CN103232617A - 一种用于sbs改性沥青的稳定剂组合物 - Google Patents

一种用于sbs改性沥青的稳定剂组合物 Download PDF

Info

Publication number
CN103232617A
CN103232617A CN2013101592581A CN201310159258A CN103232617A CN 103232617 A CN103232617 A CN 103232617A CN 2013101592581 A CN2013101592581 A CN 2013101592581A CN 201310159258 A CN201310159258 A CN 201310159258A CN 103232617 A CN103232617 A CN 103232617A
Authority
CN
China
Prior art keywords
sbs
parts
asphalt
modifying asphalt
stabiliser composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101592581A
Other languages
English (en)
Other versions
CN103232617B (zh
Inventor
韩凌
齐邦峰
张田英
李福起
卢德庆
姚秀杰
权栋
车金良
李虎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China National Offshore Oil Corp CNOOC
CNOOC Oil and Petrochemicals Co Ltd
CNOOC Research Institute of Refining and Petrochemicals Beijing Co Ltd
CNOOC Qingdao Heavy Oil Processing Engineering Technology Research Center Co Ltd
Original Assignee
CNOOC Qingdao Heavy Oil Processing Engineering Technology Research Center Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CNOOC Qingdao Heavy Oil Processing Engineering Technology Research Center Co Ltd filed Critical CNOOC Qingdao Heavy Oil Processing Engineering Technology Research Center Co Ltd
Priority to CN201310159258.1A priority Critical patent/CN103232617B/zh
Publication of CN103232617A publication Critical patent/CN103232617A/zh
Application granted granted Critical
Publication of CN103232617B publication Critical patent/CN103232617B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于SBS改性沥青的稳定剂组合物，该稳定剂组合物由硫化交联剂、促进剂、抗老化剂、抗氧化剂与活性剂组成，各组分的用量以重量份计为：硫化交联剂10-100份，促进剂5-95份，抗老化剂5-50份，抗氧化剂5-50份，活性剂5-50份。本发明稳定剂组合物可使SBS改性沥青具有更好的储存稳定性和低温性能，而且适用范围广，不仅适用于高芳香分沥青，也同样适用于较难稳定的低芳香分沥青生产SBS改性沥青，如中海油绥中沥青、中海油旅大氧化沥青等。

