CN103602966B - 非晶氧化锌/钛/磷复合材料的制造方法 - Google Patents

非晶氧化锌/钛/磷复合材料的制造方法 Download PDF

Info

Publication number
CN103602966B
CN103602966B CN201310511782.0A CN201310511782A CN103602966B CN 103602966 B CN103602966 B CN 103602966B CN 201310511782 A CN201310511782 A CN 201310511782A CN 103602966 B CN103602966 B CN 103602966B
Authority
CN
China
Prior art keywords
titanium
zinc oxide
composite material
phosphorus composite
amorphous zinc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310511782.0A
Other languages
English (en)
Other versions
CN103602966A (zh
Inventor
丛国芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liyang Technology Development Center
Original Assignee
LIYANG DONGDA TECHNOLOGY TRANSFER CENTER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIYANG DONGDA TECHNOLOGY TRANSFER CENTER Co Ltd filed Critical LIYANG DONGDA TECHNOLOGY TRANSFER CENTER Co Ltd
Priority to CN201310511782.0A priority Critical patent/CN103602966B/zh
Publication of CN103602966A publication Critical patent/CN103602966A/zh
Application granted granted Critical
Publication of CN103602966B publication Critical patent/CN103602966B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种非晶氧化锌/钛/磷复合材料的制造方法，依次包括如下步骤：（1）准备纯钛板，将纯钛板清洗干净后干燥备用；（2）配置混合镀液；（3）将步骤（2）中的混合镀液升温，当温度达到50-75℃时，将纯钛板浸入混合镀液中进行化学镀，当镀层达到预定厚度后将镀有非晶氧化锌/钛/磷复合材料的纯钛板取出，清洗后进行干燥处理；（4）将非晶氧化锌/钛/磷复合材料的镀层从纯钛板表面分离出来；（5）将分离出来的非晶氧化锌/钛/磷复合材料的镀层浸入重新配置的混合镀液中，在温度为50-75℃的条件下进行化学镀，当达到设定总厚度后取出，清洗后进行干燥处理，完成非晶氧化锌/钛/磷复合材料的制作。

