CN103602234A - Alkyd resin waterproof paint - Google Patents
Alkyd resin waterproof paint Download PDFInfo
- Publication number
- CN103602234A CN103602234A CN201310520668.4A CN201310520668A CN103602234A CN 103602234 A CN103602234 A CN 103602234A CN 201310520668 A CN201310520668 A CN 201310520668A CN 103602234 A CN103602234 A CN 103602234A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof paint
- alkyd resin
- raw material
- ball milling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an alkyd resin waterproof paint which is composed of the following raw materials: by weight, 60-68 parts of ZY628-75 alkyd resin, 10-20 parts of a styrene acrylic emulsion, 2-3 parts of ammonium metaborate, 2-3 parts of sodium gluconate, 1-2 parts of sodium molybdate, 2-4 parts of monoethanolamine, 1-2 parts of amyl acetate, 3-4 parts of magnesium silicate, 2-3 parts of pentaerythritol, 1-2 parts of poly(ethylene glycol) monooleate, 6-10 parts of wollastonite powder, 6-8 parts of a bonding auxiliary agent, and 13-20 parts of deionized water. The waterproof paint provided by the invention is convenient for construction, has good waterproofness, good tensile strength and good extensibility, is safe, and has no toxic or side effect.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of alkyd resin waterproof paint.
Background technology
Brushing, on building surface, forms thin film through the volatilization of solvent or moisture or the chemical reaction of two kinds of components, makes building surface and water isolated, thereby plays the effect of waterproof, sealing, and the thick liquid of these brushings is called waterproof paint.The waterproofing membrane that waterproof paint forms after solidifying has certain extensibility, elastoplasticity, splitting resistance, impermeability and weathering resistance, can play waterproof, prevent blending provide protection.Waterproof paint has good thermal adaptability, easy and simple to handle, for ease of maintenaince with maintenance.
Summary of the invention
The object of the invention is just to provide a kind of alkyd resin waterproof paint.
The present invention is achieved by the following technical solutions:
An alkyd resin waterproof paint, it is comprised of the raw material of following weight parts:
ZY628-75 Synolac 60-68, benzene emulsion 10-20, ammonium metaborate 2-3, Sunmorl N 60S 2-3, Sodium orthomolybdate 1-2, Monoethanolamine MEA BASF 2-4, pentyl acetate 1-2, Magnesium Silicate q-agent 3-4, tetramethylolmethane 2-3, polyoxyethylene oleic acid ester 1-2, wollastonite powder 6-10, adhesive aid 6-8, deionized water 13-20;
Described adhesive aid is comprised of the raw material of following weight parts:
Eva emulsion 40-45, aluminum isopropylate 3-5, polyamide wax micropowder 3-4, silane resin acceptor kh-550 1-2, stearic acid direactive glyceride 2-4, urea 2-3, nano-sized carbon 0.1-1;
Above-mentioned aluminum isopropylate is heated to 130-135 ℃, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, stirring reaction 10-15 minute at 100-120 ℃, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 200-300 rev/min of dispersed with stirring 3-4 minute, mixes with particle obtained above and each raw material of residue, fully ball milling, obtains described adhesive aid.
A preparation method for alkyd resin waterproof paint, comprises the following steps:
Above-mentioned wollastonite powder is mixed with pentyl acetate, Magnesium Silicate q-agent, and ball milling 1-2 hour, adds each raw material of residue, and high-speed stirring, to mixing, obtains described alkyd resin waterproof paint.
Advantage of the present invention is:
Waterproof paint easy construction of the present invention, good waterproof performance, tensile strength is good, good-extensibility, safe without toxic side effect.
Embodiment
Embodiment 1
An alkyd resin waterproof paint, it by following weight parts (kilogram) raw material form:
ZY628-75 Synolac 68, benzene emulsion 20, ammonium metaborate 3, Sunmorl N 60S 3, Sodium orthomolybdate 1, Monoethanolamine MEA BASF 4, pentyl acetate 2, Magnesium Silicate q-agent 4, tetramethylolmethane 3, polyoxyethylene oleic acid ester 1, wollastonite powder 10, adhesive aid 8, deionized water 20;
Described adhesive aid is comprised of the raw material of following weight parts:
Eva emulsion 45, aluminum isopropylate 3, polyamide wax micropowder 4, silane resin acceptor kh-550 2, stearic acid direactive glyceride 2, urea 3, nano-sized carbon 0.1;
Above-mentioned aluminum isopropylate is heated to 135 ℃, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, at 120 ℃, stirring reaction is 15 minutes, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 200 revs/min of dispersed with stirring 3 minutes, mix with particle obtained above and each raw material of residue, fully ball milling, obtains described adhesive aid.
A preparation method for alkyd resin waterproof paint, comprises the following steps:
Above-mentioned wollastonite powder is mixed with pentyl acetate, Magnesium Silicate q-agent, and ball milling 1 hour, adds each raw material of residue, and high-speed stirring, to mixing, obtains described alkyd resin waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an alkyd resin waterproof paint, is characterized in that what it was comprised of the raw material of following weight parts:
ZY628-75 Synolac 60-68, benzene emulsion 10-20, ammonium metaborate 2-3, Sunmorl N 60S 2-3, Sodium orthomolybdate 1-2, Monoethanolamine MEA BASF 2-4, pentyl acetate 1-2, Magnesium Silicate q-agent 3-4, tetramethylolmethane 2-3, polyoxyethylene oleic acid ester 1-2, wollastonite powder 6-10, adhesive aid 6-8, deionized water 13-20;
Described adhesive aid is comprised of the raw material of following weight parts:
Eva emulsion 40-45, aluminum isopropylate 3-5, polyamide wax micropowder 3-4, silane resin acceptor kh-550 1-2, stearic acid direactive glyceride 2-4, urea 2-3, nano-sized carbon 0.1-1;
Above-mentioned aluminum isopropylate is heated to 130-135 ℃, add polyamide wax micropowder, granulation after ball milling, mixes urea with stearic acid direactive glyceride, stirring reaction 10-15 minute at 100-120 ℃, be cooled to normal temperature, add silane resin acceptor kh-550, nano-sized carbon, 200-300 rev/min of dispersed with stirring 3-4 minute, mixes with particle obtained above and each raw material of residue, fully ball milling, obtains described adhesive aid.
2. a preparation method for alkyd resin waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned wollastonite powder is mixed with pentyl acetate, Magnesium Silicate q-agent, and ball milling 1-2 hour, adds each raw material of residue, and high-speed stirring, to mixing, obtains described alkyd resin waterproof paint.