CN103614006A - Glaze for PU (Polyurethane) American style coating and preparation method thereof - Google Patents
Glaze for PU (Polyurethane) American style coating and preparation method thereof Download PDFInfo
- Publication number
- CN103614006A CN103614006A CN201310608529.7A CN201310608529A CN103614006A CN 103614006 A CN103614006 A CN 103614006A CN 201310608529 A CN201310608529 A CN 201310608529A CN 103614006 A CN103614006 A CN 103614006A
- Authority
- CN
- China
- Prior art keywords
- american
- glaze
- lisi
- coating
- european style
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a glaze for PU (Polyurethane) American style coating. The glaze comprises the following components in percentage by weight: 30%-45% of blown castor oil, 15%-20% of high-transparency pigments, 15%-20% of transparent fillers, 23%-26% of diluting agents, 1%-2% of dispersing agents and 1%-2% of dust-proof agents. The invention also provides a preparation method of the glaze for the PU American style coating. The glaze provided by the invention can generate a cross-linking reaction with a solidifying agent contained in a PU coating because the blown castor oil resin contains hydroxy, thereby having excellent adhesive force and very good wiping property by being wiped on wood by using PU polyurethane paint; in addition, the glaze provided by the invention can also enhance the paint film toughness of the PU coating.
Description
Technical field
The present invention relates to a kind of Ge Lisi, be specifically related to a kind of Ge Lisi for PU American and European style, the invention allows for the preparation method of described Ge Lisi.
Background technology
Ge Lisi is a kind of translucent to transparent pigment colorant, resin dissolves, in oil solvent, is consisted of, slowly dry, can be by wiping, and grooming and do level light and shade, makes that integral color is soft, nature, gradation sense be strong.Ge Lisi is the indispensable color-tinted product of American and European style.At present, the product of the American and European style circulating on market is mostly pyroxylin(e)finish, while being used in PU coating system, generally can have the functional defects such as poor adhesive force.
Summary of the invention
First object of the present invention is to provide a kind of Ge Lisi for PU American and European style, has good sticking power in PU American and European style, and has good wiping properties.
Second object of the present invention is to provide the preparation method of the above-mentioned Ge Lisi for PU American and European style.
First object of the present invention is achieved by the following technical programs:
For a Ge Lisi for PU American and European style, it forms and weight percent is: blowing Viscotrol C 30-45%; High transparent pigment 15-20%; Transparent stopping composition 15-20%; Thinner 23-26%; Dispersion agent 1-2%; Dust-proofing agent 1-2%.
Ge Lisi for PU American and European style of the present invention can also do following improvement:
Described dispersion agent is soybean lecithin.
Described dust-proofing agent is organobentonite.
Described thinner is rosin or durene.
Second object of the present invention is achieved by the following technical programs:
The preparation method of the above-mentioned Ge Lisi for PU American and European style, comprises the following steps:
(1) blowing Viscotrol C, dispersion agent are joined and disperse in cylinder, open dispersion machine and disperse 8-20 minute;
(2) high transparent pigment, transparent stopping composition are joined and disperse in cylinder, high speed dispersion 8-20 minute;
(3) with pump, the material in dispersion machine is sent in runner milling, after milling, got product.
Wherein the weight percent of each component is: blowing Viscotrol C 30-45%; High transparent pigment 15-20%; Transparent stopping composition 15-20%; Thinner 23-26%; Dispersion agent 1-2%; Dust-proofing agent 1-2%.
Ge Lisi for PU American and European style of the present invention can also do following improvement:
Described dispersion agent is soybean lecithin.
Described dust-proofing agent is organobentonite.
Described thinner is rosin or durene.
The beneficial effect compared with prior art having is: because containing hydroxyl in blowing Viscotrol C resin, can with PU coating in solidifying agent generation crosslinking reaction, so Ge Lisi wiping of the present invention has outstanding sticking power on timber, and there is good wiping properties, can also improve in addition the paint film toughness of PU coating, simultaneously, in the present invention, for choosing of dispersion agent, unique employing beat even Yelkin TTS, and coordinate the organobentonite of certain selected, and using rosin and durene as thinner, all different from conventional means, above component coordinates, make finished product there is better paint film toughness, and wiping properties etc., the preparation method of the Ge Lisi of the PU American and European style that the present invention proposes, technique is simple, be easy to promote.
