光泽无卤阻燃PC/ABS合金材料，主要由如下质量份的组分组成：PC树脂 65～80，ABS树脂 10-20，相容剂3-8，无卤阻燃剂 5-15，抗滴落剂 0.1-0.3。
优化的，还包括抗氧剂 0.1～0.5， 润滑剂 0.1～0.5。
优化的，所述阻燃剂采用缩聚型无卤磷酸酯阻燃剂。
本发明提供的上述任意一种高光泽无卤阻燃PC/ABS合金材料的制备方法，包括如下步骤：首先将各组分按照质量份用高速搅拌机搅拌混匀，然后转入双螺杆挤出机中熔融挤出，冷却，最后造粒即可制得产品。
优化的，原料在高速搅拌机中搅拌5-10min。
优化的，最后经造粒制得圆柱状颗粒产品。
优化的，挤出时双螺杆挤出机的料筒温度为：后段200-210℃，中段210-220℃，前段220-225℃，机头温度225-230℃。
    本发明的高光无卤阻燃PC/ABS合金材料具有良好的流动性、韧性、刚性三高平衡性，阻燃达到UL-94 V0。
    本发明的有益效果在于：
    通过高光高流动的ABS与高流动PC的结合，并采用新型环保无卤阻燃剂，制备了高光泽无卤阻燃PC/ABS合金材料，材料具有表面极高的光泽度，良好的加工成型性，良好的阻燃性，其外观好、使用安全的特点使其能够广泛应用在家电领域，尤其是在高端电视壳体以及手机部件上有着广泛的应用前景。
具体实施方式
下面结合实施方式具体说明本发明。
 本实施方式的技术方案为：一种高光泽无卤阻燃PC/ABS合金材料，   主要由如下质量份的组分组成：PC树脂 65～80，ABS树脂 10-20，相容剂3-8，无卤阻燃剂 5-15，抗滴落剂 0.1-0.3。
其还包括抗氧剂 0.1～0.5， 润滑剂 0.1～0.5。
其中，所述阻燃剂采用缩聚型无卤磷酸酯阻燃剂。
本实施方式提供的上述高光泽无卤阻燃PC/ABS合金材料的制备方法，包括如下步骤：首先将各组分按照质量百分比用高速搅拌机搅拌混匀，然后转入双螺杆挤出机中熔融挤出，冷却，最后造粒即可制得产品。
其中，原料在高速搅拌机中搅拌5-10min。
其中，最后经造粒制得圆柱状颗粒产品。
其中，挤出时双螺杆挤出机的料筒温度为：后段200-210℃，中段210-220℃，前段220-225℃，机头温度225-230℃。
为进一步说明本实施方式，本实施方式提供了三个样品，记为样品1-3，其组成见表1，将其和ABS分别通过注塑成型制成液晶电视机前壳，并检验其强度、韧性和阻燃性，并记录在表1中。
表1
Figure DEST_PATH_IMAGE002A
     通过上表可知，本发明提供的PC/ABS合金材料的强度、韧性都要比高光ABS产品要高，同时其阻燃性达到UL-94 1.6mmV0，相比目前市面上使用的非阻燃高光ABS材料，提高了产品的安全性，因此本发明优于对比例。
     综上所述，本发明的特点在于：
    通过高光高流动的ABS与高流动PC的结合，并采用新型环保无卤阻燃剂，制备了高光泽无卤阻燃PC/ABS合金材料，材料具有表面极高的光泽度，良好的加工成型性，良好的阻燃性，其外观好、使用安全的特点使其能够广泛应用在家电领域，尤其是在高端电视壳体以及手机部件上有着广泛的应用前景。

Claims (7)

1. 一种高光泽无卤阻燃PC/ABS合金材料，其特征在于：主要由如下质量份的组分组成：PC树脂 65～80，ABS树脂 10-20，相容剂3-8，无卤阻燃剂 5-15，抗滴落剂 0.1-0.3。
2.根据权利要求1所述的高光泽无卤阻燃PC/ABS合金材料，其特征在于：还包括抗氧剂 0.1～0.5， 润滑剂 0.1～0.5。
3.根据权利要求2所述的高光泽无卤阻燃PC/ABS合金材料，其特征在于：所述阻燃剂采用缩聚型无卤磷酸酯阻燃剂。
4.根据权利要求1-3任意一项所述的高光泽无卤阻燃PC/ABS合金材料的制备方法，其特征在于：包括如下步骤：首先将各组分按照质量份用高速搅拌机搅拌混匀，然后转入双螺杆挤出机中熔融挤出，冷却，最后造粒即可制得产品。
5.根据权利要求4所述的高光泽无卤阻燃PC/ABS合金材料的制备方法，其特征在于：原料在高速搅拌机中搅拌5-10min。
6.根据权利要求5所述的高光泽无卤阻燃PC/ABS合金材料的制备方法，其特征在于：最后经造粒制得圆柱状颗粒产品。
7.根据权利要求5-6任意一项所述的高光泽无卤阻燃PC/ABS合金材料的制备方法，其特征在于：挤出时双螺杆挤出机的料筒温度为：后段200-210℃，中段210-220℃，前段220-225℃，机头温度225-230℃。
CN201310733811.8A 2013-12-27 2013-12-27 一种高光泽无卤阻燃pc/abs合金材料及其制备方法 Pending CN103740076A (zh)