CN103638910B - 一种交联淀粉、富勒烯复合膜的制备方法 - Google Patents

一种交联淀粉、富勒烯复合膜的制备方法 Download PDF

Info

Publication number
CN103638910B
CN103638910B CN201310545647.8A CN201310545647A CN103638910B CN 103638910 B CN103638910 B CN 103638910B CN 201310545647 A CN201310545647 A CN 201310545647A CN 103638910 B CN103638910 B CN 103638910B
Authority
CN
China
Prior art keywords
fullerene
composite membrane
preparation
crosslinked starch
fullerene composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310545647.8A
Other languages
English (en)
Other versions
CN103638910A (zh
Inventor
苏建丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Lansuo Electronic Technology Co ltd
Original Assignee
Qingdao Wenchuang Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Wenchuang Technology Co Ltd filed Critical Qingdao Wenchuang Technology Co Ltd
Priority to CN201310545647.8A priority Critical patent/CN103638910B/zh
Publication of CN103638910A publication Critical patent/CN103638910A/zh
Application granted granted Critical
Publication of CN103638910B publication Critical patent/CN103638910B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种用于吸附金属离子的交联淀粉、富勒烯复合膜的制备方法，步骤为：(1)取富勒烯粉末，研磨后过200目筛；(2)取淀粉水溶液，加入富勒烯粉末，进行超声处理，使得富勒烯粉末与淀粉水溶液混合均匀，加入丙二胺溶液，微波下反应得制膜液；(3)取制膜液进行制膜，得到的丙二胺交联淀粉/富勒烯复合膜具有非常好的吸水性及较大的比表面积，有利于复合膜对重金属的吸附。