Description

一种用于SBS改性沥青的稳定剂组合物
技术领域
本发明涉及一种用于SBS改性沥青的稳定剂组合物。
背景技术
伴随公路建设的迅速发展和行驶车辆的重载化，人们对聚合物改性沥青的需求日益增长，SBS改性沥青具有优良的高温抗车辙、低温抗开裂、抗疲劳性能和优异的弹性恢复能力，主要应用于高速公路的上面层、重交通及超载车较多的路段等高等级路面。基于以上优异的路用性能，SBS改性沥青成为改性沥青中的主流产品。在生产SBS改性沥青的过程中，SBS改性剂与沥青因物理性质的差异，相容性不好，很容易发生分层现象，影响SBS改性沥青的储存稳定效果。为使SBS改性沥青不发生离析现象，最常见的方式是加入稳定剂进行化学改性，提高产品的的储存稳定性。
在改性沥青产品剪切和发育过程中，伴随着产品储存稳定性的增强，产品的老化和氧化作用逐渐加深，产品的低温性能受到严重制约，尤其中海油沥青芳香分含量低，与SBS相容性较差，沥青酸值高，抗老化和氧化的能力低，采用普通稳定剂易出现产品离析和低温指标无法同时满足的情况。
发明内容
针对现有稳定剂的不足，本发明提供一种用于SBS改性沥青的稳定剂组合物，该稳定剂组合物不仅能有效改善产品储存稳定性，而且对各种油源沥青具有普遍的适用性。
本发明的技术解决方案是：
一种用于SBS改性沥青的稳定剂组合物，其由硫化交联剂、促进剂、抗老化剂、抗氧化剂与活性剂组成，各组分的用量以重量份计为：硫化交联剂10-100份，促进剂5-95份，抗老化剂5-50份，抗氧化剂5-50份，活性剂5-50份。
上述硫化交联剂优选为硫磺、多聚磷酸、马来酸酐和1,4-苯醌中的一种或任意两种以上的混合物。
上述促进剂优选为二甲基二硫代氨基甲酸锌、异丙基黄原酸钠和N-叔丁基-2-双苯并噻唑次磺酰胺中的一种或任意两种以上的混合物。
上述抗老化剂和抗氧化剂分别优选为酮胺、醛胺和二芳仲胺中的一种或任意两种以上的混合物。
上述活性剂优选为金属氧化物、氢氧化物、氯化物、碱式碳酸盐和硬脂酸中的一种或任意两种以上的混合物。
本发明的有益技术效果是：
本发明稳定剂组合物可使SBS改性沥青具有更好的储存稳定性和低温性能，而且适用范围广，不仅适用于高芳香分沥青，也同样适用于较难稳定的低芳香分沥青生产SBS改性沥青，如中海油绥中沥青、中海油旅大氧化沥青等。而且本发明稳定剂组合物还具有原料丰富、价格低廉等优点。
具体实施方式
本发明的稳定剂组合物通过选取各组分的相互协同配合作用，可使最终制得的SBS改性沥青具有优良的储存稳定性和低温性能。稳定剂组合物中促进剂的作用为降低硫化温度，缩短硫化时间，促进SBS与硫化交联剂的交联反应，增加产量，降低生产成本；抗老化剂和抗氧化剂的作用为抑制改性沥青在剪切和搅拌过程中的氧化和老化，提高SBS改性沥青的使用性能；活性剂的作用为增加促进剂的活性，减少促进剂的用量，缩短硫化时间。
下面通过具体实施例对本发明进行说明：
实施例1
一种用于SBS改性沥青的稳定剂组合物，其是由下述重量份配比的原料制成：硫磺50份，二甲基二硫代氨基甲酸锌45份，6-乙氧基-2,2,4-三甲基-1,2-二氢化喹啉25份，乙醛-α-萘胺缩合物25份，氧化镁25份。
实施例2
一种用于SBS改性沥青的稳定剂组合物，其是由下述重量份配比的原料制成：多聚磷酸100份，异丙基黄原酸钠50份，6-乙氧基-2,2,4-三甲基-1,2-二氢化喹啉30份，乙醛-α-萘胺缩合物30份，氧化锌35份。
实施例3
一种用于SBS改性沥青的稳定剂组合物，其是由下述重量份配比的原料制成：硫磺20份，N-叔丁基-2-双苯并噻唑次磺酰胺30份，6-乙氧基-2,2,4-三甲基-1,2-二氢化喹啉25份，乙醛-α-萘胺缩合物25份，氯化镁10份。
实施例4
一种用于SBS改性沥青的稳定剂组合物，其是由下述重量份配比的原料制成：硫磺20份，马来酸酐10份，异丙基黄原酸钠5份，N-叔丁基-2-双苯并噻唑次磺酰胺30份，6-乙氧基-2,2,4-三甲基-1,2-二氢化喹啉25份，3-羟基丁醛-α-萘胺20份，碱式碳酸锌10份。
实施例5
一种用于SBS改性沥青的稳定剂组合物，其是由下述重量份配比的原料制成：1,4-苯醌60份，二甲基二硫代氨基甲酸锌30份，N-叔丁基-2-双苯并噻唑次磺酰胺10份，N-苯基-α-萘胺25份，乙醛-α-萘胺缩合物25份，硬脂酸25份。
实施例6
一种用于SBS改性沥青的稳定剂组合物，其是由下述重量份配比的原料制成：硫磺10份，1,4-苯醌60份，二甲基二硫代氨基甲酸锌30份，N-叔丁基-2-双苯并噻唑次磺酰胺10份，乙醛-α-萘胺缩合物50份，碱式碳酸锌25份，氢氧化钙10份。
上述实施例中制得稳定剂组合物在制备SBS改性沥青中的应用如下：
应用例1
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，高芳沥青A），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和65克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.0g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表3。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-C聚合物改性沥青技术要求。
应用例2
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，高芳沥青B），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和65克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.0g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表3。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-C聚合物改性沥青技术要求。
应用例3
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，中海油绥中沥青），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和65克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.2g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表3。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-C聚合物改性沥青技术要求。
应用例4
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，中海油旅大氧化沥青），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和65克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.5g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表3。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-C聚合物改性沥青技术要求。
应用例5
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，高芳沥青A），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和20克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.0g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表4。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-D聚合物改性沥青技术要求。
应用例6
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，高芳沥青B），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和20克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.0g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表4。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-D聚合物改性沥青技术要求。
应用例7
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，中海油绥中沥青），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和20克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.0g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表4。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-D聚合物改性沥青技术要求。
应用例8
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，中海油绥中沥青），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和20克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.5g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表4。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-D聚合物改性沥青技术要求。
应用例9
在反应桶中加入牌号为AH-70的基质沥青（质量指标见表1，中海油旅大氧化沥青），加热到沥青可流动后，加入49克SBS改性剂（牌号：YH-791，巴陵石化公司出产的产品）和20克相容剂（质量指标见表2，中海油减三线抽出油），缓慢加热并不定搅拌，使SBS充分溶胀，待温度升至185℃，以一定的剪切速率剪切1h后，加入本发明稳定剂组合物2.5g，再在183℃下充分搅拌一定时间得到SBS改性沥青产品，质量评价结果见表4。该SBS改性沥青质量符合《JTG F40-2004公路沥青路面施工技术规范》I-D聚合物改性沥青技术要求。
表1示出牌号为AH-70的基质沥青质量指标。
表1
Figure BDA00003138076400051
表2示出中海油减三线抽出油质量指标。
表2
项目 质量指标
饱和分 35
芳香分 47
胶质 12
沥青质 6
表3为I-C SBS改性沥青质量评价结果
表3
表4为I-D SBS改性沥青质量评价结果
表4
Figure BDA00003138076400062

