CN103665682A - 一种高弹性低压缩形变得橡胶密封垫材料及其制备方法 - Google Patents

一种高弹性低压缩形变得橡胶密封垫材料及其制备方法 Download PDF

Info

Publication number
CN103665682A
CN103665682A CN201310575323.9A CN201310575323A CN103665682A CN 103665682 A CN103665682 A CN 103665682A CN 201310575323 A CN201310575323 A CN 201310575323A CN 103665682 A CN103665682 A CN 103665682A
Authority
CN
China
Prior art keywords
parts
mixing
carbon black
rubber
accelerant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310575323.9A
Other languages
English (en)
Other versions
CN103665682B (zh
Inventor
王慧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HONG ENERGY-SAVING EQUIPMENT Co Ltd
Original Assignee
ANHUI HONG ENERGY-SAVING EQUIPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HONG ENERGY-SAVING EQUIPMENT Co Ltd filed Critical ANHUI HONG ENERGY-SAVING EQUIPMENT Co Ltd
Priority to CN201310575323.9A priority Critical patent/CN103665682B/zh
Publication of CN103665682A publication Critical patent/CN103665682A/zh
Application granted granted Critical
Publication of CN103665682B publication Critical patent/CN103665682B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高弹性低压缩形变得橡胶密封垫材料，其特征在于，由下列重量份的原料制成：四丙氟橡胶60-65、天然橡胶20-25、过氧化二异丙苯2.5-2.8、三烯丙基异氰脲酸酯4-4.5、三甲硅基甲基膦酸二甲酯5-8、氰尿酸三聚氰胺3-4、硬脂酸5-8、促进剂Na-221-2、N339炭黑10-20、氧化锌1-2、促进剂M1-2、N351炭黑30-34、菜籽油4-5、改性凹凸棒土10-12；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有较高的弹性以及低压缩形变，耐油、耐腐蚀、耐磨，密封性良好，经久耐用。

Description

一种高弹性低压缩形变得橡胶密封垫材料及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种高弹性低压缩形变得橡胶密封垫材料及其制备方法。
背景技术
密封垫，是一种用于机械、设备、管道等内部，起密封作用的材料。目前使用的密封垫多为橡胶密封垫，其特点是：耐高温、耐臭氧、耐天然老化、耐真空、耐燃料油、耐润滑油、耐强氧化剂、耐药品性和电绝缘性能好，广泛用于国防工业和民用工业。但是现有的橡胶密封垫密封效果不理想、耐磨性较差、强度低等缺陷，已远不能满足现实要求。因此研发一种高性能橡胶密封垫已成为当务之急。
发明内容
本发明的目的是提供一种高弹性低压缩形变得橡胶密封垫材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种高弹性低压缩形变得橡胶密封垫材料，由下列重量份的原料制成：四丙氟橡胶60-65、天然橡胶20-25、过氧化二异丙苯2.5-2.8、三烯丙基异氰脲酸酯4-4.5、三甲硅基甲基膦酸二甲酯5-8、氰尿酸三聚氰胺3-4、硬脂酸5-8、促进剂Na-221-2、N339炭黑10-20、氧化锌1-2、促进剂M1-2、N351炭黑30-34、菜籽油4-5、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土12-15、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯2-3、纳米二氧化钛3-4、纳米二氧化硅1-2、氧化锌1-2、促进剂TMTD1-2、阳起石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述高弹性低压缩形变得橡胶密封垫材料，由以下具体步骤制成：将天然橡胶、过氧化二异丙苯、三烯丙基异氰脲酸酯、三甲硅基甲基膦酸二甲酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-120℃，再加入氰尿酸三聚氰胺、硬脂酸、促进剂Na-22，混炼6-8min，再加入N339炭黑、氧化锌、促进剂M继续混炼4-6min；加入其余剩余成分混炼6-8min，即得。
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有较高的弹性以及低压缩形变，耐油、耐腐蚀、耐磨，密封性良好，经久耐用。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种高弹性低压缩形变得橡胶密封垫材料，由下列重量份（公斤）的原料制成：四丙氟橡胶60、天然橡胶20、过氧化二异丙苯2.5、三烯丙基异氰脲酸酯4、三甲硅基甲基膦酸二甲酯5、氰尿酸三聚氰胺3、硬脂酸5、促进剂Na-221、N339炭黑10、氧化锌1、促进剂M1、N351炭黑30、菜籽油4、改性凹凸棒土10；
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土20、粘土12、1,6-己二异氰酸酯3、二缩三丙二醇二丙烯酸酯2、纳米二氧化钛3、纳米二氧化硅1、氧化锌1、促进剂TMTD1、阳起石粉8、花椒籽油1；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述高弹性低压缩形变得橡胶密封垫材料，由以下具体步骤制成：将天然橡胶、过氧化二异丙苯、三烯丙基异氰脲酸酯、三甲硅基甲基膦酸二甲酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-120℃，再加入氰尿酸三聚氰胺、硬脂酸、促进剂Na-22，混炼6-8min，再加入N339炭黑、氧化锌、促进剂M继续混炼4-6min；加入其余剩余成分混炼6-8min，即得。
用本发明的密封垫材料与普通橡胶料物理性能对比如下表。
Figure BDA0000415463380000021
Figure BDA0000415463380000031
从表中可以看出用本发明的橡胶密封垫材料，综合性能比较好。

Claims (2)

1.一种高弹性低压缩形变得橡胶密封垫材料，其特征在于，由下列重量份的原料制成：四丙氟橡胶60-65、天然橡胶20-25、过氧化二异丙苯2.5-2.8、三烯丙基异氰脲酸酯4-4.5、三甲硅基甲基膦酸二甲酯5-8、氰尿酸三聚氰胺3-4、硬脂酸5-8、促进剂Na-22 1-2、N339炭黑10-20、氧化锌1-2、促进剂M1-2、N351炭黑30-34、菜籽油4-5、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土12-15、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯2-3、纳米二氧化钛3-4、纳米二氧化硅1-2、氧化锌1-2、促进剂TMTD 1-2、阳起石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述高弹性低压缩形变得橡胶密封垫材料，其特征在于，由以下具体步骤制成：将天然橡胶、过氧化二异丙苯、三烯丙基异氰脲酸酯、三甲硅基甲基膦酸二甲酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-120℃，再加入氰尿酸三聚氰胺、硬脂酸、促进剂Na-22，混炼6-8min，再加入N339炭黑、氧化锌、促进剂M继续混炼4-6min；加入其余剩余成分混炼6-8min，即得。
CN201310575323.9A 2013-11-15 2013-11-15 一种高弹性低压缩形变得橡胶密封垫材料及其制备方法 Expired - Fee Related CN103665682B (zh)