CN103641350A - 一种混凝土的抗裂改性剂 - Google Patents

一种混凝土的抗裂改性剂 Download PDF

Info

Publication number
CN103641350A
CN103641350A CN201310536293.0A CN201310536293A CN103641350A CN 103641350 A CN103641350 A CN 103641350A CN 201310536293 A CN201310536293 A CN 201310536293A CN 103641350 A CN103641350 A CN 103641350A
Authority
CN
China
Prior art keywords
parts
concrete
low
crack resistance
magnesium oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310536293.0A
Other languages
English (en)
Inventor
刘少兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO HUIERTONG TRADING Co Ltd
Original Assignee
QINGDAO HUIERTONG TRADING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO HUIERTONG TRADING Co Ltd filed Critical QINGDAO HUIERTONG TRADING Co Ltd
Priority to CN201310536293.0A priority Critical patent/CN103641350A/zh
Publication of CN103641350A publication Critical patent/CN103641350A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种混凝土的抗裂改性剂，由以下重量份数的原料制成：硫化铝2.5-3.7份、氧化镁1.3-2.6份、萘系减水剂0.5-1.6份、阿拉伯树胶2.3-4.6份、氯磺化聚乙烯2.5-4.5份、硫代硫酸铵1.2-1.8份、羧基丁苯乳胶1.6-5.8份和三元乙丙橡胶1.2-3份。本发明与现有的混凝土改性剂相比，表面韧性高，脆性低，改善混凝土的低温稳定性；使用本发明的混凝土导热系数下降，吸热值降低，热阻、冷阻值提高，温感性降低，沥青混凝土高低温稳定性变好，提高了混凝土铺装路面的抗裂性能，增加了铺装路面的使用年限，降低了维护成本。

Description

一种混凝土的抗裂改性剂
技术领域
本发明涉及一种混凝土的抗裂改性剂，属于建筑材料领域。  
背景技术
近年来，沥青公路事业发展较快，但沥青路面普遍存在技术和质量两个方面的问题，主要体现在公路工程的耐久性和路面的早期损害，尤其是在一些气候条件恶劣和交通荷载较大的路段，因此，对沥青混凝土的性能提出了更高的要求。通常，沥青混凝土得将经过加热的沥青与粗、细骨料及填充材料（矿粉、水泥等）按适当的配合比所拌合而成的均匀混合物经压实后得到。通常，沥青混凝土的温度稳定性是影响公路耐久性的主要因素，沥青混凝土的水稳定性是影响沥青路面早期破坏的主要因素，沥青混凝土路面由于稳定性不良，在未达到其设计使用年限就出现大量的龟裂、坑槽、剥落、集料脱落现象，甚至形成结构性破坏，不得不重修或养护，造成极大的资源浪费和经济损失。
发明内容
    针对现有技术存在的不足，本发明所要解决的技术问题是，提供一种混凝土的抗裂改性剂，稳定性好，在使用年限内出现龟裂、坑槽、剥落、集料脱落现象的可能性大大降低，降低了维护成本。
为解决上述技术问题，本发明采取的技术方案是，一种混凝土的抗裂改性剂，
由以下重量份数的原料制成：硫化铝2.5-3.7份、氧化镁1.3-2.6份、萘系减水剂0.5-1.6份、阿拉伯树胶2.3-4.6份、氯磺化聚乙烯2.5-4.5份、硫代硫酸铵1.2-1.8份、羧基丁苯乳胶1.6-5.8份和三元乙丙橡胶1.2-3份。
优化的，上述混凝土的抗裂改性剂，由以下重量份数的原料制成：
硫化铝3.3份、氧化镁2.4份、萘系减水剂1.2份、阿拉伯树胶3.8份、氯磺化聚乙烯3.2份、硫代硫酸铵1.5份、羧基丁苯乳胶3.2份和三元乙丙橡胶1.8份。
本发明与现有的混凝土改性剂相比，表面韧性高，脆性低，改善混凝土的低温稳定性；使用本发明的混凝土导热系数下降，吸热值降低，热阻、冷阻值提高，温感性降低，沥青混凝土高低温稳定性变好，提高了混凝土铺装路面的抗裂性能，增加了铺装路面的使用年限，降低了维护成本。  
具体实施方式
 实施例1
本发明为一种混凝土的抗裂改性剂，由以下重量份数的原料制成：
硫化铝3.3份、氧化镁2.4份、萘系减水剂1.2份、阿拉伯树胶3.8份、氯磺化聚乙烯3.2份、硫代硫酸铵1.5份、羧基丁苯乳胶3.2份和三元乙丙橡胶1.8份。
实施例2
本发明为一种混凝土的抗裂改性剂，由以下重量份数的原料制成：
硫化铝2.5份、氧化镁1.3份、萘系减水剂0.5份、阿拉伯树胶2.3份、氯磺化聚乙烯2.5份、硫代硫酸铵1.2份、羧基丁苯乳胶1.6份和三元乙丙橡胶1.2份。
实施例3
本发明为一种混凝土的抗裂改性剂，由以下重量份数的原料制成：
硫化铝3.7份、氧化镁2.6份、萘系减水剂1.6份、阿拉伯树胶4.6份、氯磺化聚乙烯4.5份、硫代硫酸铵1.8份、羧基丁苯乳胶5.8份和三元乙丙橡胶3份。
本发明与现有的混凝土改性剂相比，表面韧性高，脆性低，改善混凝土的低温稳定性；使用本发明的混凝土导热系数下降，吸热值降低，热阻、冷阻值提高，温感性降低，沥青混凝土高低温稳定性变好，提高了混凝土铺装路面的抗裂性能，增加了铺装路面的使用年限，降低了维护成本。
当然，上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改型、添加或替换，都应属于本发明的保护范围。

Claims (2)

1.一种混凝土的抗裂改性剂，其特征在于：由以下重量份数的原料制成：
硫化铝2.5-3.7份、氧化镁1.3-2.6份、萘系减水剂0.5-1.6份、阿拉伯树胶2.3-4.6份、氯磺化聚乙烯2.5-4.5份、硫代硫酸铵1.2-1.8份、羧基丁苯乳胶1.6-5.8份和三元乙丙橡胶1.2-3份。
2.根据权利要求1所述的混凝土的抗裂改性剂，其特征在于：
由以下重量份数的原料制成：硫化铝3.3份、氧化镁2.4份、萘系减水剂1.2份、阿拉伯树胶3.8份、氯磺化聚乙烯3.2份、硫代硫酸铵1.5份、羧基丁苯乳胶3.2份和三元乙丙橡胶1.8份。
CN201310536293.0A 2013-11-04 2013-11-04 一种混凝土的抗裂改性剂 Pending CN103641350A (zh)