Claims (5)

1.一种用于SBS改性沥青的稳定剂组合物，其特征在于该稳定剂组合物由硫化交联剂、促进剂、抗老化剂、抗氧化剂与活性剂组成，各组分的用量以重量份计为：硫化交联剂10-100份，促进剂5-95份，抗老化剂5-50份，抗氧化剂5-50份，活性剂5-50份。
2.根据权利要求1所述的一种用于SBS改性沥青的稳定剂组合物，其特征在于：所述硫化交联剂为硫磺、多聚磷酸、马来酸酐和1,4-苯醌中的一种或任意两种以上的混合物。
3.根据权利要求1所述的一种用于SBS改性沥青的稳定剂组合物，其特征在于：所述促进剂为二甲基二硫代氨基甲酸锌、异丙基黄原酸钠和N-叔丁基-2-双苯并噻唑次磺酰胺中的一种或任意两种以上的混合物。
4.根据权利要求1所述的一种用于SBS改性沥青的稳定剂组合物，其特征在于：所述抗老化剂和抗氧化剂分别为酮胺、醛胺和二芳仲胺中的一种或任意两种以上的混合物。
5.根据权利要求1所述的一种用于SBS改性沥青的稳定剂组合物，其特征在于：所述活性剂为金属氧化物、氢氧化物、氯化物、碱式碳酸盐和硬脂酸中的一种或任意两种以上的混合物。
CN201310159258.1A 2013-05-03 2013-05-03 一种用于sbs改性沥青的稳定剂组合物 Active CN103232617B (zh)