CN103627038A - 一种高强度橡胶衬里配方 - Google Patents
一种高强度橡胶衬里配方 Download PDFInfo
- Publication number
- CN103627038A CN103627038A CN201210302377.3A CN201210302377A CN103627038A CN 103627038 A CN103627038 A CN 103627038A CN 201210302377 A CN201210302377 A CN 201210302377A CN 103627038 A CN103627038 A CN 103627038A
- Authority
- CN
- China
- Prior art keywords
- rubber
- kilograms
- carbon black
- formula
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高强度橡胶衬里配方，它涉及应用于钢橡复合管道衬胶的制作领域。它的配方组成为：3#烟片10-15kg、顺丁胶10-15kg、丁苯胶5-10kg、炭黑18-20kg、白炭黑6-8kg、硅烷偶联剂1-1.5kg、再生胶短纤维4-8kg、硫磺0.5-0.8kg、防老剂0.5-0.8kg、活性剂1.5-2.0kg、促进剂0.5-1.0kg、软化剂5-7kg；本发明极大地提了橡胶衬里的拉伸强度、撕裂强度、耐磨性和抗颗粒冲击性，延长产了产品的使用寿命，能满足矿山生产的需求。
Description
技术领域：
本发明涉及应用于钢橡复合管道衬胶的制作领域，具体涉及一种高强度橡胶衬里配方。
背景技术：
目前我国国民经济快速发展要求加快对金属矿山资源的开采与开发，对于矿山设备衬胶与矿山矿浆输送管道衬胶在耐磨性、抗撕裂性、抗冲击性方面提出了更高的要求。而传统的橡胶衬里配方是采用普通橡胶加炭黑进行补强制作的，在抗撕裂、抗冲击、耐磨损方面性能较低，产品寿命仍不能够很好的满足矿山生产的需求。
发明内容：
本发明的目的是提供一种高强度橡胶衬里配方，它极大地提了橡胶衬里的拉伸强度、撕裂强度、耐磨性和抗颗粒冲击性，延长产了产品的使用寿命，能满足矿山生产的需求。
为了解决背景技术所存在的问题，本发明是采用以下技术方案：它的配方组成为：3#烟片10-15 kg、顺丁胶 10-15kg、丁苯胶5-10kg、炭黑18-20kg、白炭黑6-8kg、硅烷偶联剂1-1.5kg、再生胶短纤维4-8kg、硫磺 0.5-0.8kg、防老剂0.5-0.8kg、活性剂1.5-2.0kg、促进剂0.5-1.0kg、软化剂5-7 kg。
所述的炭黑为高耐磨N330，白炭黑为超细沉淀法白炭黑，硅烷偶联剂为SI69，再生胶短纤维为再生胶生产过程中剥离出来的表面附着一定少量橡胶的短纤维，防老剂为防老剂4010NA与RD并用,活性剂为氧化锌，促进剂采用后效性促进剂CZ与DM并用体系，软化剂采用软化油与古马隆并用。
本发明通过在橡胶配方中加入硅烷偶联剂，使硅烷偶联剂与白炭黑表面的羟基发生反应，使白炭黑由亲水性变为疏水性，从而增加了白炭黑与橡胶的相容性与结合力，同时减少了白炭黑的附聚现象，使白炭黑分散更加均匀；同时硅烷偶联剂与炭黑存在的化学吸附作用改善了橡胶与炭黑之间的相互作用，偶联剂表面的S原子参与了硫化交联反应，提高了炭黑聚集体附近橡胶网络的交联密度；再生胶短纤维表面的残余橡胶层参与了橡胶硫化交联反应从而与橡胶基体有机结合，并利用短纤维的高强度达到增强抗撕裂抗破坏抗裂口增长的能力。以此配方生产的橡胶衬里在拉伸强度、撕裂强度和耐磨性能等方面具有一般的橡胶衬里无法比拟的优越性，从而在抵抗固体颗粒或者含有固体颗粒的液体冲击磨损与冲击破坏方面达到寿命延长的效果。
具体实施方式：
本具体实施方式采用以下技术方案：它的配方组成为：3#烟片10-15 kg、顺丁胶 10-15kg、丁苯胶5-10kg、炭黑18-20kg、白炭黑6-8kg、硅烷偶联剂1-1.5kg、再生胶短纤维4-8kg、硫磺 0.5-0.8kg、防老剂0.5-0.8kg、活性剂1.5-2.0kg、促进剂0.5-1.0kg、软化剂5-7 kg。
所述的炭黑为高耐磨N330，白炭黑为超细沉淀法白炭黑，硅烷偶联剂为SI69，再生胶短纤维为再生胶生产过程中剥离出来的表面附着一定少量橡胶的短纤维，防老剂为防老剂4010NA与RD并用,活性剂为氧化锌，促进剂采用后效性促进剂CZ与DM并用体系，软化剂采用软化油与古马隆并用。
本具体实施方式极大地提了橡胶衬里的拉伸强度、撕裂强度、耐磨性和抗颗粒冲击性，延长产了产品的使用寿命，能满足矿山生产的需求。
Claims (2)
1.一种高强度橡胶衬里配方，其特征在于它的配方组成为：3#烟片10-15 kg、顺丁胶 10-15kg、丁苯胶5-10kg、炭黑18-20kg、白炭黑6-8kg、硅烷偶联剂1-1.5kg、再生胶短纤维4-8kg、硫磺 0.5-0.8kg、防老剂0.5-0.8kg、活性剂1.5-2.0kg、促进剂0.5-1.0kg、软化剂5-7 kg。
2.根据权利要求1所述的一种高强度橡胶衬里配方，其特征在于所述的炭黑为高耐磨N330，白炭黑为超细沉淀法白炭黑，硅烷偶联剂为SI69，再生胶短纤维为再生胶生产过程中剥离出来的表面附着一定少量橡胶的短纤维，防老剂为防老剂4010NA与RD并用,活性剂为氧化锌，促进剂采用后效性促进剂CZ与DM并用体系，软化剂采用软化油与古马隆并用。