CN103642348A - 外墙纳米防霉涂料 - Google Patents
外墙纳米防霉涂料 Download PDFInfo
- Publication number
- CN103642348A CN103642348A CN201310646139.9A CN201310646139A CN103642348A CN 103642348 A CN103642348 A CN 103642348A CN 201310646139 A CN201310646139 A CN 201310646139A CN 103642348 A CN103642348 A CN 103642348A
- Authority
- CN
- China
- Prior art keywords
- agent
- mildew
- good
- nano
- proof coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的外墙纳米防霉涂料的具体组分和重量比例是:水 15-21%;杀菌剂:0.1-0.2%;分散剂:0.3-0.6%;润湿剂:0.05-0.07%;消泡剂:2-2.15%;钛白粉:14-20%;纳米TiO2:8-10%;高岭土:7-10%;硅丙乳液 10-16%;防冻剂:26-32%;成膜助剂:0.05-0.08%;防霉剂:2.55-4%;流平剂:0.4-0.6%;PH值调节剂:适量;增稠剂:适量。该涂料具有耐候性好,光活性高,稳定性好,优异的耐碱性、耐水性,漆膜光亮,低柔韧性、附着性好。
Description
技术领域 本发明涉及一种涂料,特别涉及一种用于建筑物外墙表面的耐水、耐碱、耐沾污、耐候性、抗菌防霉、光催化活性等性能的水性涂料,属于化工涂料技术领域。
背景技术 在建筑领域普遍存在建筑物外墙表面易污染发霉和墙面水解粉化现象,是建筑领域的一项新公关任务。当前纵观国内整个涂料市场,外墙涂料品种较多,但多以具备保护、装饰功能为主,抗菌防霉功能性涂料大多是具有耐水性、耐碱性、耐沾污和较简单的防霉等性能,但效果都不是很好,其外墙涂料的抗菌防霉性能则略显薄弱。因此研究具有纳米材料的光催化活性功能的纳米抗菌防霉性的外墙涂料意义重大。
发明内容 本发明的目的是提供一种建筑物外墙表面涂料,该涂料具有耐候性好,光活性高,稳定性好,优异的耐碱性、耐水性,漆膜光亮,低柔韧性、附着性好。
本发明的外墙纳米防霉涂料的具体组分和重量比例是:
水 15-21%;杀菌剂:0.1-0.2%;分散剂:0.3-0.6%;润湿剂:0.05-0.07%;消泡剂:2-2.15%;钛白粉:14-20%;纳米TiO2:8-10%;高岭土:7-10%;硅丙乳液 10-16%;防冻剂:26-32%;成膜助剂:0.05-0.08%;防霉剂:2.55-4%;流平剂:0.4-0.6%;PH值调节剂:适量;增稠剂:适量。
本发明所使用的高岭土,其耐火度高,可达1770~1790℃。中、低可塑性,具良好的绝缘性和化学稳定性,较好的耐火性等理化性质。具有白度高、质软、易分散悬浮于水中、良好的可塑性和高的粘结性、优良的电绝缘性能;具有良好的抗酸溶性、很低的阳离子交换量、较好的耐火性等理化性质。化学稳定性好、阻燃。
本发明所使用的纳米TiO2的光催化活性功能,使涂膜具有活性高、稳定性好、无毒环保、价格低廉等优点,其耐擦洗、耐沾污性能极佳;能有效防止墙面因所处环境空气湿度大而产生霉斑,降解接触的细菌和有机污染物,解决日益严重的污染环境。
本发明所使用的硅丙乳液为基料,硅丙乳液是将含有不饱和键的有机硅单体与丙烯酸类单体加入合适的助剂,通过核壳包覆聚合工艺聚合而成的乳液。结合了有机硅耐高温性、耐候性、耐化学品性,疏水、表面能低不易污染性和丙烯酸类树脂的高保色性、柔韧性、附着性。是一种高耐候、高耐水、抗污染的环保型建筑用乳液及涂料。
