CN103724889A - 一种回弹性好的减震器油封 - Google Patents

一种回弹性好的减震器油封 Download PDF

Info

Publication number
CN103724889A
CN103724889A CN201310686782.4A CN201310686782A CN103724889A CN 103724889 A CN103724889 A CN 103724889A CN 201310686782 A CN201310686782 A CN 201310686782A CN 103724889 A CN103724889 A CN 103724889A
Authority
CN
China
Prior art keywords
parts
good
oil seal
raw material
rebound resilience
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310686782.4A
Other languages
English (en)
Inventor
韦中祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Jinying Machinery Science & Technology Development Co Ltd
Original Assignee
Wuhu Jinying Machinery Science & Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Jinying Machinery Science & Technology Development Co Ltd filed Critical Wuhu Jinying Machinery Science & Technology Development Co Ltd
Priority to CN201310686782.4A priority Critical patent/CN103724889A/zh
Publication of CN103724889A publication Critical patent/CN103724889A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种回弹性好的减震器油封，它是由下述重量份的原料组成的：氟橡胶F26100-104、万年灰3-5、聚乙二醇10002-3、二硫代水杨酸1-2、蜂胶3-4、气相白炭黑10-14、硬酯酸单甘油酯2-3、SG-3型PVC树脂6-8、无水乙醇1-2、磷酸甲苯二苯酯6-8、二甲氨基丙胺1-2、氯化镁1-2、过氧化二叔丁基1-2、硫磺0.3-0.5、促进剂CZ1-2、防老剂40101-2、复合填料18-26，本发明的回弹性好的减震器油封具有能够保持油封原有形状、跟随性能优良、密封效果好、力学性能好，耐候性强，使用寿命长等优点。

Description

一种回弹性好的减震器油封
技术领域
本发明主要涉及汽车配件领域，尤其涉及一种回弹性好的减震器油封。
背景技术
氟橡胶耐老化，耐热，耐油，几乎适用于所有的润滑油、燃料油、汽油、在含极压添加剂的油中不易硬化，但耐寒性、高温耐磨性较差，永久压缩变形较大，适用于温度-20～250℃。主要用于耐高温油封如发动机油封等，因此加入助剂改进氟橡胶的综合性能，可以加大氟橡胶的使用范围。
发明内容
本发明目的就是提供一种回弹性好的减震器油封。
本发明是通过以下技术方案实现的：
一种回弹性好的减震器油封，它是由下述重量份的原料组成的：
氟橡胶F26 100-104、万年灰3-5、聚乙二醇1000 2-3、二硫代水杨酸1-2、蜂胶3-4、气相白炭黑10-14、硬酯酸单甘油酯2-3、SG-3型PVC树脂6-8、无水乙醇1-2、磷酸甲苯二苯酯6-8、二甲氨基丙胺1-2、氯化镁1-2、过氧化二叔丁基1-2、硫磺0.3-0.5、促进剂CZ1-2、防老剂4010 1-2、复合填料18-26；
所述的复合填料是由下述重量份的原料组成的：
黑土32-40、锂基膨润土6-10、溴化聚苯乙烯2-4、硅铝酸钠2-3、环烷油1-2、氟化锆0.1-0.4、硼酸0.6-1；
将上述黑土与锂基膨润土混合，在600-700℃下煅烧1-2小时，冷却出料后与氟化锆混合，研磨成粉，加入溴化聚苯乙烯、环烷油，200-300转/分搅拌分散5-6分钟，加入剩余各原料，搅拌均匀后自然干燥，即得所述复合填料。
一种回弹性好的减震器油封的制备方法，包括以下步骤：
将上述氟橡胶F26放入密炼机进行密炼，温度105-110℃，时间为1-3min；加入除了过氧化二叔丁基、硫磺、促进剂CZ以外的各原料，继续密炼10-15分钟，当温度达到95-100℃，开始排料，排料后停放冷却24-30小时；投入开炼机内，加入剩余各原料，薄通6-8遍即得所述回弹性好的减震器油封。
本发明的优点是：
本发明的回弹性好的减震器油封具有能够保持油封原有形状、跟随性能优良、密封效果好、力学性能好，耐候性强，使用寿命长等优点。
具体实施方式
实施例1
一种回弹性好的减震器油封，它是由下述重量份（公斤）的原料组成的：
氟橡胶F26 104、万年灰3、聚乙二醇1000 3、二硫代水杨酸2、蜂胶3、气相白炭黑14、硬酯酸单甘油酯2、SG-3型PVC树脂8、无水乙醇2、磷酸甲苯二苯酯8、二甲氨基丙胺2、氯化镁1、过氧化二叔丁基1、硫磺0.5、促进剂CZ2、防老剂4010 2、复合填料26；
所述的复合填料是由下述重量份的原料组成的：
黑土40、锂基膨润土10、溴化聚苯乙烯4、硅铝酸钠3、环烷油1、氟化锆0.4、硼酸0.6；
将上述黑土与锂基膨润土混合，在700℃下煅烧2小时，冷却出料后与氟化锆混合，研磨成粉，加入溴化聚苯乙烯、环烷油，300转/分搅拌分散6分钟，加入剩余各原料，搅拌均匀后自然干燥，即得所述复合填料。
一种回弹性好的减震器油封的制备方法，包括以下步骤：
将上述氟橡胶F26放入密炼机进行密炼，温度110℃，时间为3min；加入除了过氧化二叔丁基、硫磺、促进剂CZ以外的各原料，继续密炼15分钟，当温度达到100℃，开始排料，排料后停放冷却30小时；投入开炼机内，加入剩余各原料，薄通8遍即得所述回弹性好的减震器油封。
性能测试：
Figure BDA0000437116020000031

Claims (2)

1.一种回弹性好的减震器油封，其特征在于它是由下述重量份的原料组成的：
氟橡胶F26 100-104、万年灰3-5、聚乙二醇1000 2-3、二硫代水杨酸1-2、蜂胶3-4、气相白炭黑10-14、硬酯酸单甘油酯2-3、SG-3型PVC树脂6-8、无水乙醇1-2、磷酸甲苯二苯酯6-8、二甲氨基丙胺1-2、氯化镁1-2、过氧化二叔丁基1-2、硫磺0.3-0.5、促进剂CZ1-2、防老剂4010 1-2、复合填料18-26；
所述的复合填料是由下述重量份的原料组成的：
黑土32-40、锂基膨润土6-10、溴化聚苯乙烯2-4、硅铝酸钠2-3、环烷油1-2、氟化锆0.1-0.4、硼酸0.6-1；
将上述黑土与锂基膨润土混合，在600-700℃下煅烧1-2小时，冷却出料后与氟化锆混合，研磨成粉，加入溴化聚苯乙烯、环烷油，200-300转/分搅拌分散5-6分钟，加入剩余各原料，搅拌均匀后自然干燥，即得所述复合填料。
2.一种如权利要求1所述的回弹性好的减震器油封的制备方法，其特征在于包括以下步骤：
将上述氟橡胶F26放入密炼机进行密炼，温度105-110℃，时间为1-3min；加入除了过氧化二叔丁基、硫磺、促进剂CZ以外的各原料，继续密炼10-15分钟，当温度达到95-100℃，开始排料，排料后停放冷却24-30 小时；投入开炼机内，加入剩余各原料，薄通6-8 遍即得所述回弹性好的减震器油封。
CN201310686782.4A 2013-12-13 2013-12-13 一种回弹性好的减震器油封 Pending CN103724889A (zh)