CN103627369A - 研磨膏及其制备方法 - Google Patents

研磨膏及其制备方法 Download PDF

Info

Publication number
CN103627369A
CN103627369A CN201310673755.3A CN201310673755A CN103627369A CN 103627369 A CN103627369 A CN 103627369A CN 201310673755 A CN201310673755 A CN 201310673755A CN 103627369 A CN103627369 A CN 103627369A
Authority
CN
China
Prior art keywords
silicon carbide
water
preparation
lotion
quality
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310673755.3A
Other languages
English (en)
Other versions
CN103627369B (zh
Inventor
刘圣淮
周忠旺
刘跃
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XINGHUA TAILIN MACHINERY Co Ltd
Original Assignee
XINGHUA TAILIN MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XINGHUA TAILIN MACHINERY Co Ltd filed Critical XINGHUA TAILIN MACHINERY Co Ltd
Priority to CN201310673755.3A priority Critical patent/CN103627369B/zh
Publication of CN103627369A publication Critical patent/CN103627369A/zh
Application granted granted Critical
Publication of CN103627369B publication Critical patent/CN103627369B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种研磨膏的制备方法，步骤包括：1）选取碳化硅磨料：80#～220#，标准采用GB/T2480-1996；2）膏体制备；3）将步骤1）的碳化硅磨料加入膏体中，混合均匀；碳化硅磨料与膏体的质量百分比为：碳化硅磨料25%～35%，膏体65%～75%。本研磨膏的用途是作为高尔夫球场草坪剪草机械的刀片专用研磨膏。

Description

研磨膏及其制备方法
技术领域
本发明涉及金属研磨制品，具体是一种研磨膏，它是专用于高尔夫球场等草坪用的剪草机械刀片进行研磨。
背景技术
对于高尔夫球场来说，包括球道草，一般是早熟禾、高羊茅、黑麦草等三种按特定比例混合种植，一年四季青，抗病。这三种草都要修剪的，不修剪它就结籽，草就老化；还包括果岭草，也就是匍匐翦股颖，匍匐茎生长，长势低，高5CM左右，有帕特、攀可斯等草种。高尔夫球场草坪是用专用修剪机修剪的，养护要好。而高尔夫球场专用修剪机的研磨刀片有其特殊性，基本上每天都要研磨刀组。研磨后需及时清洗干净，且要求清洗液体对草坪不能有伤害。
现有的金属研磨膏体，通常由油脂、机油与磨料混合而成，研磨性能上能够研磨出锋刃，却油腻沾刀，不易清洗，膏体容易沉淀，用时需现场搅拌。特别是其属油性，对草有伤害，影响草坪生长。
发明内容
针对以上问题，本发明以聚乙二醇为基础膏体，碳化硅为磨料，混合成水溶性研磨膏体，具体技术方案如下：
一种研磨膏，其用途是高尔夫球场等草坪用的剪草机械刀片专用研磨膏。本研磨膏的制备方法，步骤包括：
1）选取碳化硅磨料：80#～220#，标准采用GB/T2480-1996；
2）膏体制备：
2.1）先将聚乙二醇加热熔化；
2.2）然后，加入水，水的加入质量为聚乙二醇熔液质量的1.8～2.5倍，边加水边搅拌后成胶体；
2.3）而后，在胶体中加水，水的加入质量为胶状物质量的1.8～2.5倍，边加水边搅拌，然后冷却至室温，结成膏体；
3）将步骤1）的碳化硅磨料加入膏体中，混合均匀；碳化硅磨料与膏体的质量百分比为：碳化硅磨料25%～35%，膏体65%～75%。
所述步骤1）中，碳化硅磨料为黑碳化硅或绿碳化硅。
所述步骤2.1）中，聚乙二醇加热到80～96℃。
所述步骤2.1）中，聚乙二醇加热到90℃。
所述步骤2.2）中，加入水的水温与聚乙二醇熔液的温度差不超过8℃；所述步骤2.3）中，加入水的水温与胶体的温度差不超过5℃。
所述步骤2.2）中，水的加入质量为聚乙二醇熔液质量的2倍；所述步骤2.3）中，水的加入质量为胶状物质量的2倍。
所述步骤3）中，碳化硅磨料与膏体的质量百分比为：碳化硅30%，膏体70%。
本发明的效果说明如下：
因聚乙二醇易溶于水，不象油脂那样沾刀，故此研磨膏易于清洗，刀具研磨后用水很容易清洗干净。聚乙二醇本身具有润滑性，且有适中的粘度，在研磨中能含住磨料，故能保证膏体的研磨性能。此膏体的保持性较好，不会发生磨料沉淀。保证随取随用，无需进行任何调配。满足日常使用方便要求。其基本成份为聚乙二醇，中性，对草坪无害。
具体实施方式
下面结合具体实施例对本技术方案进一步说明如下：
一种研磨膏，其用途是高尔夫球场等草坪用的剪草机械刀片专用研磨膏。本研磨膏的制备方法，步骤包括：
1）选取碳化硅磨料：80#～220#，标准采用GB/T2480-1996；
2）膏体制备：
2.1）先将聚乙二醇加热熔化；
2.2）然后，加入水，水的加入质量为聚乙二醇熔液质量的1.8～2.5倍，边加水边搅拌后成胶体；
2.3）而后，在胶体中加水，水的加入质量为胶状物质量的1.8～2.5倍，边加水边搅拌，然后冷却至常温（本方案中指25%），结成膏体；
3）将步骤1）的碳化硅磨料加入膏体中，混合均匀；碳化硅磨料与膏体的质量百分比为：碳化硅磨料25%～35%，膏体65%～75%。
经过试验，碳化硅磨料一般选用黑碳化硅即可满足日常作业要求，而对于修剪机器的刀具为高端的硬质合金等，则要用绿碳化硅，才能确保刀具刃口的锋利。
经过试验，聚乙二醇加热到80～96℃后能确保其与水混合良好。作为优选，聚乙二醇加热到90℃，在该温度下聚乙二醇的流动性以及与水的混合为最优。
经过试验，步骤2.2）中，加入水的水温与聚乙二醇熔液的温度差不超过8℃；所述步骤2.3）中，加入水的水温与胶体的温度差不超过5℃。温差大于该温度时候，水对聚乙二醇以及胶体的温度带来的影响陡增，造成混合效果变坏。
经过试验，优选的方案是，步骤2.2）中，水的加入质量为聚乙二醇熔液质量的2倍；所述步骤2.3）中，水的加入质量为胶状物质量的2倍。该质量比例下，所得到胶体和膏体混合状态最稳定，久置后未见分层等现象。
经过试验，碳化硅磨料与膏体的质量百分比为：碳化硅30%，膏体70%。在该比例下，碳化硅颗粒由膏体包裹效果最好，而且碳化硅散布均匀、密度最适宜刀具的研磨。

