CN103736443A - 一种凹凸棒粘土回收处理工艺 - Google Patents

一种凹凸棒粘土回收处理工艺 Download PDF

Info

Publication number
CN103736443A
CN103736443A CN201310689587.7A CN201310689587A CN103736443A CN 103736443 A CN103736443 A CN 103736443A CN 201310689587 A CN201310689587 A CN 201310689587A CN 103736443 A CN103736443 A CN 103736443A
Authority
CN
China
Prior art keywords
attapulgite clay
sodium carbonate
stirring
add
moisture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310689587.7A
Other languages
English (en)
Inventor
李振国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MINGGUANG GUOXING ATTAPULGITE CLAY Co Ltd
Original Assignee
MINGGUANG GUOXING ATTAPULGITE CLAY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MINGGUANG GUOXING ATTAPULGITE CLAY Co Ltd filed Critical MINGGUANG GUOXING ATTAPULGITE CLAY Co Ltd
Priority to CN201310689587.7A priority Critical patent/CN103736443A/zh
Publication of CN103736443A publication Critical patent/CN103736443A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种处理凹凸棒粘土的回收处理工艺，包括以下步骤：（1）取已用凹凸棒粘土在自然条件下进行风化；（2）将碳酸钠配制成溶液，加入搅拌池；（3）取凹凸棒粘土加入搅拌池中，进行清洗；（4）将清洗好的凹凸棒粘土使用压片机进行压片；（5）将压片的凹凸棒粘土使用烘干机烘干，然后使用破碎机破碎，再放入搅拌机搅拌，边搅拌边加盐酸；（6）将上述凹凸棒粘土放入窑炉，烘干至水分不大于5%，冷却制得成品。本方法工艺简单，处理后凹凸棒粘土的性能均匀，处理后的凹凸棒粘土吸附性能好，含杂质量少，对凹凸棒粘土的回收利用，减少了资源的浪费，节约了资源，具有很高的推广价值。

Description

一种凹凸棒粘土回收处理工艺
技术领域
本发明涉及一种处理凹凸棒粘土的工艺，具体涉及一种凹凸棒粘土回收处理工艺。
背景技术
凹凸棒粘土是一种以凹凸棒石为主的矿石物，可以加工成吸附剂等使用，吸附能力强，无污染，但是随着凹凸棒粘土开发的日益严峻，凹凸棒粘土资源终将匮乏，所以我们需要进行凹凸棒粘土资源的回收利用。
发明内容
本发明的目的是提供一种凹凸棒粘土回收处理工艺。
本发明通过以下技术方案实现：
一种凹凸棒粘土回收处理工艺，其包括以下处理步骤：
（1）、取已用凹凸棒粘土在自然条件下进行风化3-5个月，每周翻晒1-2次；
（2）、将碳酸钠配制成8%的碳酸钠溶液，加入搅拌池，备用；
（3）、取凹凸棒粘土加入含有碳酸钠溶液的搅拌池中，使用搅拌机搅拌30-50min，进行清洗；
（4）、将清洗好的凹凸棒粘土使用压片机进行压片，片的厚度为3-5mm；
（5）、将压片的凹凸棒粘土使用烘干机在150-180℃下烘干至水分不大于20%，然后使用破碎机破碎成6-8mm的颗粒，再放入搅拌机搅拌，边搅拌边加盐酸，调节PH；
（6）、将上述步骤处理好的凹凸棒粘土放入窑炉，在300-400℃烘干，烘干至水分不大于5%，自然冷却，包装，制得成品。
上述步骤中，按重量计包括：凹凸棒粘土70-90份、碳酸钠6-9份、盐酸5-13份。
本发明的有益效果在于：本方法工艺简单，处理后凹凸棒粘土的性能均匀，处理后的凹凸棒粘土吸附性能好，含杂质量少，对凹凸棒粘土的回收利用，减少了资源的浪费，节约了资源，具有很高的推广价值。
具体实施方式
一种凹凸棒粘土回收处理工艺，其包括以下处理步骤：
（1）、取已用凹凸棒粘土在自然条件下进行风化3-5个月，每周翻晒1-2次；
（2）、将碳酸钠配制成8%的碳酸钠溶液，加入搅拌池，备用；
（3）、取凹凸棒粘土加入含有碳酸钠溶液的搅拌池中，使用搅拌机搅拌30-50min，进行清洗；
（4）、将清洗好的凹凸棒粘土使用压片机进行压片，片的厚度为3-5mm；
（5）、将压片的凹凸棒粘土使用烘干机在150-180℃下烘干至水分不大于20%，然后使用破碎机破碎成6-8mm的颗粒，再放入搅拌机搅拌，边搅拌边加盐酸，调节PH；
（6）、将上述步骤处理好的凹凸棒粘土放入窑炉，在300-400℃烘干，烘干至水分不大于5%，自然冷却，包装，制得成品。
上述步骤中，按重量计包括：凹凸棒粘土70-90份、碳酸钠6-9份、盐酸5-13份。

Claims (1)

1.一种凹凸棒粘土回收处理工艺，其包括以下处理步骤：
（1）、取已用凹凸棒粘土在自然条件下进行风化3-5个月，每周翻晒1-2次；
（2）、将碳酸钠配制成8%的碳酸钠溶液，加入搅拌池，备用；
（3）、取凹凸棒粘土加入含有碳酸钠溶液的搅拌池中，使用搅拌机搅拌30-50min，进行清洗；
（4）、将清洗好的凹凸棒粘土使用压片机进行压片，片的厚度为3-5mm；
（5）、将压片的凹凸棒粘土使用烘干机在150-180℃下烘干至水分不大于20%，然后使用破碎机破碎成6-8mm的颗粒，再放入搅拌机搅拌，边搅拌边加盐酸，调节PH；
（6）、将上述步骤处理好的凹凸棒粘土放入窑炉，在300-400℃烘干，烘干至水分不大于5%，自然冷却，包装，制得成品；
上述步骤中，按重量计包括：凹凸棒粘土70-90份、碳酸钠6-9份、盐酸5-13份。
CN201310689587.7A 2013-12-17 2013-12-17 一种凹凸棒粘土回收处理工艺 Pending CN103736443A (zh)