Embodiment
For understanding better the present invention; below by following examples, the present invention is done to further concrete elaboration; but unintelligible is limitation of the invention; some nonessential improvement and adjustment of for those skilled in the art, according to foregoing invention content, doing, be also considered as dropping in protection scope of the present invention.
Embodiment 1
For a Ge Lisi for PU American and European style, it forms and weight percent is: blowing Viscotrol C 30%; High transparent pigment 20%; Transparent stopping composition 20%; Thinner 26%; Dispersion agent 2%; Dust-proofing agent 2%, it is made and is formed by following step:
(1) blowing Viscotrol C, dispersion agent are joined and disperse in cylinder, open dispersion machine and disperse 10 minutes;
(2) high transparent pigment, transparent stopping composition are joined and disperse in cylinder, high speed dispersion 10 minutes;
(3) with pump, the material in dispersion machine is sent in runner milling, after milling, got product 1.
Wherein, high transparent pigment adopts yellow H10G, and transparent stopping composition adopts polyolefine, and thinner adopts rosin, and dispersion agent adopts soybean lecithin, and dust-proofing agent adopts organobentonite SD-1, and above component all can be buied from market.
Embodiment 2
Employing is with the same preparation method of embodiment 1, and difference is that the ratio of component is slightly different, as follows:
Blowing Viscotrol C 45%; High transparent pigment 15%; Transparent stopping composition 15%; Thinner 23%; Dispersion agent 1%; Dust-proofing agent 1%.
Wherein, high transparent pigment adopts red FGR, and transparent stopping composition adopts polyolefine, and thinner adopts durene, and dispersion agent adopts soybean lecithin, and dust-proofing agent adopts organobentonite SD-1, and above component all can be buied from market.
Embodiment 3
Employing is with the same preparation method of embodiment 1, and difference is that the ratio of component is slightly different, as follows:
Blowing Viscotrol C 40%; High transparent pigment 18%; Transparent stopping composition 18%; Thinner 24%; Dispersion agent 1%; Dust-proofing agent 1%.
Wherein, high transparent pigment adopts red FGR, and transparent stopping composition adopts polyolefine, and thinner adopts durene, and dispersion agent adopts soybean lecithin, and dust-proofing agent adopts organobentonite SD-1, and above component all can be buied from market.
Because containing hydroxyl in blowing Viscotrol C resin, can with PU coating in solidifying agent generation crosslinking reaction, so Ge Lisi wiping of the present invention has outstanding sticking power on timber, and there is good wiping properties, can also improve in addition the paint film toughness of PU coating, simultaneously, in the present invention, for choosing of dispersion agent, unique employing beat even Yelkin TTS, and coordinate the organobentonite of certain selected, and using rosin and durene as thinner, all different from conventional means, above component coordinates, make finished product there is better paint film toughness, and wiping properties etc.
The foregoing is only preferred embodiment of the present invention, in order to limit the present invention, within the spirit and principles in the present invention not all, any modification of doing, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (5)
1. for a Ge Lisi for PU American and European style, it is characterized in that it forms and weight percent is: blowing Viscotrol C 30-45%; High transparent pigment 15-20%; Transparent stopping composition 15-20%; Thinner 23-26%; Dispersion agent 1-2%; Dust-proofing agent 1-2%.
2. the Ge Lisi for PU American and European style according to claim 1, is characterized in that: described dispersion agent is soybean lecithin.
3. the Ge Lisi for PU American and European style according to claim 1, is characterized in that: described dust-proofing agent is organobentonite.
4. the Ge Lisi for PU American and European style according to claim 1, is characterized in that: described thinner is rosin or durene.
5. according to the preparation method of the Ge Lisi for PU American and European style described in claim 1-4 any one, it is characterized in that comprising the following steps:
(1) blowing Viscotrol C, dispersion agent are joined and disperse in cylinder, open dispersion machine and disperse 8-20 minute;
(2) high transparent pigment, transparent stopping composition are joined and disperse, in cylinder, to disperse 8-20 minute;
(3) with pump, the material in dispersion machine is sent in runner milling, after milling, obtained finished product.