Description

非晶氧化锌/钛/磷复合材料的制造方法
技术领域
本发明涉及一种材料科学领域，特别是涉及一种非晶氧化锌/钛/磷复合材料的制造方法。
背景技术
一般的非晶合金材料由于电阻率高，并且无晶体的各向异性，因此具有高的导磁率，是优良的磁材料，可广泛应用于变压器、互感器、传感器等领域。但是非晶合金材料的制造方法一般采用电弧熔炼等，工艺步骤较多，能源消耗很大，成本高，不够环保。
现有技术中，非晶合金材料由于还需采用大量的贵金属材料，因此无可避免的导致价格高，无法广泛的大量推广应用。
发明内容
针对现有技术的不足，本发明提供一种工艺简单，节能的非晶氧化锌/钛/磷复合材料的制造方法。本发明提出的方法依次包括如下步骤：
（1）准备纯钛板，将纯钛板清洗干净后干燥备用；
（2）配置混合镀液；其中，该混合镀液具有15.2～17.6克/升的硫酸钛、0.8～1.9克/升的氧化锌、13.4～16.3克/升的醋酸钠、11.5～14.8克/升的次亚磷酸钠；
（3）将步骤（2）中的混合镀液升温，当温度达到50-75℃时，将纯钛板浸入混合镀液中进行化学镀，当镀层达到预定厚度后将镀有非晶氧化锌/钛/磷复合材料的纯钛板取出，清洗后进行干燥处理；
（4）将非晶氧化锌/钛/磷复合材料的镀层从纯钛板表面分离出来；
（5）将分离出来的非晶氧化锌/钛/磷复合材料的镀层浸入重新配置的混合镀液中，在温度为50-75℃的条件下进行化学镀，当达到设定总厚度后取出，清洗后进行干燥处理，完成非晶氧化锌/钛/磷复合材料的制作。
其中，步骤（3）中的预定厚度为60-80微米，步骤（5）中的预定总厚度为100-200微米。
本发明的方法实施简单易行，采用化学镀的方式逐层产生非晶氧化锌/钛/磷复合材料的镀层，可以生产出任意厚度的成品，而且制造过程无需耗电，降低了成本，节约能源。
具体实施方式
一种非晶氧化锌/钛/磷复合材料的制造方法，依次包括如下步骤：
（1）准备纯钛板，将纯钛板清洗干净后干燥备用；
（2）配置混合镀液；其中，该混合镀液具有15.2～17.6克/升的硫酸钛、0.8～1.9克/升的氧化锌、13.4～16.3克/升的醋酸钠、11.5～14.8克/升的次亚磷酸钠；
（3）将步骤（2）中的混合镀液升温，当温度达到50-75℃时，将纯钛板浸入混合镀液中进行化学镀，当镀层达到预定厚度后将镀有非晶氧化锌/钛/磷复合材料的纯钛板取出，清洗后进行干燥处理；
（4）将非晶氧化锌/钛/磷复合材料的镀层从纯钛板表面分离出来；
（5）将分离出来的非晶氧化锌/钛/磷复合材料的镀层浸入重新配置的混合镀液中，在温度为50-75℃的条件下进行化学镀，当达到设定总厚度后取出，清洗后进行干燥处理，完成非晶氧化锌/钛/磷复合材料的制作。
其中，步骤（3）中的预定厚度为60-80微米，步骤（5）中的预定总厚度为100-200微米。
优选的实施例
一种非晶氧化锌/钛/磷复合材料的制造方法，依次包括如下步骤：
（1）准备纯钛板，将纯钛板清洗干净后干燥备用；
（2）配置混合镀液；其中，该混合镀液具有16.2克/升的硫酸钛、1.3克/升的氧化锌、14.4克/升的醋酸钠、13.2克/升的次亚磷酸钠；
（3）将步骤（2）中的混合镀液升温，当温度达到60℃时，将纯钛板浸入混合镀液中进行化学镀，当镀层达到预定厚度后将镀有非晶氧化锌/钛/磷复合材料的纯钛板取出，清洗后进行干燥处理；
（4）将非晶氧化锌/钛/磷复合材料的镀层从纯钛板表面分离出来；
（5）将分离出来的非晶氧化锌/钛/磷复合材料的镀层浸入重新配置的混合镀液中，在温度为50-75℃的条件下进行化学镀，当达到设定总厚度后取出，清洗后进行干燥处理，完成非晶氧化锌/钛/磷复合材料的制作。
其中，步骤（3）中的预定厚度为70微米，步骤（5）中的预定总厚度为160微米。
至此已对本发明做了详细的说明，但前文的描述的实施例仅仅只是本发明的优选实施例，其并非用于限定本发明。本领域技术人员可对本发明做任何的修改，而本发明的保护范围由所附的权利要求来限定。

Claims (2)

1.一种非晶氧化锌/钛/磷复合材料的制造方法，依次包括如下步骤：
(1)准备纯钛板，将纯钛板清洗干净后干燥备用；
(2)配置混合镀液；
(3)将步骤(2)中的混合镀液升温，当温度达到50-75℃时，将纯钛板浸入混合镀液中进行化学镀，当镀层达到预定厚度后将镀有非晶氧化锌/钛/磷复合材料的纯钛板取出，清洗后进行干燥处理；
(4)将非晶氧化锌/钛/磷复合材料的镀层从纯钛板表面分离出来；
(5)将分离出来的非晶氧化锌/钛/磷复合材料的镀层浸入重新配置的混合镀液中，在温度为50-75℃的条件下进行化学镀，当达到设定总厚度后取出，清洗后进行干燥处理，完成非晶氧化锌/钛/磷复合材料的制作；
其中，该混合镀液具有15.2～17.6克/升的硫酸钛、0.8～1.9克/升的氧化锌、13.4～16.3克/升的醋酸钠、11.5～14.8克/升的次亚磷酸钠。
2.如权利要求1所述的方法，其特征在于：
其中，步骤(3)中的预定厚度为60-80微米；步骤(5)中的设定总厚度为100-200微米。
CN201310511782.0A 2013-10-26 2013-10-26 非晶氧化锌/钛/磷复合材料的制造方法 Active CN103602966B (zh)