CN103645304B - 检测乳胶漆漆膜脱落的方法 - Google Patents
检测乳胶漆漆膜脱落的方法 Download PDFInfo
- Publication number
- CN103645304B CN103645304B CN201310626315.2A CN201310626315A CN103645304B CN 103645304 B CN103645304 B CN 103645304B CN 201310626315 A CN201310626315 A CN 201310626315A CN 103645304 B CN103645304 B CN 103645304B
- Authority
- CN
- China
- Prior art keywords
- paint
- constant
- emulsion paint
- paint film
- pull
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种检测乳胶漆漆膜脱落的方法，该方法是1）制备乳胶漆漆膜：先在砖面上批上两道水泥砂浆或混凝土，并通风干燥至含水率小于10%且pH值小于10；接着在砖面上再批上两道内墙腻子，待内墙腻子干燥后用砂纸打磨平整并将浮灰抹去；最后在砖面上再辊涂两道内墙乳胶漆后，在恒温恒湿环境中保养两天以上；2）将步骤1）已制备好乳胶漆漆膜的泥土砖漆膜朝上平放在容器中，往容器中加入水，当水位位于漆膜表面下方1‑5mm的距离后，停止加水，将容器置于恒温恒湿环境中放置一天以上，期间保持水位位于漆膜表面下方1‑5mm的距离，之后取出泥土砖，通过观察漆膜表面是否有鼓泡、开裂或脱落等破坏现象，判断乳胶漆漆膜是否会脱落以及可能产生的破坏程度。
Description
技术领域
本发明涉及乳胶漆漆膜性能测试领域，特别涉及一种检测乳胶漆漆膜脱落的方法。
背景技术
合成树脂乳液涂料俗称乳胶漆，是目前用于室内外装修最为主流的一种涂料，可对墙面起装饰和保护等作用；乳胶漆干燥后，保证漆膜不脱落是乳胶漆最基本的要求。
目前检测乳胶漆漆膜性能的方法有很多的项目，有抗藻性、防霉性、耐水性、耐候性、耐光性等，却没有一种检测是真实反映乳胶漆涂在墙体上，经过墙体的浸泡后，漆膜是否会脱落的方法；现实生活中有许多房子的外墙可能还是毛坯墙体，没有做过任何处理；特别是南方为多发雨季的地方，有时下雨就是十天半个月不停，在这种情况就容易导致内墙漆膜脱落；由于生活中我们砌墙的砖大多是用红色的泥土砖，其吸水性极强，连续下雨就像是整个墙体浸泡在水中一样，并且加速了内墙乳胶漆漆膜的老化。
发明内容
为了解决现有技术所存在的上述问题，本发明提供了一种检测乳胶漆漆膜脱落的方法，该方法是模拟有些现实外墙毛坯墙体的特性做出的乳胶漆漆膜性能检测，它可以方便快捷地检测判断乳胶漆漆膜是否会脱落以及可能产生的破坏程度，从而可以为消费者减少一部分损失，还可以指导施工队对待特定的墙体要特定处理，同时也为涂料生产商归避一些因乳胶漆漆膜脱落而受到投诉的风险。
本发明技术方案如下：
一种检测乳胶漆漆膜脱落的方法，其特征在于：包括如下步骤：
1）制备乳胶漆漆膜：选择至少一块泥土砖，按照以下方法在各泥土砖的其中一个砖面上制备乳胶漆漆膜：先在砖面上批上两道水泥砂浆或混凝土，并通风干燥至含水率小于10%且pH值小于10；接着在砖面上再批上两道内墙腻子，待内墙腻子干燥后用砂纸打磨平整并将浮灰抹去；最后在砖面上再辊涂两道内墙乳胶漆后，在恒温恒湿环境中保养两天以上；
