CN103657443B - 聚偏氟乙烯超滤膜 - Google Patents

聚偏氟乙烯超滤膜 Download PDF

Info

Publication number
CN103657443B
CN103657443B CN201310688680.6A CN201310688680A CN103657443B CN 103657443 B CN103657443 B CN 103657443B CN 201310688680 A CN201310688680 A CN 201310688680A CN 103657443 B CN103657443 B CN 103657443B
Authority
CN
China
Prior art keywords
ester
methyl
make
pvdf
polyvinylidene fluoride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310688680.6A
Other languages
English (en)
Other versions
CN103657443A (zh
Inventor
徐建林
邹建良
宗建青
仇峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu three Ai Fuzhenfu novel material company limited
Original Assignee
CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd filed Critical CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd
Priority to CN201310688680.6A priority Critical patent/CN103657443B/zh
Publication of CN103657443A publication Critical patent/CN103657443A/zh
Application granted granted Critical
Publication of CN103657443B publication Critical patent/CN103657443B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚偏氟乙烯超滤膜，通过如下步骤制成：1）将由45g/L聚偏氟乙烯单聚物、1g/L二丙酮醇、6g/L二甲亚砜、15g/L二甲基酰胺、2g/L烷基醇酰胺聚氧乙烷醚、5g/L二甲基乙酰胺、1g/L异丁基酮、1g/L正丁基乙酸酯、3g/L四甲基尿素、8g/L三甲基磷酸酯、1g/L甲酰胺、1g/L环己酮、1g/L乙酰乙酸乙基酯、1g/L乙二醇醚酯、3g/L油酸聚氧乙烯酯制备的铸膜液通入真空纤维刮膜模具，制成湿膜；2）在50℃将湿膜浸入充有由1-2g/L三乙基磷酸酯、15g/L甲醇、1g/L异佛乐酮、1g/L丙烯基碳酸酯、20g/L乙醇、25g/L异丙醇、1g/L乙二醇醚、1g/L甲异丁酮制备的凝胶液的沉淀槽，使之发生相转变制膜；3）在65℃干燥，形成多孔干膜。本发明聚偏氟乙烯超滤膜，其具有大量亚微米级的均匀孔隙，且强度大。

