CN103710999B - A kind of environmental protection composite dye and preparation method thereof - Google Patents
A kind of environmental protection composite dye and preparation method thereof Download PDFInfo
- Publication number
- CN103710999B CN103710999B CN201310644112.6A CN201310644112A CN103710999B CN 103710999 B CN103710999 B CN 103710999B CN 201310644112 A CN201310644112 A CN 201310644112A CN 103710999 B CN103710999 B CN 103710999B
- Authority
- CN
- China
- Prior art keywords
- sodium
- raw material
- dye
- acid
- environmental protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of novel environment friendly composite dye, it is characterized in that, be made up of the raw material of following weight portion: organic dye raw material 100-110, xylitol 5-6, sorbierite 2-3, octadecyl alcolol 4-5, oleic acid 2-3, sodium ascorbate 1-2, Tea Polyphenols 1-2, phenolic resins 1-2, sodium lauryl sulfate 3-4, sodium peroxydisulfate 1-2, vitamin A acid 4-5, sodium thiosulfate 1-2, sodium sulfite 2-3, auxiliary agent 4-5, water 150; The present invention has excellent high-temperature stability, and the dyeing of cotton textiles, BLENDED FABRIC, polyester-cotton fabric is had to good result, significantly can provide the quality of fabric, and dye solubility is good, good level-dyeing property, salt dosage is few, is environment amenable new product.
Description
Technical field
The present invention relates to staining technique field, particularly a kind of environmental protection composite dye and preparation method thereof.
Background technology
Dyestuff to make certain color be attached to material on fiber, and difficult drop-off, variable color.Dyestuff is usually soluble in water, and a part of dyestuff needs mordant that dyestuff can be attached on fiber.The color of dyestuff and the affinity between it and tissue are determined by the molecular structure of dyestuff itself, colorific chromophoric group and and the auxochrome group that produces affinity between organizing jointly determine the dyeing property of coloring agent.As dye substance, except having chromophoric group, also need a kind of auxochrome group making compound generation ionization.As often defined chromophoric group by nitro (-NO2), azo group (-N=N-), vinyl etc. in dye composition, and constitute auxochrome group by the acidic-groups such as-OH ,-SO3H ,-COOH and the basic group such as-NH2 ,-NHCH3 ,-N (CH3) 2.Their existence makes dye substance ionization, and polarity strengthens, and promotes to have an effect between dyestuff and tissue, produces Color.We are called acidity or basic stain the dyestuff in auxochrome group with acidity or basic group.
Dyeing be printing and dyeing production process in important step, ACID DYES usually can be used to dye, dye level the object of the invention is to for the problems referred to above, provide a kind of good stability, dye firmly environmental protection coloring composition and production method.
Summary of the invention
The object of this invention is to provide a kind of environmental protection composite dye and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
A kind of environmental protection composite dye, is made up of the raw material of following weight portion: organic dye raw material 100-110, xylitol 5-6, sorbierite 2-3, octadecyl alcolol 4-5, oleic acid 2-3, sodium ascorbate 1-2, Tea Polyphenols 1-2, phenolic resins 1-2, sodium lauryl sulfate 3-4, sodium peroxydisulfate 1-2, vitamin A acid 4-5, sodium thiosulfate 1-2, sodium sulfite 2-3, auxiliary agent 4-5, water 150;
Described auxiliary agent is made up of the raw material of following weight portion: Silane coupling agent KH550 1-2, penetrating agent JFC 1-2, citric acid 1-2, neopentyl glycol 3-4, methacrylic acid-2-hydroxy methacrylate 10-12, water 10-12; Preparation method is that be heated to 60-70 DEG C, stirring reaction 30-45 minute, to obtain final product by after each raw material mixing.
