CN103709600A - 一种改性三聚氰胺甲醛树脂的配方 - Google Patents
一种改性三聚氰胺甲醛树脂的配方 Download PDFInfo
- Publication number
- CN103709600A CN103709600A CN201310728234.3A CN201310728234A CN103709600A CN 103709600 A CN103709600 A CN 103709600A CN 201310728234 A CN201310728234 A CN 201310728234A CN 103709600 A CN103709600 A CN 103709600A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde resin
- accounts
- modified melamine
- formula
- terpolycyantoamino
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明揭示了一种改性三聚氰胺甲醛树脂的配方，所述改性三聚氰胺甲醛树脂的配方中包括三聚氰胺甲醛树脂、增塑剂、增韧剂、填充剂、抗氧化剂以及稳定剂，所述的增塑剂由邻苯二甲酸二甲酯构成，所述的增韧剂由苯乙烯-丁二烯热塑性弹性体构成，所述的填充剂由滑石粉构成，所述的抗氧化剂由二丁基羟基甲苯构成，所述的稳定剂由二巯基乙酸异辛酯二正辛基锡构成。该改性三聚氰胺甲醛树脂的配方使制得的改性脲醛树脂可塑性强、韧性好、成本低、机械强度高、耐老化以及使用寿命长等功效。
Description
技术领域
本发明涉及一种塑料配方，具体涉及一种改性三聚氰胺甲醛树脂的配方。
背景技术
三聚氰胺甲醛树脂固化后胶层容易破裂，韧性较差，同时在成型过程中较为困难，另外，由于三聚氰胺甲醛树脂单独使用时性能虽然较好，但是成本较高，对企业的利润相对较低，另外，由于三聚氰胺甲醛树脂储存期短、易变质，使得三聚氰胺甲醛树脂在使用过程中容易造成浪费。
发明内容
本发明的目的在于提供一种可塑性强、韧性好、成本低、机械强度高、耐老化以及使用寿命长的改性三聚氰胺甲醛树脂的配方。
本发明的技术方案是，一种改性三聚氰胺甲醛树脂的配方，所述改性三聚氰胺甲醛树脂的配方中包括三聚氰胺甲醛树脂、增塑剂、增韧剂、填充剂、抗氧化剂以及稳定剂，所述的增塑剂由邻苯二甲酸二甲酯构成，所述的增韧剂由苯乙烯-丁二烯热塑性弹性体构成，所述的填充剂由滑石粉构成，所述的抗氧化剂由二丁基羟基甲苯构成，所述的稳定剂由二巯基乙酸异辛酯二正辛基锡构成。
在本发明一个较佳实施例中，所述的改性三聚氰胺甲醛树脂的配方各成分所占重量百分比分别为三聚氰胺甲醛树脂占67.4%-75.3%，邻苯二甲酸二甲酯占1.8%-3.2%，苯乙烯-丁二烯热塑性弹性体占5.3%-6.9%，滑石粉占12.4%-15.7%，二丁基羟基甲苯占2.5%-3.6%，二巯基乙酸异辛酯二正辛基锡占2.7%-3.2%。
在本发明一个较佳实施例中，所述的改性三聚氰胺甲醛树脂的配方各成分所占重量百分比分别为三聚氰胺甲醛树脂占70.2%，邻苯二甲酸二甲酯占2.8%，苯乙烯-丁二烯热塑性弹性体占6.3%，滑石粉占14.6%，二丁基羟基甲苯占3.2%，二巯基乙酸异辛酯二正辛基锡占2.9%。
本发明所述为一种改性三聚氰胺甲醛树脂的配方，使制得的改性脲醛树脂可塑性强、韧性好、成本低、机械强度高、耐老化以及使用寿命长等功效。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种改性三聚氰胺甲醛树脂的配方，所述改性三聚氰胺甲醛树脂的配方中包括三聚氰胺甲醛树脂、增塑剂、增韧剂、填充剂、抗氧化剂以及稳定剂，所述的增塑剂由邻苯二甲酸二甲酯构成，所述的增韧剂由苯乙烯-丁二烯热塑性弹性体构成，所述的填充剂由滑石粉构成，所述的抗氧化剂由二丁基羟基甲苯构成，所述的稳定剂由二巯基乙酸异辛酯二正辛基锡构成。
进一步地，所述的改性三聚氰胺甲醛树脂的配方各成分所占重量百分比分别为三聚氰胺甲醛树脂占67.4%-75.3%，邻苯二甲酸二甲酯占1.8%-3.2%，苯乙烯-丁二烯热塑性弹性体占5.3%-6.9%，滑石粉占12.4%-15.7%，二丁基羟基甲苯占2.5%-3.6%，二巯基乙酸异辛酯二正辛基锡占2.7%-3.2%。
进一步地，所述的改性三聚氰胺甲醛树脂的配方各成分所占重量百分比分别为三聚氰胺甲醛树脂占70.2%，邻苯二甲酸二甲酯占2.8%，苯乙烯-丁二烯热塑性弹性体占6.3%，滑石粉占14.6%，二丁基羟基甲苯占3.2%，二巯基乙酸异辛酯二正辛基锡占2.9%。
进一步地，所述的改性三聚氰胺甲醛树脂的配方各成分所占重量百分比分别为三聚氰胺甲醛树脂占73.4%，邻苯二甲酸二甲酯占2.1%，苯乙烯-丁二烯热塑性弹性体占5.7%，滑石粉占13.1%，二丁基羟基甲苯占2.6%，二巯基乙酸异辛酯二正辛基锡占3.1%。
本发明所述为一种改性三聚氰胺甲醛树脂的配方，使制得的改性脲醛树脂可塑性强、韧性好、成本低、机械强度高、耐老化以及使用寿命长等功效。
以上所述仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (3)
1.一种改性三聚氰胺甲醛树脂的配方，其特征在于：所述改性三聚氰胺甲醛树脂的配方中包括三聚氰胺甲醛树脂、增塑剂、增韧剂、填充剂、抗氧化剂以及稳定剂，所述的增塑剂由邻苯二甲酸二甲酯构成，所述的增韧剂由苯乙烯-丁二烯热塑性弹性体构成，所述的填充剂由滑石粉构成，所述的抗氧化剂由二丁基羟基甲苯构成，所述的稳定剂由二巯基乙酸异辛酯二正辛基锡构成。
2.根据权利要求1所述的改性三聚氰胺甲醛树脂的配方，其特征在于：所述的改性三聚氰胺甲醛树脂的配方各成分所占重量百分比分别为三聚氰胺甲醛树脂占67.4%-75.3%，邻苯二甲酸二甲酯占1.8%-3.2%，苯乙烯-丁二烯热塑性弹性体占5.3%-6.9%，滑石粉占12.4%-15.7%，二丁基羟基甲苯占2.5%-3.6%，二巯基乙酸异辛酯二正辛基锡占2.7%-3.2%。
3.根据权利要求2所述的改性三聚氰胺甲醛树脂的配方，其特征在于：所述的改性三聚氰胺甲醛树脂的配方各成分所占重量百分比分别为三聚氰胺甲醛树脂占70.2%，邻苯二甲酸二甲酯占2.8%，苯乙烯-丁二烯热塑性弹性体占6.3%，滑石粉占14.6%，二丁基羟基甲苯占3.2%，二巯基乙酸异辛酯二正辛基锡占2.9%。