CN103614004A - 一种环保防脱落擦色剂 - Google Patents
一种环保防脱落擦色剂 Download PDFInfo
- Publication number
- CN103614004A CN103614004A CN201310576547.1A CN201310576547A CN103614004A CN 103614004 A CN103614004 A CN 103614004A CN 201310576547 A CN201310576547 A CN 201310576547A CN 103614004 A CN103614004 A CN 103614004A
- Authority
- CN
- China
- Prior art keywords
- wiping
- durene
- environmental protection
- preventing
- stain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明一种环保防脱落擦色剂,使用高固含长油度树脂与各色色粉经研磨成基础色浆,通过与透明擦色主剂、四甲苯调制成各色擦色剂,擦色剂固含高,溶剂含量少且毒性较小。通过树脂与分散剂的作用,使色粉在体系中均匀分散,提升体系的同类相效果,使得擦色剂上色均匀,并可反复擦涂至着色满意为止,施工宽容性大,施工简便,具有优异的附着力性能、不影响涂层附着力,施工效果木材纹理清晰、立体层次感效果好。
Description
技术领域
本发明涉及一种适用于溶剂型木器漆的环保、防脱落擦色剂,属于木器涂料行业。
背景技术
现代生活的家具装饰色彩缤纷、五彩斑斓。色漆的涂装需要良好的喷涂技术及对色彩的敏感度,并且在施工过程中,稍不注意就极易造成色差且不容易返工修复,因色彩性质限制,在开放和半开放的涂装效果中漆膜亦缺乏立体感和层次感。擦色剂的使用,可以使底材表面的阴影、色调变化、年轮及错综交织的纤维等特点自然呈现,层次清晰,具有较强的立体感。常规擦色剂干燥速度快,施工工艺要求严格,稍不注意就容易产生上色不均匀、脱层等弊病,且溶剂含量高,不利于生活环境的健康发展。
发明内容
本发明的目的是解决擦色剂上色不均匀以及对涂层附着力影响的技术问题,针对木器木纹擦色(上色、着色)所设计的一款施工简单快捷且宽容性较高的着色产品。
本发明是这样实现的:一种环保防脱落擦色剂,由基础色浆30%~65%、透明擦色剂35~69%和溶剂0%~1%三种组分按重量百分含量混合制成。施工时,使用棉布直接对基材均匀连续性擦涂(圈涂、横涂)所需色系的擦色剂,擦完后,使用干净的棉布按上色着色时顺序,均匀连续性擦拭干净木纹外多余的擦色剂即可。
1. 基础色浆的制备
。
所述亚麻仁油树脂,其固含为95%~97%,粘度为350±50Mpa.s/25℃,色泽为≤2#,油度为72,优选自马来西亚油脂有限公司生产的型号为2058-100GLAEE的亚麻仁油树脂。
所述分散剂,优选德国毕克公司生产的型号为BYK163分散剂,可根据具体情况选择性加入。
所述聚酰胺蜡,其固含为15%,优选自日本楠本化工EY-6900。其主要作用是起防沉,在制备过程中可根据具体测试情况选择性加入。
所述色粉,优选自日本三菱公司生产的型号为MA-100炭黑;澳大利亚美礼联公司生产的型号595钛白粉;比利时卡佩勒颜料(CAPPELLE PIGMENTS)有限公司生产的型号分别为2114660红色粉、625黑棕色粉、J4658棕色粉、4435B透明氧化铁红色粉、YD-302桔黄色粉。
所述基础色浆的制备步骤如下:选用干净符合标准的分散缸,按重量百分比依次加入亚麻仁油树脂45~70%、分散剂0~3%、聚酰胺蜡0~1.5%、四甲苯1%~3%,以转速800~1200 r/min中速搅拌10min至充分分散均匀,以转速400~600 r/min低速搅拌下加入色粉25%~45%,以转速1600~1800 r/min高速分散10~15 min后,停止搅拌,润湿浸泡12h,过砂磨研磨至细度≤ 20 μm,加入四甲苯2%~4%搅拌均匀即可。
