CN103601982A - 一种阻燃三元乙丙橡胶材料 - Google Patents

一种阻燃三元乙丙橡胶材料 Download PDF

Info

Publication number
CN103601982A
CN103601982A CN201310522832.5A CN201310522832A CN103601982A CN 103601982 A CN103601982 A CN 103601982A CN 201310522832 A CN201310522832 A CN 201310522832A CN 103601982 A CN103601982 A CN 103601982A
Authority
CN
China
Prior art keywords
parts
flame retardant
diene monomer
propylene
monomer rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310522832.5A
Other languages
English (en)
Inventor
叶春会
王泽平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jia Mu Rubber Industry Co Ltd
Original Assignee
Anhui Jia Mu Rubber Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jia Mu Rubber Industry Co Ltd filed Critical Anhui Jia Mu Rubber Industry Co Ltd
Priority to CN201310522832.5A priority Critical patent/CN103601982A/zh
Publication of CN103601982A publication Critical patent/CN103601982A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃三元乙丙橡胶材料，按照重量份计，由以下组分制备而成：三元乙丙橡胶基体100份、天然橡胶15-25份、抗氧剂1-3份、光稳定剂0.5-1.2份、阻燃剂8-24份、交联剂0.2-1份、乙烯基三乙氧基硅烷偶联剂1-2份。本发明不含增塑剂，阻燃过程中不会产生烟雾，阻燃效果好；本发明阻燃剂由1∶3∶2∶3的红磷、三氧化二锑、蒙脱土、高岭土组成，原料易得，价格便宜，不含无机氢氧化物，对材料的力学和电性能影响较小。

Description

一种阻燃三元乙丙橡胶材料
 
技术领域
   本发明涉及橡胶领域，具体是一种阻燃三元乙丙橡胶材料。
背景技术
三元乙丙橡胶是乙烯、丙烯以及非共轭二烯烃的三元共聚物，具有优越的耐氧化、抗臭氧和抗侵蚀的能力，具有极好的硫化特性。
目前对三元乙丙橡胶进行阻燃的文献很多，其中氢氧化物集阻燃、抑烟、填充三重功能于一体，燃烧时无毒、无腐蚀性物质产生，原料易得、价廉，但由于其加入量较大，对聚合物的力学和电性能影响严重。
发明内容
本发明的目的在于提供一种阻燃三元乙丙橡胶材料。
本发明的目的可以通过以下技术方案实现：
一种阻燃三元乙丙橡胶材料，其特征在于，按照重量份计，由以下组分制备而成：三元乙丙橡胶基体100份、天然橡胶15-25份、抗氧剂1-3份、光稳定剂0.5-1.2份、阻燃剂8-24份、交联剂0.2-1份、乙烯基三乙氧基硅烷偶联剂1-2份。
本发明按照重量份计，由以下组分制备而成：三元乙丙橡胶基体100份、天然橡胶20份、抗氧剂2份、光稳定剂0.9份、阻燃剂16份、交联剂0.6份、乙烯基三乙氧基硅烷偶联剂1.5份。
所述阻燃剂为重量比为1:3:2:2的红磷、三氧化二锑、蒙脱土、高岭土组成。
本发明的有益效果：本发明不含增塑剂，阻燃过程中不会产生烟雾，阻燃效果好；本发明阻燃剂由1:3:2:3的红磷、三氧化二锑、蒙脱土、高岭土组成，原料易得，价格便宜，不含无机氢氧化物，对材料的力学和电性能影响较小。
具体实施方式
下面结合具体实施例对本发明作进一步详细描述。
实施例1
一种阻燃三元乙丙橡胶材料，按照重量份计，由以下组分制备而成：三元乙丙橡胶基体100份、天然橡胶20份、抗氧剂2份、光稳定剂0.9份、红磷2份、三氧化二锑6份、蒙脱土4份、高岭土4份、交联剂0.6份、乙烯基三乙氧基硅烷偶联剂1.5份。
实施例2
一种阻燃三元乙丙橡胶材料，其特征在于，按照重量份计，由以下组分制备而成：三元乙丙橡胶基体100份、天然橡胶15份、抗氧剂1份、光稳定剂0.5份、红磷1份、三氧化二锑3份、蒙脱土2份、高岭土2份、交联剂0.2份、乙烯基三乙氧基硅烷偶联剂1份。
实施例3
一种阻燃三元乙丙橡胶材料，其特征在于，按照重量份计，由以下组分制备而成：三元乙丙橡胶基体100份、天然橡胶25份、抗氧剂3份、光稳定剂1.2份、红磷3份、三氧化二锑9份、蒙脱土6份、高岭土6份、交联剂1份、乙烯基三乙氧基硅烷偶联剂2份。

Claims (3)

1.一种阻燃三元乙丙橡胶材料，其特征在于，按照重量份计，由以下组分制备而成：三元乙丙橡胶基体100份、天然橡胶15-25份、抗氧剂1-3份、光稳定剂0.5-1.2份、阻燃剂8-24份、交联剂0.2-1份、乙烯基三乙氧基硅烷偶联剂1-2份。
2. 根据权利要求1所述的阻燃三元乙丙橡胶材料，其特征在于，按照重量份计，由以下组分制备而成：三元乙丙橡胶基体100份、天然橡胶20份、抗氧剂2份、光稳定剂0.9份、阻燃剂16份、交联剂0.6份、乙烯基三乙氧基硅烷偶联剂1.5份。
3. 根据权利要求1或2所述的阻燃三元乙丙橡胶材料，其特征在于，所述阻燃剂为重量比为1:3:2:2的红磷、三氧化二锑、蒙脱土、高岭土组成。
 
CN201310522832.5A 2013-10-30 2013-10-30 一种阻燃三元乙丙橡胶材料 Pending CN103601982A (zh)