Description

一种交联淀粉、富勒烯复合膜的制备方法
技术领域
本发明涉及一种用于吸附金属离子的交联淀粉、富勒烯复合膜的制备方法，属材料加工领域。
技术背景
水对自然界和人类的生存发展起着不可替代的作用，随着社会的发展，水体的重金属污染越来越严重，重金属污染具有隐蔽性、长期性和不可逆性等特点。金属离子不可微生物降解、易在生物体内积累。由于各个行业排放的废水不同，废水的成分复杂，重金属离子种类多样，浓度波动性较大，给废水处理增加了难度。
发明内容
本发明的目的是提供一种用于吸附金属离子的交联淀粉、富勒烯复合膜的制备方法。
为实现以上目的，本发明的交联淀粉、富勒烯复合膜的制备方法，步骤为：
(1)取富勒烯粉末，研磨后过200目筛；
(2)取100mL质量浓度为2%的淀粉水溶液，加入富勒烯粉末，进行超声处理，使得富勒烯粉末与淀粉水溶液混合均匀，加入5mL质量浓度为1%的丙二胺溶液，在微波条件下，400r/min进行搅拌反应，得制膜液；
(3)取制膜液进行制膜，烘干后放入0.1mol/L的氢氧化钠溶液中浸泡揭膜，使用乙醇和蒸馏水反复冲洗，直至中性，自然晾干，得到丙二胺交联淀粉/富勒烯复合膜。
进一步的，所述富勒烯为C60。
进一步的，所述C60的用量为0.01-0.02g。
进一步的，所述微波功率为300-400W。
进一步的，所述反应温度为20-40℃，反应时间为5-15min。
本发明产生的有益效果为，本发明在微波加热条件下，通过丙二胺对淀粉进行交联，再与富勒烯进行复合，生成的交联淀粉/富勒烯复合膜具有非常好的吸水性，湿膜拉伸强度与干膜拉伸强度均有所提高，其中富勒烯的粒径小，能更好的分布于膜中，增大比表面积，有利于复合膜对重金属的吸附。
实施例
实施例1：
一种用于金属离子吸附的交联淀粉、富勒烯复合膜的制备方法为：
(1)取富勒烯粉末，研磨后过200目筛；
(2)取100mL质量浓度为2%的淀粉水溶液放入溶液中，加入0.01g富勒烯粉末，进行超声处理，使得富勒烯粉末与溶液混合均匀，加入5mL质量浓度为1%的丙二胺溶液，在微波条件下，400r/min搅拌反应，微波功率为300W，反应温度20℃，反应时间10min，得制膜液；
(3)取制膜液制膜，烘干后放入0.1mol/L的氢氧化钠溶液中浸泡揭膜，使用乙醇和蒸馏水反复冲洗，直至中性，自然晾干，得到丙二胺交联淀粉/富勒烯复合膜。
本实施例所制得的交联淀粉/富勒烯复合膜，吸水饱和后平均含水率为362%，湿膜拉伸强度61.2MPa，干膜拉伸强度88.3MPa，比表面积为57.7m2/g。
实施例2：
一种用于金属离子吸附的交联淀粉/富勒烯复合膜的制备方法为：
(1)取富勒烯粉末，研磨后过200目筛；
(2)取100mL质量浓度为2%的淀粉水溶液放入溶液中，加入0.02g富勒烯粉末，进行超声处理，使得富勒烯粉末与溶液混合均匀，加入5mL质量浓度为1%的丙二胺溶液，在微波条件下，400r/min搅拌反应一定时间，微波功率为350W，反应温度30℃，反应时间5min，得制膜液；
(3)取制膜液制膜，烘干后放入0.1mol/L的氢氧化钠溶液中浸泡揭膜，使用乙醇和蒸馏水反复冲洗，直至中性，自然晾干，得到丙二胺交联淀粉/富勒烯复合膜。
本实施例所制得的交联淀粉/富勒烯复合膜，吸水饱和后平均含水率为367%，湿膜拉伸强度69.2MPa，干膜拉伸强度86.8MPa，比表面积为58.5m2/g。
实施例3：
一种用于金属离子吸附的交联淀粉、富勒烯复合膜的制备方法为：
(1)取富勒烯粉末，研磨后过200目筛；
(2)取100mL质量浓度为2%的淀粉水溶液放入溶液中，加入0.02g富勒烯粉末，进行超声处理，使得富勒烯粉末与溶液混合均匀，加入5mL质量浓度为1%的丙二胺溶液，在微波条件下400r/min搅拌反应一定时间，，微波功率为400W，反应温度40℃，反应时间10min，得制膜液；
(3)取制膜液制膜，烘干后放入0.1mol/L的氢氧化钠溶液中浸泡揭膜，使用乙醇和蒸馏水反复冲洗，直至中性，自然晾干，得到丙二胺交联淀粉/富勒烯复合膜。
本实施例所制得的交联淀粉/富勒烯复合膜，吸水饱和后平均含水率为351%，湿膜拉伸强度63.2MPa，干膜拉伸强度73.9MPa，比表面积为59.1m2/g。

Claims (5)

1.一种交联淀粉、富勒烯复合膜的制备方法，其特征在于：步骤为：
(1)取富勒烯粉末，研磨后过200目筛；
(2)取100mL质量浓度为2%的淀粉水溶液，加入富勒烯粉末，进行超声处理，使得富勒烯粉末与淀粉水溶液混合均匀，加入5mL质量浓度为1%的丙二胺溶液，在微波条件下，400r/min进行搅拌反应，得制膜液；
(3)取制膜液进行制膜，烘干后放入0.1mol/L的氢氧化钠溶液中浸泡揭膜，使用乙醇和蒸馏水反复冲洗，直至中性，自然晾干，得到丙二胺交联淀粉/富勒烯复合膜。
2.根据权利要求1所述的一种交联淀粉、富勒烯复合膜的制备方法，其特征在于：所述富勒烯为C60。
3.根据权利要求2所述的一种交联淀粉、富勒烯复合膜的制备方法，其特征在于：所述C60的用量为0.01-0.02g。
4.根据权利要求1所述的一种交联淀粉、富勒烯复合膜的制备方法，其特征在于：所述微波功率为300-400W。
5.根据权利要求1所述的一种交联淀粉、富勒烯复合膜的制备方法，其特征在于：所述反应温度为20-40℃，反应时间为5-15min。
CN201310545647.8A 2013-11-07 2013-11-07 一种交联淀粉、富勒烯复合膜的制备方法 Active CN103638910B (zh)