CN103628350B - 一种阻燃性碳纤维电热纸及其制备方法 - Google Patents

一种阻燃性碳纤维电热纸及其制备方法 Download PDF

Info

Publication number
CN103628350B
CN103628350B CN201310311069.1A CN201310311069A CN103628350B CN 103628350 B CN103628350 B CN 103628350B CN 201310311069 A CN201310311069 A CN 201310311069A CN 103628350 B CN103628350 B CN 103628350B
Authority
CN
China
Prior art keywords
carbon fiber
paper
powder
fire resistance
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310311069.1A
Other languages
English (en)
Other versions
CN103628350A (zh
Inventor
程坤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI IDEAR FOR WARM LIFE ENVIRONMENT TECHNOLOGY Co Ltd
Original Assignee
ANHUI IDEAR FOR WARM LIFE ENVIRONMENT TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI IDEAR FOR WARM LIFE ENVIRONMENT TECHNOLOGY Co Ltd filed Critical ANHUI IDEAR FOR WARM LIFE ENVIRONMENT TECHNOLOGY Co Ltd
Priority to CN201310311069.1A priority Critical patent/CN103628350B/zh
Publication of CN103628350A publication Critical patent/CN103628350A/zh
Application granted granted Critical
Publication of CN103628350B publication Critical patent/CN103628350B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种阻燃性碳纤维电热纸及其制备方法，其由下列重量份的原料制成：碳纤维70-80、木浆50-60、明胶3-4、聚乙烯醇1-2、木质素2-3、交联剂TAC1-2、聚乙烯吡咯烷酮2-3、硼砂1-2、氢氧化铝12-13、过硫酸铵1-2、葡萄籽油1-2、改性云母粉3-4；本发明原料配方中增加了氢氧化铝，具有较好的阻燃性能，使得本发明电热纸使用安全，不会引起火灾。本发明碳纤维纸中的碳纤维整体分散均匀，抗折性好，不易撕裂、破损，可以便于加工成不同温度要求的面状发热体。

Description

一种阻燃性碳纤维电热纸及其制备方法
技术领域
本发明涉及到一种电热材料技术领域，具体是一种阻燃性碳纤维电热纸及其制备方法。
背景技术
碳纤维纸是使用碳纤维或活性碳纤维及碳纤维或活性碳纤维与其它植物或非植物纤维混合生产的具有特殊性能的功能纸。碳纤维纸具备许多优良特性，如导电、导热、多孔、吸附性等，因而被广泛应用于能源、军事、环保、土木、电子电器、采暖等领域。现有的碳纤维纸主要由碳纤维与纸浆复合制成纸，这种纸存在电阻不均匀，碳纤维在纸中分散不均匀，导致发热不均匀，而且，纸容易折断，牢度不高，易撕裂等。
发明内容
本发明的目的是提供一种阻燃性碳纤维电热纸及其制备方法。生产的碳纤维纸表面电阻均匀，耐热性好，具有较好的阻燃性能，使用安全，牢度高，不易撕裂、破损。
本发明的技术方案如下：
一种阻燃性碳纤维电热纸，其特征在于由下列重量份的原料制成：碳纤维70-80、木浆50-60、明胶3-4、聚乙烯醇1-2、木质素2-3、交联剂TAC1-2、聚乙烯吡咯烷酮2-3、硼砂1-2、氢氧化铝12-13、过硫酸铵1-2、葡萄籽油1-2、改性云母粉3-4；所述的改性云母粉由下列重量份的原料制成：云母粉10-12、凹凸棒土3-4、氮化铝1-2、柠檬酸正丁酯2-3、石油磺酸钡2-3、偏硅酸钠2-3、硅烷偶联剂KH5502-3、二甲基硅油2-3、聚乙烯醇2-3、吗啉1-2；制备方法是：将各物料混合，加入到8-10倍量云母粉的水中，加热至95-100℃，搅拌煮2-3小时，冷却后，脱水烘干，研磨得到200-300目粉末，再在粉末上喷洒相当于云母粉重量1-2%的氯化石蜡，混匀即可。
所述的碳纤维纸的制备方法，其特征在于包括以下步骤：
（1）、将木质素、交联剂TAC、聚乙烯吡咯烷酮、硼砂、氢氧化铝加入50-60重量份的水中，加热至70-75℃，搅拌40-55分钟，再加入过硫酸钠，搅拌反应30-45分钟；
（2）、将碳纤维、木浆、明胶、聚乙烯醇及适量水混合打浆，得到浓度为5.8～7.8%的碳纤维纸浆；再加入步骤（1）反应物料加入纸浆中，加水及其它剩余物料在75-78℃下磨浆，得到浓度为1.8～2.6%的纸浆；
（3）、纸浆经网部及压榨部脱水成形，湿纸页进入前干阶段进行烘干，生产出碳纤维电热纸。
本发明原料配方中增加了氢氧化铝，具有较好的阻燃性能，使得本发明电热纸使用安全，不会引起火灾。本发明碳纤维纸中的碳纤维整体分散均匀，抗折性好，不易撕裂、破损，可以便于加工成不同温度要求的面状发热体。
具体实施方式
所述的改性云母粉由下列重量份（公斤）的原料制成：云母粉12、凹凸棒土3、氮化铝2、柠檬酸正丁酯2、石油磺酸钡2、偏硅酸钠3、硅烷偶联剂KH5502、二甲基硅油2、聚乙烯醇2、吗啉2；制备方法是：将各物料混合，加入到8-10倍量云母粉的水中，加热至95-100℃，搅拌煮2-3小时，冷却后，脱水烘干，研磨得到200-300目粉末，再在粉末上喷洒相当于云母粉重量1-2%的氯化石蜡，混匀即可。
用此工艺制备的碳纤维纸，测试600mm×400mm面积的电阻值(电极方向为长度方向)，其值为440Ω。使用220V的交流电压进行通电测试，其表面平均温度为44℃，在其表面上的10处不同的位置测试其温度分布，温度偏差小于3℃。抗拉强度为：11Mpa。

