CN103737201B - 一种铸铁焊条 - Google Patents
一种铸铁焊条 Download PDFInfo
- Publication number
- CN103737201B CN103737201B CN201310707251.9A CN201310707251A CN103737201B CN 103737201 B CN103737201 B CN 103737201B CN 201310707251 A CN201310707251 A CN 201310707251A CN 103737201 B CN103737201 B CN 103737201B
- Authority
- CN
- China
- Prior art keywords
- coating
- core wire
- cast iron
- electrode
- welding rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种铸铁焊条，该铸铁焊条由焊芯、药皮组成，焊芯、药皮占焊条总质量的百分比为：焊芯占55～65，药皮占35～45;焊芯为H08A，药皮成分：C：2.00‑4.00，Mn：0‑0.75，Si：2.5‑6.5，S：0‑0.10，P：0‑0.15，Ni：20‑30，Cu：60‑70，余量为Fe。焊条的采用较常规偏粗的焊条直径，如3.2mm、4.0mm、5.0mm等。本发明铸铁焊条药皮中的Ni含量降低，减少了焊条成本；所述焊条焊接后，焊缝金属具有较好的塑性，增强了焊缝的抗裂性；同时因为加入C、Si、Ni等元素促进石墨化，对消除或减弱半熔化区白口的形成是有利的。
Description
技术领域
本发明涉及一种金属焊接材料，具体的来说是涉及一种铸铁焊条。
技术背景
铸铁应用非常广泛，如机床床身、汽缸、箱体等结构件铸造结构件。但是，铸铁的特点是碳与硫、磷杂质含量高，组织不均匀，塑性低，属于焊接性不良的材料。铸铁焊接时容易出现的主要问题，一是焊接接头区域易出现白口及淬硬组织，二是易出现裂纹。铸铁焊条(或焊补)大致分为冷焊、半热焊和热焊三种，焊材的选择分为同质焊缝和异质焊缝两类。目前国内可以提供数十种铸铁焊条，可根据铸铁焊条的特性，对焊补件的要求(如是否切削加工)、铸铁材料的性能以及焊补件的重要性等分别选用。对焊后要求灰口铸铁焊缝的，可选用Z208、Z248焊条，对焊缝表面需经加工的，可选用Z308、Z408、Z418、Z508焊条，其中Z308最易加工；对球墨铸铁和高强度铸铁，可选用Z258、Z408、Z418焊条。以上这些焊条中含有大量的镍，这样焊接性能得到一定改善，但是成本大大增加。
发明内容
本发明的目的在于提供一种铸铁焊条，针对现有技术中的不足，该铸铁焊条价格比较低，克服了在焊接铸铁时出现白口、淬硬组织、焊接裂纹等缺陷。
本发明通过如下方式实现：
一种铸铁焊条，由焊芯、药皮组成，焊芯、药皮占焊条总质量的百分比为：焊芯55-65，药皮35-45；焊芯为H08A；药皮中各成分占药皮总质量的百分比：C：2.00-4.00，Mn：0-0.75，Si：2.5-6.5，S：0-0.10，P：0-0.15，Ni：20-30，Cu：60-70，余量为Fe和不可避免的杂质。
本发明焊芯、药皮占焊条总质量的百分比为：焊芯60，药皮40；药皮中各成分占药皮总质量的百分比：C：4.00，Mn：0.45，Si：6.5，S：0.01，P：0.05，Ni：20，Cu：65,余量为不可避免的杂质。
与现有技术相比，本发明的有益效果是：
本发明铸铁焊条药皮中的Ni含量降低减少了成本，同时添加了较大量的Cu,由于Cu的熔点较低，而铁的熔点较高，因此在熔池开始结晶时，先析出的是铁，受到电弧和电流的力，使得Cu在熔池中不断上浮，覆盖在熔池上面，阻止熔池过快的冷却，使得处于保护区域的珠光体个部分铁素体重结晶，细化晶粒，达到退火目的，使焊缝金属具有较好的塑性，改善焊缝的抗裂性。同时加入C、Si、Ni等元素促进石墨化消除或减弱半熔化区白口的形成是有利的。
具体实施方案
一种铸铁焊条，由焊芯、药皮组成，焊芯、药皮占焊条总质量的百分比为：焊芯55-65，药皮35-45；焊芯为H08A；药皮中各成分占药皮总质量的百分比：C：2.00-4.00，Mn：0-0.75，Si：2.5-6.5，S：0-0.10，P：0-0.15，Ni：20-30，Cu：60-70，余量为Fe和不可避免的杂质。
Claims (2)
1.一种铸铁焊条，由焊芯、药皮组成，其特征在，焊芯、药皮占焊条总质量的百分比为：焊芯55-65，药皮35-45；焊芯为H08A；药皮中各成分占药皮总质量的百分比：C：2.00-4.00，Mn：0-0.75，Si：2.5-6.5，S：0-0.10，P：0-0.15，Ni：20-30，Cu：60-70，余量为Fe和不可避免的杂质。
2.如权利要求1所述的铸铁焊条，其特征在于，焊芯、药皮占焊条总质量的百分比为：焊芯60，药皮40；药皮中各成分占药皮总质量的百分比：C：4.00，Mn：0.45，Si：6.5，S：0.01，P：0.05，Ni：20，Cu：65, 余量为Fe和不可避免的杂质。