Claims (9)

1.一种研磨膏的制备方法，其特征是步骤包括：
1）选取碳化硅磨料：80#～220#，标准采用GB/T2480-1996；
2）膏体制备：
2.1）先将聚乙二醇加热熔化；
2.2）然后，加入水，水的加入质量为聚乙二醇熔液质量的1.8～2.5倍，边加水边搅拌后成胶体；
2.3）而后，在胶体中加水，水的加入质量为胶状物质量的1.8～2.5倍，边加水边搅拌，然后冷却至常温，结成膏体；
3）将步骤1）的碳化硅磨料加入膏体中，混合均匀；碳化硅磨料与膏体的质量百分比为：碳化硅磨料25%～35%，膏体65%～75%。
2.根据权利要求1所述的制备方法，其特征是所述步骤1）中，碳化硅磨料为黑碳化硅或绿碳化硅。
3.根据权利要求1所述的制备方法，其特征是所述步骤2.1）中，聚乙二醇加热到80～96℃。
4.根据权利要求1所述的制备方法，其特征是所述步骤2.1）中，聚乙二醇加热到90℃。
5.根据权利要求1所述的制备方法，其特征是所述步骤2.2）中，加入水的水温与聚乙二醇熔液的温度差不超过8℃；所述步骤2.3）中，加入水的水温与胶体的温度差不超过5℃。
6.根据权利要求1所述的制备方法，其特征是所述步骤2.2）中，水的加入质量为聚乙二醇熔液质量的2倍；所述步骤2.3）中，水的加入质量为胶状物质量的2倍。
7.根据权利要求1所述的制备方法，其特征是所述步骤3）中，碳化硅磨料与膏体的质量百分比为：碳化硅30%，膏体70%。
8.一种研磨膏，其特征是本研磨膏由权利要求1～7任一方法制备得到。
9.一种研磨膏，其特征是本研磨膏的用途是作为高尔夫球场草坪剪草机械的刀片专用研磨膏。
CN201310673755.3A 2013-12-11 2013-12-11 研磨膏及其制备方法 Active CN103627369B (zh)