2. 透明擦色主剂的制备
。
所述悬浮剂为防沉降助剂,其色泽为≤1#,有效含量100%,本发明优选自晨晟化工有限公司生产的型号为BL-5901悬浮剂。
所述滑石粉,其细度为325目,吸油量为23~27g/100g,本发明优选自广西桂广矿业有限公司型号325目滑石粉。
所述透明擦色主剂的制备步骤如下:选用干净符合标准的分散缸,按重量百分比依次投入亚麻仁油树脂32%、聚酰胺蜡4%、悬浮剂5%、滑石粉45%、四甲苯4%、,启动分散机, 以转速600~800 r/min低速搅拌均匀后,以转速1200~1500 r/min高速搅拌10~15 min,至细度≤ 20 μm,用环已酮 10%调粘度,粘度:15000~25000 mpa.s/30℃,待用。
3. 擦色剂的制备:
所述擦色剂的制备步骤如下:选用干净符合标准的分散缸,按重量百分比依次加入基础色浆30%~65%、擦色主剂35%~69%,启动分散机,以转速600~800 r/min低速搅拌均匀后,用四甲苯0%~1%清洗缸边,即制得擦色剂。
施工工艺:擦涂施工,即使用棉球或碎布浸沾擦色剂后,手工直接均匀连续性对基材进行擦涂(圈涂、横涂),擦完后,使用干净的棉布按上色着色时顺序,均匀连续性擦拭干净木纹外多余的擦色剂即可。
本发明一种环保、防脱落擦色剂,使用高固含长油度树脂与各色色粉经研磨成基础色浆,通过与透明擦色主剂、四甲苯调制成各色擦色剂,擦色剂固含高,溶剂含量少且毒性较小。同时,通过树脂与分散剂的作用,使色粉在体系中均匀分散,提升体系的同类相效果,使得上色均匀,并可反复擦涂至着色满意为止,施工宽容性大,且施工简便。经检测和试用证明,其具有优异的附着力性能、不影响涂层附着力,施工效果木材纹理清晰、立体层次感效果好。
具体实施方式
以下实施例中亚麻仁油树脂均为马来西亚油脂有限公司生产的型号2058-100GLAEE亚麻仁油树脂;所述分散剂均为德国毕克化学有限公司成产的型号BKY163分散剂;所述聚酰胺蜡均为日本楠本化工EY-6900;所述悬浮剂均为自晨晟化工有限公司生产的型号为BL-5901悬浮剂;滑石粉均为广西桂广矿业有限公司生产的325目滑石粉;所述色粉均为日本三菱公司生产的型号MA-100炭黑;澳大利亚美礼联公司生产的型号595钛白粉;比利时卡佩勒颜料(CAPPELLE PIGMENTS)有限公司生产的型号分别为2114660红色粉、625黑棕色粉、J4658棕色粉、4435B透明氧化铁红色粉、YD-302桔黄色粉。
实施例1 黑色擦色剂
1) 黑色基础色浆的制备
所述黑色基础色浆的制备步骤如下:选用干净符合标准的分散缸,依次加入亚麻仁油树脂67 kg、分散剂2 kg、四甲苯2 kg,以转速800~1200 r/min中速搅拌10min至充分分散均匀,以转速400~600 r/min低速搅拌下加入炭黑27 kg,以转速1600~1800 r/min高速分散10~15 min后,停止搅拌,润湿浸泡12 h,过砂磨研磨至细度≤ 20 μm,加入四甲苯2 kg搅拌均匀即可。
2) 透明擦拭主剂的制备
所述透明擦色主剂的制备步骤如下:选用干净符合标准的分散缸,依次加入亚麻仁油树脂32 kg、聚酰胺蜡4 kg、悬浮剂5 kg、滑石粉45 kg、四甲苯4 kg、,启动分散机, 以转速600~800 r/min低速搅拌均匀后,以转速1200~1500 r/min高速搅拌10~15 min,至细度≤ 20 μm,用环已酮10 kg调粘度,粘度:15000~25000 mpa.s/30℃,待用。
3) 黑色擦色剂的制备
所述擦色剂的制备步骤如下:选用干净符合标准的分散缸,依次加入黑色基础色浆40 kg、擦色主剂59 kg,启动分散机,以转速600~800 r/min低速搅拌均匀后,用四甲苯1 kg清洗缸边,即制得擦色剂。