Environmental protection composite dye of the present invention, be made up of following concrete steps:
(1) organic dye raw material, xylitol, sorbierite, octadecyl alcolol, oleic acid, sodium ascorbate, Tea Polyphenols, phenolic resins, sodium lauryl sulfate are put into the reactor with agitator, mix and blend 15-25 minute;
(2) in reactor, add sodium peroxydisulfate again, be heated to 90-100 DEG C, and be incubated 30-40 minute;
(3) finally add auxiliary agent and all the other residual componentss, stir 1-2 hour, cross leaching filtrate and get final product.
Excellent effect of the present invention is: the present invention has excellent high-temperature stability, the dyeing of cotton textiles, BLENDED FABRIC, polyester-cotton fabric is had to good result, significantly can provide the quality of fabric, and dye solubility is good, good level-dyeing property, salt dosage is few, is environment amenable new product.
Detailed description of the invention
Below by instantiation, the present invention is described in detail.
A kind of environmental protection composite dye, is made up of the raw material of following weight portion (kilogram): organic dye raw material 100, xylitol 5, sorbierite 2, octadecyl alcolol 4, oleic acid 2, sodium ascorbate 1, Tea Polyphenols 1, phenolic resins 1, sodium lauryl sulfate 3, sodium peroxydisulfate 1, vitamin A acid 4, sodium thiosulfate 1, sodium sulfite 2, auxiliary agent 4, water 150;
Described auxiliary agent is made up of the raw material of following weight portion (kilogram): Silane coupling agent KH550 1, penetrating agent JFC 1, citric acid 2, neopentyl glycol 3, methacrylic acid-2-hydroxy methacrylate 10, water 10; Preparation method is that be heated to 60-70 DEG C, stirring reaction 30-45 minute, to obtain final product by after each raw material mixing.
Environmental protection composite dye of the present invention, be made up of following concrete steps:
(1) organic dye raw material, xylitol, sorbierite, octadecyl alcolol, oleic acid, sodium ascorbate, Tea Polyphenols, phenolic resins, sodium lauryl sulfate are put into the reactor with agitator, mix and blend 15-25 minute;
(2) in reactor, add sodium peroxydisulfate again, be heated to 90-100 DEG C, and be incubated 30-40 minute;
(3) finally add auxiliary agent and all the other residual componentss, stir 1-2 hour, cross leaching filtrate and get final product.
After testing, the light fastness of dyestuff of the present invention is 6 grades, and soaping fastness is 4 grades, and crock fastness is 4 grades, chlorine drift fastness 4 grades.
Claims (2)
1. an environmental protection composite dye, it is characterized in that, be made up of the raw material of following weight portion: organic dye raw material 100-110, xylitol 5-6, sorbierite 2-3, octadecyl alcolol 4-5, oleic acid 2-3, sodium ascorbate 1-2, Tea Polyphenols 1-2, phenolic resins 1-2, sodium lauryl sulfate 3-4, sodium peroxydisulfate 1-2, vitamin A acid 4-5, sodium thiosulfate 1-2, sodium sulfite 2-3, auxiliary agent 4-5, water 150;
Described auxiliary agent is made up of the raw material of following weight portion: Silane coupling agent KH550 1-2, penetrating agent JFC 1-2, citric acid 1-2, neopentyl glycol 3-4, methacrylic acid-2-hydroxy methacrylate 10-12, water 10-12; Preparation method is that be heated to 60-70 DEG C, stirring reaction 30-45 minute, to obtain final product by after each raw material mixing.
2. environmental protection composite dye according to claim 1, is characterized in that, be made up of following concrete steps:
(1) organic dye raw material, xylitol, sorbierite, octadecyl alcolol, oleic acid, sodium ascorbate, Tea Polyphenols, phenolic resins, sodium lauryl sulfate are put into the reactor with agitator, mix and blend 15-25 minute;
(2) in reactor, add sodium peroxydisulfate again, be heated to 90-100 DEG C, and be incubated 30-40 minute;
(3) finally add auxiliary agent and all the other residual componentss, stir 1-2 hour, cross leaching filtrate and get final product.