CN103643575A - 一种薯渣印刷纸浆的制备方法 - Google Patents
一种薯渣印刷纸浆的制备方法 Download PDFInfo
- Publication number
- CN103643575A CN103643575A CN201310673859.4A CN201310673859A CN103643575A CN 103643575 A CN103643575 A CN 103643575A CN 201310673859 A CN201310673859 A CN 201310673859A CN 103643575 A CN103643575 A CN 103643575A
- Authority
- CN
- China
- Prior art keywords
- paper pulp
- weight
- potato slag
- micrometers
- diameter smaller
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种薯渣印刷纸浆的制备方法,具体步骤如下:(1)利用蒸汽爆破法将经过清洗的干燥薯渣进行爆破,得到平均粒径在80微米以下的颗粒料;(2)将颗粒料放入水中,同时加入4,4’-二环己基甲烷二异氰酸酯、聚乙烯蜡、甘油松香酯和聚酰胺树脂,升温搅拌;(3)向步骤(2)得到的混合物中加入温度为40~50℃的水,同时加入明矾,搅拌后过滤,排出滤液,保留滤料;(4)将滤料投入反应釜,同时加入平均粒径为10微米以下的二氧化钛、淀粉、聚丙烯胺、脲醛树脂,搅拌即可。本纸浆制备出来的纸制品颜色鲜艳、坚韧耐用、印刷性好、使用寿命长,适用于大规模工业化生产。
Description
技术领域
本发明涉及印刷造纸技术领域,尤其是涉及一种绿色环保的纸浆制备方法。
背景技术
进入21世纪以后,随着科学技术的持续进步,人们的生活水平越来越高,各种物质供应极大丰富,其中纸制品也是随处可见。各种报刊、杂志、书籍、笔记本、便签纸、文件袋、打印纸,乃至纸箱、包装盒等的使用量极其庞大。制造这些纸制品大部分用的是植物纤维,其中又以木纤维的用量居多。然而,木材过度砍伐会带来一系列严重的环境问题,这些环境问题又会回过头来影响人们的生活质量。尽管现在社会上一直在提倡节约用纸,但是相比于大量的浪费,节约只是杯水车薪,因此开发利用废弃物制备的纸制品迫在眉睫。目前利用废弃物制备的纸制品主要有再生纸,再生纸是利用废旧纸品制造的纸制品,具有制造工艺复杂、颜色发黄发暗、纸质较厚较脆等缺点。
发明内容
针对现有技术存在的上述问题,本申请人提供了一种薯渣印刷纸浆的制备方法。本纸浆制备出来的纸制品颜色鲜艳、坚韧耐用、印刷性好、使用寿命长,适用于大规模工业化生产。
本发明的技术方案如下:
一种薯渣印刷纸浆的制备方法,具体步骤如下:
(1)利用蒸汽爆破法将100重量份的经过清洗的干燥薯渣进行爆破,得到平均粒径在80微米以下的颗粒料;
(2)将颗粒料放入30~70重量份的水中,同时加入7~10重量份4,4’-二环己基甲烷二异氰酸酯、1~3重量份聚乙烯蜡、3~5重量份甘油松香酯和0.5~2重量份聚酰胺树脂,升温至50~70℃,搅拌1~2小时;
(3)向步骤(2)得到的混合物中加入温度为40~50℃的水,同时加入1~3重量份的明矾,搅拌20~30分钟后过滤,排出滤液,保留滤料;
(4)将滤料投入反应釜,同时加入15~20重量份平均粒径为10微米以下的二氧化钛、3~4重量份淀粉、2~3重量份聚丙烯胺、0.3~0.5重量份脲醛树脂,在40~50℃下搅拌30~40分钟即可得到本薯渣印刷纸浆。
步骤(3)中所述水的重量份数为210~230份。
本发明有益的技术效果在于:
