CN107954635A - 沥青混凝土改性剂 - Google Patents

沥青混凝土改性剂 Download PDF

Info

Publication number
CN107954635A
CN107954635A CN201810006603.0A CN201810006603A CN107954635A CN 107954635 A CN107954635 A CN 107954635A CN 201810006603 A CN201810006603 A CN 201810006603A CN 107954635 A CN107954635 A CN 107954635A
Authority
CN
China
Prior art keywords
modifying agent
parts
asphalt concrete
modified
additive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810006603.0A
Other languages
English (en)
Inventor
宋良友
燕同凯
蒋毓
田治宪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Keda Infrastructure Co Ltd
Original Assignee
Shandong Keda Infrastructure Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Keda Infrastructure Co Ltd filed Critical Shandong Keda Infrastructure Co Ltd
Priority to CN201810006603.0A priority Critical patent/CN107954635A/zh
Publication of CN107954635A publication Critical patent/CN107954635A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种沥青混凝土改性剂。包括下列重量份数的组分:生物胶100份,改性助剂10‑20份,功能助剂5‑15份。所述的改性助剂选自白炭黑、空心玻璃微珠、云母粉。所述的功能助剂选自异戊橡胶。本发明选择食品级的生物胶作为改性剂加入到沥青混凝土中,能够提高沥青混凝土的胁从性、抗疲劳性和抗剪能力,在高温条件下稳定性较好,具有良好的层间粘结度。本发明的沥青混凝土改性剂对沥青混凝土进行改性时,只需要将改性剂和待改性的沥青、矿粉简单拌合即可达到均匀分散的效果,不需要添加另外的设备,不会增加拌合难度。