本发明所使用的金红石钛白粉,保持了晶体结构致密和稳定,较强的遮盖力和消色力,有较好的分散性以及良好的外用耐久性。其性能与涂膜的遮盖力、耐候性及耐粉化性有着密切关系。
本发明所使用的水溶剂型弹性乳液,其优异的回弹性、柔韧性、耐积尘性和耐紫外线等性能,可有效地弥盖墙体细微裂纹,墙面的抗开裂性能极强,既保护和美化墙体的华丽,又无毒环保、无公害。
本发明所使用的干膜防霉剂,与配方的相容性好、PH值和光稳定性高,对颜色和液体的流变能力没有影响,对霉菌和藻类具有高活性,可以防止真菌在涂层上生长,保护外墙涂层不被细菌和真菌感染,因此具有独特的防霉功能。
本发明的目的是为了利用乳液和干膜防霉剂在配料中的相容性,使本外墙纳米抗菌防霉涂料具有耐水、耐碱、耐候、耐沾污和高弹性抗开裂性能;通过纳米TiO2的光催化活性,降解建筑物外墙涂层的污染物和有害物质,既发挥本涂料的强耐老化性和遮盖力,又突出体现纳米抗菌防霉涂料可抑制霉菌生长的耐沾污抗菌性能,保色保光性好,在光学作用下使外墙纳米抗菌防霉涂料产生光催化自清洁性,形成具有纳米自清洁抗菌型防霉涂料。
一般来说,纳米TiO2由于其具有活性高、稳定性好、耐水、耐碱、耐沾污、弹性抗开裂、防霉菌性强,无毒、价格低廉等优点,是目前应用最广泛的光催化材料,并且已经成功地应用于很多领域,如卫生洁具、光学仪表、涂料、玻璃、高速公路的护墙等建筑等领域,应用效果较好。
具体实施方式 下面是本发明的一个实例。本发明的外墙纳米防霉涂料的组成(重量百分比)及生产工艺为:
低速以每分钟200~400转依次加入16%的水、0.1%的杀菌剂、0.5%的分散剂、0.07%的润湿剂、2.15%的消泡剂,待10分钟搅拌均匀后,再依次加入20%的钛白粉、9%的TiO2、8%的高岭土后,进行高速1200转/min运转30分钟,再低速依次加入14%的硅丙乳液、27%的防冻剂、0.05%的成膜助剂、2.73%的防霉剂、0.4%的流平剂、适量的PH值调节剂和增稠剂,之后以每分钟600-800转进行搅拌40分钟,最后经过检验、过滤、称重包装。
依据本发明制作的建筑外墙用的纳米防霉涂料,其各项指标均达到外墙水性涂料GB/T9755-2001标准,无霉环保、无公害。关于外墙涂料所规定的要求,该外墙纳米抗菌防霉涂料集多项功能于一身,具有光催化活性,可降解涂膜污染物和有害物质,高弹性抗开裂和抗菌防霉功能,遮盖力强,化学稳定性好,不水解;漆膜光亮,在弱酸弱碱下稳定,耐候性好,防霉杀菌力强,其制作工艺简单,原料容易获得,成本低,产品抗菌防霉效果好,保色性好,可持久延长华丽的墙面寿命,可应用于多种建筑居室外墙体的防霉功能使用。
Claims (4)
1.本发明的外墙纳米防霉涂料的具体组分和重量比例是:
水 15-21%;杀菌剂:0.1-0.2%;分散剂:0.3-0.6%;润湿剂:0.05-0.07%;消泡剂:2-2.15%;钛白粉:14-20%;纳米TiO2:8-10%;高岭土:7-10%;硅丙乳液 10-16%;防冻剂:26-32%;成膜助剂:0.05-0.08%;防霉剂:2.55-4%;流平剂:0.4-0.6%;PH值调节剂:适量;增稠剂:适量。
2.根据权利要求1所述的外墙纳米防霉涂料,其特征是所说的纳米TiO2的光催化活性功能,使涂膜具有活性高、稳定性好、无毒环保、价格低廉等优点,其耐擦洗、耐沾污性能极佳;能有效防止墙面因所处环境空气湿度大而产生霉斑。
3.根据权利要求1所述的外墙纳米防霉涂料,其特征是所说的金红石钛白粉,保持了晶体结构致密和稳定,较强的遮盖力和消色力,有较好的分散性以及良好的外用耐久性。其性能与涂膜的遮盖力、耐候性及耐粉化性有着密切关系。
4.根据权利要求1所述的外墙纳米防霉涂料,其特征是所说的干膜防霉剂,与配方的相容性好、PH值和光稳定性高,保护外墙涂层不被细菌和真菌感染,因此具有独特的防霉功能。