CN100595324C - 非晶镍/磷/氧化铝复合材料的制造方法 - Google Patents
非晶镍/磷/氧化铝复合材料的制造方法 Download PDFInfo
- Publication number
- CN100595324C CN100595324C CN200710071175A CN200710071175A CN100595324C CN 100595324 C CN100595324 C CN 100595324C CN 200710071175 A CN200710071175 A CN 200710071175A CN 200710071175 A CN200710071175 A CN 200710071175A CN 100595324 C CN100595324 C CN 100595324C
- Authority
- CN
- China
- Prior art keywords
- plating
- composite material
- phosphorus
- alumina composite
- nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种非晶镍/磷/氧化铝复合材料的制造方法，先取用纯镍板并清洗，将纯镍板浸入配置好的镀液中化学施镀，每镀设定周期都将该纯镍板快速移到新配置镀液中，当镀层达到设定厚度后将镀有非晶镍/磷/氧化铝复合材料的纯镍板取出并清洗，然后将镀层从纯镍板表面物理脱离，再将镀层单独浸入新配置镀液中化学施镀，每镀设定周期都取出并浸没于新配置镀液中进行反复施镀，当达到设定总厚度后取出清洗，即可得到成品材料。本发明的方法实施非常简单，采用化学镀的方式逐层产生非晶镍/磷/氧化铝复合材料的镀层，可以生产出任意厚度的成品，生产的非晶镍/磷/氧化铝复合材料的性能优良，而且制造过程无需耗电，降低了成本，节约能源，更加环保。
Description
技术领域：
本发明涉及一种非晶镍/磷/氧化铝复合材料的制造方法。
背景技术：
一般的非晶合金由于没有晶体的各向异性，并且电阻率高，因此具有高的导磁率、低的损耗，是优良的磁材料，可以代替硅钢、坡莫合金和铁氧体等作为变压器铁芯、互感器、传感器等。非晶合金还具有高强韧性、优良的耐磨性等，用途非常广泛。但是非晶合金材料的制造方法一般采用电弧熔炼等，工艺步骤较多，能源消耗很大，成本高，不够环保节能。
发明内容：
针对现有技术的不足，本发明提供一种工艺简单，节能的非晶镍/磷/氧化铝复合材料的制造方法。
本发明依次采用下列步骤：
(a)取用尺寸规格符合要求的纯镍板，并清洗干净；
(b)配置好含有硫酸镍14.8～18.5克/升、次亚磷酸钠14.5～16克/升、醋酸钠12.8～14.3克/升、直径为5-10纳米的氧化铝0.5～2.0克/升的镀液，在45-80℃的镀液中将纯镍板浸入化学施镀，每镀设定周期都将该纯镍板快速移出并浸没于新配置的镀液中，当镀层达到设定厚度后将镀有非晶镍/磷/氧化铝复合材料的纯镍板取出并清洗；
(c)将非晶镍/磷/氧化铝复合材料的镀层从纯镍板表面物理脱离；
(d)将非晶镍/磷/氧化铝复合材料的镀层单独浸入新配置镀液中化学施镀，每镀设定周期都取出并浸没于新配置镀液中进行反复施镀，当达到设定总厚度后取出清洗，即可得到成品的非晶镍/磷/氧化铝复合材料。
本发明的方法实施非常简单，采用化学镀的方式逐层产生非晶镍/磷/氧化铝复合材料的镀层，可以生产出任意厚度的成品，生产的非晶镍/磷/氧化铝复合材料的性能优良，而且制造过程无需耗电，降低了成本，节约能源，更加环保。
实际上，在步骤(b)中的施镀设定周期可非常灵活的改变，一般为1小时以上，过短则镀液的有效成分未充分利用，浪费镀液，过长则降低生产效率。镀层的设定厚度也可灵活调整，一般为40微米以上，这样镀层已可以较容易的从纯镍板表面物理脱离。
同样，在步骤(d)中的施镀设定周期一般也为1小时以上。一般在新配置镀液中的各成分的含量均取上限值，可以使镀层的生产效率更高。
下面通过实施例进一步说明本发明。
实施例：
生产时依次采用下列步骤，
(a)取用一定尺寸规格的纯镍板，并清洗干净；
(b)配置好含有硫酸镍18.5克/升、次亚磷酸钠16克/升、醋酸钠14.3克/升、直径为10纳米的氧化铝2.0克/升的镀液，在50℃的镀液中将纯镍板浸入化学施镀，每镀2小时都将该纯镍板快速移出并浸没于新配置镀液中，当镀层达到40微米后，一般是镀22小时左右，将镀有非晶镍/磷/氧化铝复合材料的纯镍板取出并清洗；
(c)将非晶镍/磷/氧化铝复合材料的镀层从纯镍板表面物理脱离；
(d)将非晶镍/磷/氧化铝复合材料的镀层单独浸入新配置镀液中化学施镀，每镀2小时都取出并浸没于新配置镀液中进行反复施镀，当达到需要的总厚度后取出清洗，即可得到成品的非晶镍/磷/氧化铝复合材料。
生产的非晶镍/磷/氧化铝复合材料中镍、磷、氧化铝的含量会周期性变化，是成分调制的材料，各种性能更加优良。
Claims (5)
1、一种非晶镍/磷/氧化铝复合材料的制造方法，其特征在于依次采用下列步骤：
(a)取用尺寸规格符合要求的纯镍板，并清洗干净；
(b)配置好含有硫酸镍14.8～18.5克/升、次亚磷酸钠14.5～16克/升、醋酸钠12.8～14.3克/升、直径为5-10纳米的氧化铝0.5～2.0克/升的镀液，在45-80℃的镀液中将纯镍板浸入化学施镀，每镀第一设定周期后都将该纯镍板快速移出并浸没于新配置的镀液中，当镀层达到设定厚度后将镀有非晶镍/磷/氧化铝复合材料的纯镍板取出并清洗；
(c)将非晶镍/磷/氧化铝复合材料的镀层从纯镍板表面物理脱离；
(d)将非晶镍/磷/氧化铝复合材料的镀层单独浸入新配置镀液中化学施镀，每镀第二设定周期后都取出并浸没于新配置镀液中进行反复施镀，当达到设定总厚度后取出清洗，即可得到成品的非晶镍/磷/氧化铝复合材料。
2、根据权利要求1所述的非晶镍/磷/氧化铝复合材料的制造方法，其特征为：在步骤(b)中，施镀的第一设定周期为1小时以上，镀层设定厚度为40微米以上。
3、根据权利要求1或2所述的非晶镍/磷/氧化铝复合材料的制造方法，其特征为：在步骤(d)中，施镀的第二设定周期为1小时以上。
4、根据权利要求1或2所述的非晶镍/磷/氧化铝复合材料的制造方法，其特征为：在步骤(b)或(d)中，新配置镀液中的各成分的含量均取上限值。
5、根据权利要求3所述的非晶镍/磷/氧化铝复合材料的制造方法，其特征为：在步骤(b)或(d)中，新配置镀液中的各成分的含量均取上限值。