Description

沥青混凝土改性剂
技术领域
[0001] 本发明涉及一种沥青混凝土改性剂,属于道路交通工程领域。
背景技术
[0002] 沥青路面具有良好的力学强度、耐磨耗、行车舒适、振动小、噪音低、施工简便等优 点。随着公路工程建设的大规模铺开,沥青路面在高等级道路中所占比例越来越大。传统的 沥青混凝土路面经常会出现裂缝现象,同时汽车数量的不断攀升,汽车尾气对环境造成的 污染成为重要的社会问题,需大力治理。
[0003] 沥青改性剂是指在沥青或沥青混合料中加入的天然或人工合成的有机或无机材 料,可熔融或分散在沥青中以改善或提高沥青的路用性能的物质。如为了提高沥青的机械 性能(强度和韧性等),就加入聚合物、树脂、塑料、炭黑、无机盐等增加强度和韧性的材料。 在沥青中加入改性剂的主要目的就是要改善沥青混合料在高温下的路用性能,减少高温时 的永久形变,提高其抗车辙、抗疲劳、抗老化,以及抵抗低温开裂或增加低温时抗疲劳能力 等方面的性能,使其满足设计使用期间交通条件的要求。
[0004] 改性沥青是在基质沥青中掺加改性剂,如橡胶、高分子聚合物,或其他填料等外掺 剂,或采取对沥青轻度氧化等方法,制成性能得到提高的沥青结合料。改性剂对沥青的改性 其机理有两种,一种使沥青化学组成改变的化学改性,另一种则是使改性剂均匀熔入沥青 中并且形成具有一定空间网络结构的物理改性。沥青改性剂是指在沥青加入天然的或人工 合成的有机或无机材料,可熔融、均匀的分散在沥青中,使沥青路面性能得到提高。
[0005] 沥青改性剂大体上可分为聚合沥青改性剂和非聚合沥青改性剂两类。聚合沥青改 性剂可分为热塑性弹性体沥青改性剂、塑料与合成树脂沥青改性剂、橡胶沥青改性剂和共 混型高分子聚合物沥青改性剂四类。而非聚合沥青改性剂是由矿物质和添加剂改性剂两类 构成的。
发明内容
[0006] 本发明要解决的技术问题是,提供一种沥青混凝土改性剂。
[0007] 本发明将改性生物胶应用到沥青混凝土改性剂上。所述的生物胶选自下列物质的 一种:瓜尔胶、卡拉胶、琼脂、阿拉伯胶、槐豆胶、果胶、魔芋胶、壳聚糖和黄原胶。本发明所述 的生物胶,其主要应用在食品添加剂上,作为增稠剂等应用。本发明通过对其改性,应用到 沥青混凝土改性剂上。
[0008] 根据上述应用,本发明还提供一种沥青混凝土改性剂,包括下列重量份数的组分: 生物胶100份,改性助剂10-20份,功能助剂5-15份。
[0009] 所述的改性助剂选自白炭黑、空心玻璃微珠、云母粉。
[0010] 所述的功能助剂选自异戊橡胶。
[0011] 本发明还提供一种沥青混凝土改性剂的制备方法,包括下列步骤: 将改性助剂、生物胶和功能助剂加入反应釜,在150_200°C条件下,反应体系压力保持 在0.5-1.5即3,搅拌反应1-211。
[0012] 本发明的有益效果: 本发明选择食品级的生物胶作为改性剂加入到沥青混凝土中,能够提高沥青混凝土的 胁从性、抗疲劳性和抗剪能力,在高温条件下稳定性较好,具有良好的层间粘结度。
[0013]本发明的沥青混凝土改性剂对沥青混凝土进行改性时,只需要将改性剂和待改性 的沥青、矿粉简单拌合即可达到均匀分散的效果,不需要添加另外的设备,不会增加拌合难 度。
具体实施方式
[0014] 实施例1 本实施例提供了一种沥青混凝土改性剂,包括生物胶100份,改性助剂10份,功能助剂 15份。
[0015] 生物胶选自瓜尔胶,改性助剂选自白炭黑,功能助剂选自异戊橡胶。
[0016] 沥青混凝土改性剂的制备方法,包括下列步骤: 将改性助剂、生物胶和功能助剂加入反应釜,在200°C条件下,反应体系压力保持在 lKPa,搅拌反应2h。
[0017] 实施例2 本实施例提供了一种沥青混凝土改性剂,包括下列重量份数的组分:生物胶100份,改 性助剂13份,功能助剂9份。
[0018] 生物胶选自卡拉胶,改性助剂选自空心玻璃微珠,功能助剂选自异戊橡胶。
[0019] 将改性助剂、生物胶和功能助剂加入反应釜,在200 °C条件下,反应体系压力保持 在1.5KPa,搅拌反应1.5h。
[0020] 实施例3 本实施例提供了一种沥青混凝土改性剂,包括下列重量份数的组分:生物胶100份,改 性助剂18份,功能助剂13份。
[0021] 生物胶选自阿拉伯胶,改性助剂选自云母粉,功能助剂选自异戊橡胶。
[0022] 沥青混凝土改性剂的制备方法,包括下列步骤: 将改性助剂、生物胶和功能助剂加入反应釜,在190 °C条件下,反应体系压力保持在 1.5KPa,搅拌反应2h。
[0023] 实施例4 将本发明实施例1-3的沥青混凝土改性剂应用到具体的沥青混凝土中,测定其性能参 数。
[0024] 测试用的改性沥青混凝土,包括下列重量分数的组分,粗细碎矿石100份、磁铁矿 15份、沥青30份、实施例1 -3中公开的改性剂10份。
[0025] 对照例的沥青混凝土不添加改性剂 进行性能测试。结果如下表
Figure CN107954635AD00051
当然,上述说明并非是对本发明的限制,本发明也并不限于上述举例,本技术领域的普 通技术人员,在本发明的实质范围内,作出的变化、改型、添加或替换,都应属于本发明的保 护范围。

Claims (6)

1. 改性生物胶在沥青混凝土改性剂上的应用。
2. 根据权利要求1所述的应用,所述的生物胶选自下列物质的一种:瓜尔胶、卡拉胶、琼 月旨、阿拉伯胶、槐豆胶、果胶、魔芋胶、壳聚糖和黄原胶。
3. —种沥青混凝土改性剂,其特征在于,包括下列重量份数的组分:生物胶100份,改性 助剂10-20份,功能助剂5-15份。
4. 根据权利要求3所述的沥青混凝土改性剂,其特征在于,所述的改性助剂选自白炭 黑、空心玻璃微珠、云母粉。
5. 根据权利要求3所述的沥青混凝土改性剂,其特征在于,所述的功能助剂选自异戊橡 胶。
6. —种沥青混凝土改性剂的制备方法,其特征在于,包括下列步骤: 将改性助剂、生物胶和功能助剂加入反应釜,在150-200°C条件下,反应体系压力保持 在0.5-1.5即3,搅拌反应1-211。
CN201810006603.0A 2018-01-04 2018-01-04 沥青混凝土改性剂 Pending CN107954635A (zh)