CN103667786A - 一种耐冲击的铜镍合金及其制备方法 - Google Patents

一种耐冲击的铜镍合金及其制备方法 Download PDF

Info

Publication number
CN103667786A
CN103667786A CN201310638526.8A CN201310638526A CN103667786A CN 103667786 A CN103667786 A CN 103667786A CN 201310638526 A CN201310638526 A CN 201310638526A CN 103667786 A CN103667786 A CN 103667786A
Authority
CN
China
Prior art keywords
melting
cupronickel
preparation
impact
copper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310638526.8A
Other languages
English (en)
Inventor
王惠
张松岩
钱忆张
陈新燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU PAQINI COPPER INDUSTRY Co Ltd
Original Assignee
JIANGSU PAQINI COPPER INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU PAQINI COPPER INDUSTRY Co Ltd filed Critical JIANGSU PAQINI COPPER INDUSTRY Co Ltd
Priority to CN201310638526.8A priority Critical patent/CN103667786A/zh
Publication of CN103667786A publication Critical patent/CN103667786A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐冲击的铜镍合金及其制备方法，铜镍合金由以下成分按照重量比组成：Ni为7.7wt%～8.4wt%、Pt为0.2wt%～0.4wt%、Ti为0.1wt%～0.3wt%、Rb为0.03wt%～0.06wt%、Os为0.04wt%～0.06wt%、余量为铜。铜镍合金的各组成成分通过高温熔合、冶炼、按照一定速率冷却等步骤制备得到耐冲击的铜镍合金。

Description

一种耐冲击的铜镍合金及其制备方法
技术领域
本发明涉及一种合金及其制备方法，特别是涉及一种耐冲击的铜镍合金及其制备方法。
背景技术
合金材料的冲击性对合金材料的性能有至关重要的作用，冲击性过弱，铜合金材料在受到外界的应力冲击时，铜合金材料会发生一定程度的扭曲和变形，如果外力冲击足够大，有可能会导致铜合金材料的断裂等现象发生。耐冲击性能是衡量铜合金材料性能好坏的一个重要的参数，现阶段成熟的铜合金材料的耐冲击性能都较差，不能完全的抵抗外力的冲击，需要提高铜合金材料的冲击性。
发明内容
要解决的技术问题：常规的铜合金材料耐冲击性能较低的问题。
技术方案：本发明公开了一种铜镍合金及其制备方法，铜镍合金由以下成分按照重量比组成：Ni为7.7wt%～8.4wt%、Pt为0.2wt%～0.4wt%、Ti为0.1wt%～0.3wt%、Rb为0.03wt%～0.06wt%、Os为0.04wt%～0.06wt%、余量为铜。
一种耐冲击的铜镍合金的制备方法，包括以下步骤：（1）调节熔炼炉温度为1300℃；（2）温度稳定后向熔炼炉中加入Ni为77kg～84kg、Pt为2kg～4kg、Ti为1kg～3kg；（3）在1300℃下熔炼5h；（4）再将熔炼炉升温至1800℃，加入Rb为0.3kg～0.6kg、Os为0.4kg～0.6kg、铜为907.8kg～919.3kg，熔炼5h；（5）按照45℃/s的速率将熔炼后的合金材料降至室温，得到铜镍合金。
在进行熔炼时，合金材料组成中加入的Ni的重量优选为77kg；熔炼时合金材料组成中加入Pt的重量优选为2kg；熔炼时合金材料组成中加入Ti的重量优选为3kg。
有益效果：本发明制备的铜镍合金具有良好的耐冲击性能，冲击韧性的测试标准为GB/T1817-1995，铜镍合金的冲击韧性为760至774J，具有良好的冲击韧性。
具体实施方式
实施例1
耐冲击的铜镍合金的制备方法包括以下步骤：（1）调节熔炼炉温度为1300℃；（2）温度稳定后向熔炼炉中加入Ni为84kg、Pt为4kg、Ti为3kg；（3）在1300℃下熔炼5h；（4）再将熔炼炉升温至1800℃，加入Rb为0.6kg、Os为0.6kg、铜为907.8kg，熔炼5h；（5）按照45℃/s的速率将熔炼后的合金材料降至室温，得到铜镍合金。
实施例2
耐冲击的铜镍合金的制备方法包括以下步骤：（1）调节熔炼炉温度为1300℃；（2）温度稳定后向熔炼炉中加入Ni为77kg、Pt为2kg、Ti为1kg；（3）在1300℃下熔炼5h；（4）再将熔炼炉升温至1800℃，加入Rb为0.3kg、Os为0.4kg、铜为919.3kg，熔炼5h；（5）按照45℃/s的速率将熔炼后的合金材料降至室温，得到铜镍合金。
实施例3
耐冲击的铜镍合金的制备方法包括以下步骤：（1）调节熔炼炉温度为1300℃；（2）温度稳定后向熔炼炉中加入Ni为80kg、Pt为3kg、Ti为2kg；（3）在1300℃下熔炼5h；（4）再将熔炼炉升温至1800℃，加入Rb为0.5kg、Os为0.6kg、铜为913.9kg，熔炼5h；（5）按照45℃/s的速率将熔炼后的合金材料降至室温，得到铜镍合金。
测定了实施例1、实施例2、实施例3制备的铜镍合金的冲击韧性。冲击韧性的测试标准为GB/T1817-1995，测定结果如下表。
  实施例1 实施例2 实施例3
冲击韧性（J） 774 760 766
实施例1、实施例2、实施例3的铜镍合金材料都具有良好的冲击韧性，可以用于抵抗外力的冲击。

Claims (5)

1.一种耐冲击的铜镍合金，其特征在于铜镍合金由以下成分按照重量比组成：Ni为7.7wt%～8.4wt%、Pt为0.2wt%～0.4wt%、Ti为0.1wt%～0.3wt%、Rb为0.03wt%～0.06wt%、Os为0.04wt%～0.06wt%、余量为铜。
2.根据权利要求1所述的一种耐冲击的铜镍合金的制备方法，其特征在于包括以下步骤：（1）调节熔炼炉温度为1300℃；（2）温度稳定后向熔炼炉中加入Ni为77kg～84kg、Pt为2kg～4kg、Ti为1kg～3kg；（3）在1300℃下熔炼5h；（4）再将熔炼炉升温至1800℃，加入Rb为0.3kg～0.6kg、Os为0.4kg～0.6kg、铜为907.8kg～919.3kg，熔炼5h；（5）按照45℃/s的速率将熔炼后的合金材料降至室温，得到铜镍合金。
3.根据权利要求2所述的一种耐冲击的铜镍合金的制备方法，其特征在于熔炼时加入Ni的重量为77kg。
4.根据权利要求2所述的一种耐冲击的铜镍合金的制备方法，其特征在于熔炼时加入Pt的重量为2kg。
5.根据权利要求2所述的一种耐冲击的铜镍合金的制备方法，其特征在于熔炼时加入Ti的重量为3kg。
CN201310638526.8A 2013-12-03 2013-12-03 一种耐冲击的铜镍合金及其制备方法 Pending CN103667786A (zh)