2）将步骤1）已制备好乳胶漆漆膜的泥土砖漆膜朝上平放在容器中，往容器中加入水，当水位位于漆膜表面下方1-5mm的距离后，停止加水，将容器置于恒温恒湿环境中放置一天以上，期间保持水位位于漆膜表面下方1-5mm的距离，之后取出泥土砖，通过观察漆膜表面是否有鼓泡、开裂或脱落等破坏现象，判断乳胶漆漆膜是否会脱落以及可能产生的破坏程度。
步骤1）在恒温恒湿环境中保养的天数为7天；步骤2）将容器置于恒温恒湿环境中放置的天数为14天。
步骤1）中选择3块砖做平行检测。
较之现有技术而言，本发明的优点在于：本发明所述的检测乳胶漆漆膜脱落的方法是模拟有些现实外墙毛坯墙体的特性做出的乳胶漆漆膜性能检测，它可以方便快捷地检测判断乳胶漆漆膜是否会脱落以及可能产生的破坏程度，从而可以为消费者减少一部分损失，还可以指导施工队对待特定的墙体要特定处理，同时也为涂料生产商归避一些因乳胶漆漆膜脱落而受到投诉的风险。此外，还可以检测出乳胶漆漆膜的透气性。
具体实施方式
下面结合具体实施方式对本发明内容进行详细说明：
本发明的具体实施方式提供了一种检测乳胶漆漆膜脱落的方法，包括如下步骤：
1）制备乳胶漆漆膜：选择至少一块泥土砖，按照以下方法在各泥土砖的其中一个砖面上制备乳胶漆漆膜：先在砖面上批上两道水泥砂浆或混凝土，并通风干燥至含水率小于10%且pH值小于10；接着在砖面上再批上两道内墙腻子，待内墙腻子干燥后打磨平整并将浮灰抹去（可用400目砂纸打磨，用砂布抹灰）；最后在砖面上再辊涂两道内墙乳胶漆后，在恒温恒湿环境中保养两天以上；
2）将步骤1）已制备好乳胶漆漆膜的泥土砖漆膜朝上平放在容器中，往容器中加入水，当水位位于漆膜表面下方1-5mm的距离后，停止加水，将容器置于恒温恒湿环境中放置一天以上，期间保持水位位于漆膜表面下方1-5mm的距离，之后取出泥土砖，通过观察漆膜表面是否有鼓泡、开裂或脱落等破坏现象，判断乳胶漆漆膜是否会脱落以及可能产生的破坏程度。
步骤1）在恒温恒湿环境中保养的天数为7天；步骤2）将容器置于恒温恒湿环境中放置的天数为14天。
步骤1）中最好选择3块砖做平行检测。
具体实施时，可依据GB/T1766-2008涂层老化中的破坏变化程度等级方法来评判乳胶漆漆膜的破坏程度，评判标准可参见下表：
| 等级 | 变化程度 |
| 0 | 无变化，即无可觉察的变化 |
| 1 | 很轻微，即刚可觉察的变化 |
| 2 | 轻微，即有明显觉察的变化 |
| 3 | 中等，即有很明显觉察的变化 |
| 4 | 较大，即有较大的变化 |
| 5 | 严重，即有强的变化 |
上述具体实施方式只是对本发明的技术方案进行详细解释，凡是依据上述原理及精神在本发明基础上的改进、替代，都应在本发明的保护范围之内。
Claims (1)
1.一种检测乳胶漆漆膜脱落的方法，其特征在于：包括如下步骤：
1）制备乳胶漆漆膜：选择至少一块泥土砖，按照以下方法在各泥土砖的其中一个砖面上制备乳胶漆漆膜：先在砖面上批上两道水泥砂浆或混凝土，并通风干燥至含水率小于10%且pH值小于10；接着在砖面上再批上两道内墙腻子，待内墙腻子干燥后用砂纸打磨平整并将浮灰抹去；最后在砖面上再辊涂两道内墙乳胶漆后，在恒温恒湿环境中保养两天以上；
2）将步骤1）已制备好乳胶漆漆膜的泥土砖漆膜朝上平放在容器中，往容器中加入水，当水位位于漆膜表面下方1-5mm的距离后，停止加水，将容器置于恒温恒湿环境中放置一天以上，期间保持水位位于漆膜表面下方1-5mm的距离，之后取出泥土砖，通过观察漆膜表面是否有鼓泡、开裂或脱落破坏现象，判断乳胶漆漆膜是否会脱落以及可能产生的破坏程度；
步骤1）在恒温恒湿环境中保养的天数为7天；
步骤1）中选择3块砖做平行检测；
步骤2）将容器置于恒温恒湿环境中放置的天数为14天。