CN103642238A - 一种耐高温绝缘硅橡胶添加剂 - Google Patents
一种耐高温绝缘硅橡胶添加剂 Download PDFInfo
- Publication number
- CN103642238A CN103642238A CN201310610431.5A CN201310610431A CN103642238A CN 103642238 A CN103642238 A CN 103642238A CN 201310610431 A CN201310610431 A CN 201310610431A CN 103642238 A CN103642238 A CN 103642238A
- Authority
- CN
- China
- Prior art keywords
- silicon rubber
- additive
- temperature insulation
- insulation silicon
- aluminium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐高温绝缘硅橡胶添加剂，包括氢氧化铝、偏硼酸、气相白炭黑、甲基乙基硅油、羟基硅油和耐热添加剂。使用本发明添加剂所制备的硅橡胶具有电绝缘性、耐漏电起痕、耐电弧、及实用的物理机械性能，适用于承受高电场的环境中。经测试，本发明制备的硅橡胶耐漏电起痕性可以达到4.5kV以上。
Description
技术领域
本发明涉及硅橡胶技术领域，特别是涉及一种耐高温绝缘硅橡胶添加剂。
背景技术
硅橡胶在建筑、交通运输、电子电器、化工、生物材料以及航空航天材料领域有着广泛的用途，其优良的耐热性、耐低温、绝缘性、抗震、抗压、抗磨特性使其有着很大的优势，但随着科技的发展，对其耐热性、绝缘性提出了更高的要求，要求硅橡胶在更高的温度下长期使用，且具有更好的绝缘性。通过配合技术和添加新助剂，改变交联方式及共聚、共混等改性技术，使硅橡胶能够在较高温度下得到更广泛的应用，且具有更好的绝缘性。
发明内容
本发明的目的就是针对上述存在的缺陷而提供一种耐高温绝缘硅橡胶添加剂。使用本发明添加剂所制备的硅橡胶具有电绝缘性、耐漏电起痕、耐电弧、及实用的物理机械性能，适用于承受高电场的环境中。经测试，本发明制备的硅橡胶耐漏电起痕性可以达到4.5kV以上。
本发明的一种耐高温绝缘硅橡胶添加剂技术方案为，包括氢氧化铝、偏硼酸、气相白炭黑、甲基乙基硅油、羟基硅油和耐热添加剂。
具体含有按重量比的以下成分：氢氧化铝20-55份、偏硼酸0.01-0.2份、气相白炭黑25-50 份、甲基乙基硅油2-5 份、羟基硅油1-5 份、耐热添加剂4-35 份。
所述耐热添加剂为含铈聚有机硅氧烷或纳米二氧化锡。
所述气相白炭黑为硅烷化处理疏水型气相白炭黑。
氢氧化铝采用硅烷偶联剂处理。
氢氧化铝粒径为3-15um。
该添加剂的加入量，按重量百分比为，每100份硅橡胶生胶加入添加剂35-80份。
本发明的有益效果为：本发明使用的耐热添加剂为含铈聚有机硅氧烷或纳米二氧化锡。其中，含铈聚有机硅氧烷是一种以铈为中心金属，以离子键与硅氧烷相连的有机硅聚合物。作为硅橡胶的耐热助剂，含铈硅氧烷与硅橡胶相容性好，在硅橡胶中的分散较为均匀，从而更好地提高硅橡胶的耐热性。纳米二氧化锡属于金红石，具有高熔点、热稳定性好、耐腐蚀、机械稳定性好等特点。羟基硅油和甲基乙基硅油在本组合物中起集中交联的作用，使其产生不均匀的集中交联，形成高度交联的据点，具有高抗撕裂性。