施工工艺:擦涂施工,即使用棉球或碎布浸沾擦色剂后,手工直接均匀连续性对基材进行擦涂(圈涂、横涂),擦完后,使用干净的棉布按上色着色时顺序,均匀连续性擦拭干净木纹外多余的擦色剂即可。
实施例2-7
1) 基础色浆的制备
按照表1准备原料,采用与实施例1相同的制备方法分别制备好各色基础色浆。
表1:
2) 透明擦色主剂的制备
按照表2准备原料,采用与实施例1相同的方法制备透明擦色主剂。
表2:
3) 擦色剂的制备
根据表3所示准备原料,采用与实施例1相同的方法分别制备出各色擦色剂。
表3:
施工工艺:实施例2-7均采用与实施例1相同的施工工艺。
实施例1-7通过圈涂、横涂的施工工艺分别擦拭于不同的基材上,擦拭量可按客户颜色要求进行施工,待擦色剂完全干后,重涂面漆完全干燥后,通过划格器对产品的附着力进行测试,测试方法参照GB/T23997-2009,测试结果如下所示:
采用相同的施工方法将本发明样品与市售样品A和B进行对比,结果如下:
从以上数据可知,本发明具有优异的附着力。
此外,在使用了本发明的漆膜上重涂聚氨酯油漆,施工效果显示漆膜无脱层、无跑油现象。经检测和试用证明,本发明具有优异的附着力,同时含有的可溶性有机挥发物含量较慢较低,挥发毒性非常小,对人体伤害较小,施工宽容性大,施工简便,擦拭基材后木纹自然清晰、层次感强,是一款非常适用于溶剂型木器漆的环保、防脱落擦色剂。
Claims (7)
1.本发明一种环保防脱落擦色剂,其特征在于,其制备主要通过树脂与各色色粉研磨成的基础色浆与透明擦色主剂调制而成,其主要成分与重量百分比为:基础色浆30%~65%,透明擦色主剂35%~69%,四甲苯0%~1%;其中,基础色浆的主要成分与重量百分比如下:
亚麻仁油树脂 45%~70%
分散剂 0%~3%
聚酰胺蜡 0%~1.5%
色粉 25%~45%
四甲苯 1%~3%
四甲苯 2%~4%
透明擦色主剂的主要成分与重量百分比如下:
亚麻仁油树脂 32%
聚酰胺蜡 4%
悬浮剂 5%
滑石粉 45%
四甲苯 4%
环已酮 10% 。
2.根据权利要求1所述,本发明一种环保防脱落擦色剂,其特征在于,基础色浆分散均匀,细度≤20μm。
3.根据权利要求1所述,本发明一种环保防脱落擦色剂,其特征在于,透明擦色主剂细度≤ 20 μm,用环已酮 10%调粘度,粘度:15000~25000 mpa.s/30℃。
4.根据权利要求1所述,本发明一种环保防脱落擦色剂,其特征在于,亚麻仁油树脂固含为95%~97%,粘度为350±50Mpa.s/25℃,色泽为≤2#,油度为72。
5. 根据权利要求1所述,本发明一种环保防脱落擦色剂,其特征在于,所述聚酰胺蜡固含为15%,在制备过程中可根据具体测试情况选择性加入。
6.根据权利要求1所述,本发明一种环保防脱落擦色剂,其特征在于,分散剂可根据具体情况选择性加入;滑石粉为325目,吸油量为23~27g/100g。
7.根据权利要求1-5所述,本发明一种环保防脱落擦色剂,其特征在于,擦色剂制备步骤如下:选用干净符合标准的分散缸,按重量百分比依次加入基础色浆、擦色主剂,搅拌均匀后,用四甲苯清洗缸边,即制得擦色剂;其中,基础色浆的制备步骤如下:
选用干净符合标准的分散缸,按重量百分比依次加入亚麻仁油树脂、分散剂、聚酰胺蜡、四甲苯,以转速800~1200 r/min中速搅拌10min至充分分散均匀,以转速400~600 r/min低速搅拌下加入色粉,以转速1600~1800 r/min高速分散10~15 min后,停止搅拌,润湿浸泡12h,过砂磨研磨至细度≤ 20 μm,加入四甲苯搅拌均匀即可;
透明擦色主剂的制备步骤如下:
选用干净符合标准的分散缸,按重量百分比依次投入亚麻仁油树脂、聚酰胺蜡、悬浮剂、滑石粉、四甲苯、,启动分散机, 以转速600~800 r/min低速搅拌均匀后,以转速1200~1500 r/min高速搅拌10~15 min,至细度≤ 20 μm,用环已酮 10%调粘度,粘度:15000~25000 mpa.s/30℃,待用。