Claims (2)

1.一种阻燃性碳纤维电热纸，其特征在于由下列重量份的原料制成：碳纤维70-80、木浆50-60、明胶3-4、聚乙烯醇1-2、木质素2-3、交联剂TAC1-2、聚乙烯吡咯烷酮2-3、硼砂1-2、氢氧化铝12-13、过硫酸铵1-2、葡萄籽油1-2、改性云母粉3-4；所述的改性云母粉由下列重量份的原料制成：云母粉10-12、凹凸棒土3-4、氮化铝1-2、柠檬酸正丁酯2-3、石油磺酸钡2-3、偏硅酸钠2-3、硅烷偶联剂KH5502-3、二甲基硅油2-3、聚乙烯醇2-3、吗啉1-2；制备方法是：将各物料混合，加入到8-10倍量云母粉的水中，加热至95-100℃，搅拌煮2-3小时，冷却后，脱水烘干，研磨得到200-300目粉末，再在粉末上喷洒相当于云母粉重量1-2%的氯化石蜡，混匀即可。
2.根据权利要求1所述的一种阻燃性碳纤维电热纸的制备方法，其特征在于包括以下步骤：
（1）、将木质素、交联剂TAC、聚乙烯吡咯烷酮、硼砂、氢氧化铝加入50-60重量份的水中，加热至70-75℃，搅拌40-55分钟，再加入过硫酸铵，搅拌反应30-45分钟；
（2）、将碳纤维、木浆、明胶、聚乙烯醇及适量水混合打浆，得到浓度为5.8~7.8%的碳纤维纸浆；再将步骤（1）反应物料加入纸浆中，加水及其它剩余物料在75-78℃下磨浆，得到浓度为1.8~2.6%的纸浆；
（3）、纸浆经网部及压榨部脱水成形，湿纸页进入前干阶段进行烘干，生产出碳纤维电热纸。
CN201310311069.1A 2013-07-23 2013-07-23 一种阻燃性碳纤维电热纸及其制备方法 Expired - Fee Related CN103628350B (zh)