本发明首先利用蒸汽爆破法预处理薯渣,使其中大部分纤维断裂,纤维的长度变短,纤维素的氢键被破坏并重排,形成较多的化学活性点,使纤维素间结合成氢键的数目增加;同时这种变化使得粘结剂能够渗入到纤维素空间结构的内部,与纤维素分子的支链桥接的数目增多、结合力增强,使生产的纸品强度提高。同时蒸汽爆破可以使薯渣纤维中的灰分和木质素被分离开,在后续的清洗环节可以被容易的排除。
随后将爆破后的薯渣与各种起到粘结、桥连作用的助剂混合,使纤维分子上的化学活性点互相连接,成为三维网状的纤维结构。此时的三维结构较为牢固,因此加入热水清洗不会破坏这种结构,同时加入明矾可以促进木质素和灰分的沉淀,过滤后将木质素和灰分分离出来,得到纯度较高的三维网状薯渣纤维。然后加入填料、胶料和其他助剂,这样就得到了可以实用的纸浆。
具体实施方式
实施例1:
本发明制备了一种薯渣印刷纸浆,具体步骤如下:
(1)利用蒸汽爆破法将100kg的经过清洗的干燥薯渣进行爆破,得到平均粒径在80微米以下的颗粒料;
(2)将颗粒料放入30kg的水中,同时加入7kg4,4’-二环己基甲烷二异氰酸酯、1kg聚乙烯蜡、3kg甘油松香酯和0.5kg聚酰胺树脂,升温至50℃,搅拌1小时;
(3)向步骤(2)得到的混合物中加入温度为40℃的水,同时加入1kg的明矾,搅拌20分钟后过滤,排出滤液,保留滤料;
(4)将滤料投入反应釜,同时加入15kg平均粒径为10微米以下的二氧化钛、3kg淀粉、2kg聚丙烯胺、0.3kg脲醛树脂,在40℃下搅拌30分钟即可得到本薯渣印刷纸浆。
步骤(3)中所述水的重量份数为210kg。
实施例2:
本发明制备了一种薯渣印刷纸浆,具体步骤如下:
(1)利用蒸汽爆破法将100kg的经过清洗的干燥薯渣进行爆破,得到平均粒径在80微米以下的颗粒料;
(2)将颗粒料放入50kg的水中,同时加入9kg4,4’-二环己基甲烷二异氰酸酯、2kg聚乙烯蜡、4kg甘油松香酯和1.5kg聚酰胺树脂,升温至60℃,搅拌2小时;
(3)向步骤(2)得到的混合物中加入温度为45℃的水,同时加入2kg的明矾,搅拌25分钟后过滤,排出滤液,保留滤料;
(4)将滤料投入反应釜,同时加入18kg平均粒径为10微米以下的二氧化钛、4kg淀粉、3kg聚丙烯胺、0.4kg脲醛树脂,在45℃下搅拌35分钟即可得到本薯渣印刷纸浆。
步骤(3)中所述水的重量份数为220kg。
实施例3:
本发明制备了一种薯渣印刷纸浆,具体步骤如下:
(1)利用蒸汽爆破法将100kg的经过清洗的干燥薯渣进行爆破,得到平均粒径在80微米以下的颗粒料;
(2)将颗粒料放入70kg的水中,同时加入10kg4,4’-二环己基甲烷二异氰酸酯、3kg聚乙烯蜡、5kg甘油松香酯和2kg聚酰胺树脂,升温至70℃,搅拌2小时;
(3)向步骤(2)得到的混合物中加入温度为50℃的水,同时加入3kg的明矾,搅拌30分钟后过滤,排出滤液,保留滤料;
(4)将滤料投入反应釜,同时加入20kg平均粒径为10微米以下的二氧化钛、4kg淀粉、3kg聚丙烯胺、0.5kg脲醛树脂,在50℃下搅拌40分钟即可得到本薯渣印刷纸浆。
步骤(3)中所述水的重量份数为230kg。
Claims (2)
1.一种薯渣印刷纸浆的制备方法,其特征在于具体步骤如下:
(1)利用蒸汽爆破法将100重量份的经过清洗的干燥薯渣进行爆破,得到平均粒径在80微米以下的颗粒料;
(2)将颗粒料放入30~70重量份的水中,同时加入7~10重量份4,4’-二环己基甲烷二异氰酸酯、1~3重量份聚乙烯蜡、3~5重量份甘油松香酯和0.5~2重量份聚酰胺树脂,升温至50~70℃,搅拌1~2小时;
(3)向步骤(2)得到的混合物中加入温度为40~50℃的水,同时加入1~3重量份的明矾,搅拌20~30分钟后过滤,排出滤液,保留滤料;
(4)将滤料投入反应釜,同时加入15~20重量份平均粒径为10微米以下的二氧化钛、3~4重量份淀粉、2~3重量份聚丙烯胺、0.3~0.5重量份脲醛树脂,在40~50℃下搅拌30~40分钟即可得到本薯渣印刷纸浆。
2.根据权利要求1所述的薯渣印刷纸浆的制备方法,其特征在于步骤(3)中所述水的重量份数为210~230份。