Description

聚偏氟乙烯超滤膜
技术领域
本发明涉及聚偏氟乙烯超滤膜。
背景技术
目前常用的聚偏氟乙烯超滤膜，强度性能不是很理想。
发明内容
本发明的目的在于提供一种聚偏氟乙烯超滤膜，其具有大量亚微米级的均匀孔隙，且强度大。
为实现上述目的，本发明的技术方案是设计一种聚偏氟乙烯超滤膜，通过如下步骤制成：
1）将由45g/L聚偏氟乙烯单聚物、1g/L二丙酮醇、6g/L二甲亚砜、15g/L二甲基酰胺、2g/L烷基醇酰胺聚氧乙烷醚、5g/L二甲基乙酰胺、1g/L异丁基酮、1g/L正丁基乙酸酯、3g/L四甲基尿素、8g/L三甲基磷酸酯、1g/L甲酰胺、1g/L环己酮、1g/L乙酰乙酸乙基酯、1g/L乙二醇醚酯、3g/L油酸聚氧乙烯酯制备的铸膜液通入真空纤维刮膜模具，制成湿膜；
2）在50℃将湿膜浸入充有由1-2g/L三乙基磷酸酯、15g/L甲醇、1g/L异佛乐酮、1g/L丙烯基碳酸酯、20g/L乙醇、25g/L异丙醇、1g/L乙二醇醚、1g/L甲异丁酮制备的凝胶液的沉淀槽，使之发生相转变制膜；
3）在65℃干燥，形成多孔干膜。
本发明的优点和有益效果在于：提供一种聚偏氟乙烯超滤膜，其具有大量亚微米级的均匀孔隙，且强度大。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种聚偏氟乙烯超滤膜，通过如下步骤制成：
1）将由45g/L聚偏氟乙烯单聚物、1g/L二丙酮醇、6g/L二甲亚砜、15g/L二甲基酰胺、2g/L烷基醇酰胺聚氧乙烷醚、5g/L二甲基乙酰胺、1g/L异丁基酮、1g/L正丁基乙酸酯、3g/L四甲基尿素、8g/L三甲基磷酸酯、1g/L甲酰胺、1g/L环己酮、1g/L乙酰乙酸乙基酯、1g/L乙二醇醚酯、3g/L油酸聚氧乙烯酯制备的铸膜液通入真空纤维刮膜模具，制成湿膜；
2）在50℃将湿膜浸入充有由1g/L三乙基磷酸酯、15g/L甲醇、1g/L异佛乐酮、1g/L丙烯基碳酸酯、20g/L乙醇、25g/L异丙醇、1g/L乙二醇醚、1g/L甲异丁酮制备的凝胶液的沉淀槽，使之发生相转变制膜；
3）在65℃干燥，形成多孔干膜。
实施例2
一种聚偏氟乙烯超滤膜，通过如下步骤制成：
1）将由45g/L聚偏氟乙烯单聚物、1g/L二丙酮醇、6g/L二甲亚砜、15g/L二甲基酰胺、2g/L烷基醇酰胺聚氧乙烷醚、5g/L二甲基乙酰胺、1g/L异丁基酮、1g/L正丁基乙酸酯、3g/L四甲基尿素、8g/L三甲基磷酸酯、1g/L甲酰胺、1g/L环己酮、1g/L乙酰乙酸乙基酯、1g/L乙二醇醚酯、3g/L油酸聚氧乙烯酯制备的铸膜液通入真空纤维刮膜模具，制成湿膜；
2）在50℃将湿膜浸入充有由2g/L三乙基磷酸酯、15g/L甲醇、1g/L异佛乐酮、1g/L丙烯基碳酸酯、20g/L乙醇、25g/L异丙醇、1g/L乙二醇醚、1g/L甲异丁酮制备的凝胶液的沉淀槽，使之发生相转变制膜；
3）在65℃干燥，形成多孔干膜。
实施例3
一种聚偏氟乙烯超滤膜，通过如下步骤制成：
1）将由45g/L聚偏氟乙烯单聚物、1g/L二丙酮醇、6g/L二甲亚砜、15g/L二甲基酰胺、2g/L烷基醇酰胺聚氧乙烷醚、5g/L二甲基乙酰胺、1g/L异丁基酮、1g/L正丁基乙酸酯、3g/L四甲基尿素、8g/L三甲基磷酸酯、1g/L甲酰胺、1g/L环己酮、1g/L乙酰乙酸乙基酯、1g/L乙二醇醚酯、3g/L油酸聚氧乙烯酯制备的铸膜液通入真空纤维刮膜模具，制成湿膜；
2）在50℃将湿膜浸入充有由1.2g/L三乙基磷酸酯、15g/L甲醇、1g/L异佛乐酮、1g/L丙烯基碳酸酯、20g/L乙醇、25g/L异丙醇、1g/L乙二醇醚、1g/L甲异丁酮制备的凝胶液的沉淀槽，使之发生相转变制膜；
3）在65℃干燥，形成多孔干膜。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.聚偏氟乙烯超滤膜，其特征在于，通过如下步骤制成：
1）将由45g/L聚偏氟乙烯单聚物、1g/L二丙酮醇、6g/L二甲亚砜、15g/L二甲基酰胺、2g/L烷基醇酰胺聚氧乙烷醚、5g/L二甲基乙酰胺、1g/L异丁基酮、1g/L正丁基乙酸酯、3g/L四甲基尿素、8g/L三甲基磷酸酯、1g/L甲酰胺、1g/L环己酮、1g/L乙酰乙酸乙基酯、1g/L乙二醇醚酯、3g/L油酸聚氧乙烯酯制备的铸膜液通入真空纤维刮膜模具，制成湿膜；
2）在50℃将湿膜浸入充有由1-2g/L三乙基磷酸酯、15g/L甲醇、1g/L异佛乐酮、1g/L丙烯基碳酸酯、20g/L乙醇、25g/L异丙醇、1g/L乙二醇醚、1g/L甲异丁酮制备的凝胶液的沉淀槽，使之发生相转变制膜；
3）在65℃干燥，形成多孔干膜。
CN201310688680.6A 2013-12-17 2013-12-17 聚偏氟乙烯超滤膜 Active CN103657443B (zh)