添加硅烷处理过的氢氧化铝粉末提高了硅橡胶的电性能, 满足高电压电绝缘体的要求，在配方中添加适量的偏硼酸, 使其在混炼过程中与结构化控制剂反应, 促进混炼硅橡胶的各组分混炼均匀, 使胶料的加工性能得到改善, 硫化硅橡胶机械强度得到提升。
本发明所制备的硅橡胶具有电绝缘性、耐漏电起痕、耐电弧及实用的物理机械性能，适用于承受高电场的环境中。经测试，本发明添加剂制备的硅橡胶耐漏电起痕性可以达到4.5kV以上，可以在330-360摄氏度的环境下长时间使用，撕裂强度可达32.3KN/m。
具体实施方式：
为了更好地理解本发明，下面用具体实例来详细说明本发明的技术方案，但是本发明并不局限于此。
实施例１
本发明的一种耐高温绝缘硅橡胶添加剂，具体含有按重量比的以下成分：氢氧化铝35份、偏硼酸0.05份、气相白炭黑40 份、甲基乙基硅油4份、羟基硅油3份、耐热添加剂35份。
所述耐热添加剂为含铈聚有机硅氧烷。
所述气相白炭黑为硅烷化处理疏水型气相白炭黑。
氢氧化铝采用硅烷偶联剂处理。
氢氧化铝粒径为3-15um。
该添加剂的加入量，按重量百分比为，每100份硅橡胶生胶加入添加剂35-80份。
经测试，本发明添加剂制备的硅橡胶耐漏电起痕性可以达到4.5kV以上，可以在330-360摄氏度的环境下长时间使用，撕裂强度可达32.3KN/m。
实施例2
本发明的一种耐高温绝缘硅橡胶添加剂，具体含有按重量比的以下成分：氢氧化铝55份、偏硼酸0.2份、气相白炭黑50 份、甲基乙基硅油5 份、羟基硅油5 份、耐热添加剂15 份。
所述耐热添加剂为纳米二氧化锡。
所述气相白炭黑为硅烷化处理疏水型气相白炭黑。
氢氧化铝采用硅烷偶联剂处理。
氢氧化铝粒径为3-15um。
该添加剂的加入量，按重量百分比为，每100份硅橡胶生胶加入添加剂35-80份。
经测试，本发明添加剂制备的硅橡胶耐漏电起痕性可以达到4.5kV以上，可以在330-360摄氏度的环境下长时间使用，撕裂强度可达30.9KN/m。
实施例3
本发明的一种耐高温绝缘硅橡胶添加剂，具体含有按重量比的以下成分：氢氧化铝25份、偏硼酸0.02份、气相白炭黑25 份、甲基乙基硅油3 份、羟基硅油5 份、耐热添加剂32 份。
所述耐热添加剂为含铈聚有机硅氧烷。
所述气相白炭黑为硅烷化处理疏水型气相白炭黑。
氢氧化铝采用硅烷偶联剂处理。
氢氧化铝粒径为3-15um。
该添加剂的加入量，按重量百分比为，每100份硅橡胶生胶加入添加剂35-80份。
经测试，本发明添加剂制备的硅橡胶耐漏电起痕性可以达到4.5kV以上，可以在330-360摄氏度的环境下长时间使用，撕裂强度可达32.1KN/m。
Claims (7)
1.一种耐高温绝缘硅橡胶添加剂，其特征在于，包括氢氧化铝、偏硼酸、气相白炭黑、甲基乙基硅油、羟基硅油和耐热添加剂。
2. 根据权利要求1所述的一种耐高温绝缘硅橡胶添加剂，其特征在于，含有按重量比的以下成分：氢氧化铝20-55份、偏硼酸0.01-0.2份、气相白炭黑25-50 份、甲基乙基硅油2-5 份、羟基硅油1-5 份、耐热添加剂4-35 份。
3. 根据权利要求2所述的一种耐高温绝缘硅橡胶添加剂，其特征在于，所述耐热添加剂为含铈聚有机硅氧烷或纳米二氧化锡。
4. 根据权利要求2所述的一种耐高温绝缘硅橡胶添加剂，其特征在于，所述气相白炭黑为硅烷化处理疏水型气相白炭黑。
5. 根据权利要求2所述的一种耐高温绝缘硅橡胶添加剂，其特征在于，氢氧化铝采用硅烷偶联剂处理。
6. 根据权利要求2所述的一种耐高温绝缘硅橡胶添加剂，其特征在于，氢氧化铝粒径为3-15um。
7. 根据权利要求2所述的一种耐高温绝缘硅橡胶添加剂，其特征在于，该添加剂的加入量，按重量百分比为，每100份硅橡胶生胶加入添加剂35-80份。