CN103555259B - 水性聚氨酯胶黏剂及其制备方法 - Google Patents

水性聚氨酯胶黏剂及其制备方法 Download PDF

Info

Publication number
CN103555259B
CN103555259B CN201310529931.6A CN201310529931A CN103555259B CN 103555259 B CN103555259 B CN 103555259B CN 201310529931 A CN201310529931 A CN 201310529931A CN 103555259 B CN103555259 B CN 103555259B
Authority
CN
China
Prior art keywords
component
polyether glycol
aqueous polyurethane
polyurethane adhesives
tdi
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310529931.6A
Other languages
English (en)
Other versions
CN103555259A (zh
Inventor
陈鹏
耿佃勇
董伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zibo Dexin Lianbang Chemical Industry Co Ltd
Original Assignee
Zibo Dexin Lianbang Chemical Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zibo Dexin Lianbang Chemical Industry Co Ltd filed Critical Zibo Dexin Lianbang Chemical Industry Co Ltd
Priority to CN201310529931.6A priority Critical patent/CN103555259B/zh
Publication of CN103555259A publication Critical patent/CN103555259A/zh
Application granted granted Critical
Publication of CN103555259B publication Critical patent/CN103555259B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种水性聚氨酯胶黏剂及其制备方法，属于化工领域。本发明由A和B两种组分按照以下重量份数比配制而成：A组分：TDI-8010-12份；聚醚多元醇A33～37份；DMPA3～4份；TEA1～2份；扩链剂0.05～0.3份；溶剂8.0～9.0份；B组分：TDI-8016～17份；IPDI15～17份；聚醚多元醇B10～15份；聚醚多元醇C8～9份；溶剂30.0～40.0份。本发明采用双组份水性聚氨酯胶黏剂合成的A组份和B组份储存稳定性好，进一步提高产品的韧性。

Description

水性聚氨酯胶黏剂及其制备方法
技术领域
本发明涉及一种水性聚氨酯胶黏剂及其制备方法，属于化工领域。
背景技术
目前聚氨酯胶黏剂类型、品种很多，但是大多数聚氨酯胶黏剂采用有机溶剂，其缺点是有机溶剂易燃易爆、易挥发、气味大、使用时还会造成空气污染，而且还具有一些毒性。水性聚氨酯胶黏剂以水为基本介质，具有不燃，气味小，不污染环境，节能操作方便等优点。
发明内容
本发明的目的是提供一种水性聚氨酯胶黏剂及其制备方法，采用双组份水性聚氨酯胶黏剂合成的A组份和B组份储存稳定性好，制作的制品粘性得到极大的提高，加快了固化以及后期熟化时间，还进一步提高产品的韧性。
本发明水性聚氨酯胶黏剂，由A和B两种组分按照以下重量份数比配制而成：
A组分：
B组分
所述扩链剂为DE201，官能度为2，聚氧乙烯链段50～65％、分子量为1000的高聚物，生产厂家为淄博德信联邦化学工业有限公司生产的聚醚多元醇。扩链剂为聚醚多元醇型扩链剂，能够提高产品的韧性。
聚醚多元醇A为官能度3，分子量为1000的聚醚多元醇，牌号DMN-1000。
聚醚多元醇B为能度为2，分子量为4000的聚醚多元醇，牌号DDL-4000D。
聚醚多元醇C为官能度为3，分子量为350的聚醚多元醇，牌号为DEP-303B。
TDI-80、DMPA、TEA、IPDI均为市购。
聚醚多元醇A、聚醚多元醇B和聚醚多元醇C生产厂家均为淄博德信联邦化学工业有限公司醇。
A与B组份的溶剂为丙酮。
所述水性聚氨酯胶黏剂的制备方法如下：
A组分制备：将TDI-80与聚醚多元醇A混合，在70-90℃条件下，搅拌反应0.5-1.5小时后，加入DMPA继续反应，使NCO质量分数达到2.6-3.0%，加入丙酮制得预聚体，将扩链剂DE201和成盐剂TEA的，加入到去离子水中，再加入预聚体中充分搅拌，分散得A组分；
B组分制备：将聚醚多元醇B，聚醚多元醇C，异氰酸酯TDI-80和IPDI加入容器中，65-75℃反应0.5-1.5小时，测定NCO质量分数为5.5-6.5%，加入溶剂冷却出料备用。
A与B组份按照质量比100：10-12混合，用转速高于2000-2500r/min强力搅拌器搅拌3-5min，混合液呈乳白色，密度为1.05-1.07g/ml，可用于涂布和粘结。
与现有技术相比，本发明具有以下有益效果：
本发明采用双组份水性聚氨酯胶黏剂合成的A组份和B组份储存稳定性好，制作的制品粘性得到极大的提高，加快了固化以及后期熟化时间，还进一步提高产品的韧性。
具体实施方式
下面结合实施例对本发明做进一步的说明。
实施例1
本实施例水性聚氨酯胶黏剂，由A和B两种组分按照以下重量份数比配制而成：
A组分：
B组分：
所述水性聚氨酯胶黏剂的制备方步骤如下：
A组分制备：将TDI-80与聚醚多元醇A按照配方比例混合，在70℃条件下，搅拌反应1.5小时后，加入DMPA继续反应，使NCO质量分数达到2.6%，加入丙酮制得预聚体，将扩链剂DE201和成盐剂TEA加入到去离子水中混合后，再加入到预聚体中充分搅拌，分散得A组分。
B组分制备：将聚醚多元醇B，聚醚多元醇C，异氰酸酯TDI和IPDI加入容器中，70℃反应1小时，测定NCO质量分数6.0%，加入丙酮冷却出料备用。
A和B组份按照质量比100：10混合，用转速高于2000r/min强力搅拌器搅拌3min。
混合液呈乳白色，密度为1.05g/ml，可用于涂布和粘结。
实施例2
本发明实施例水性聚氨酯胶黏剂，由A和B两种组分按照以下重量份数比配制而成：
A组分：
B组分：
所述水性聚氨酯胶黏剂的制备方步骤如下：
A组分制备：将TDI-80与聚醚多元醇A按照配方比例混合，在80℃条件下，搅拌反应1小时后，加入DMPA继续反应，使NCO质量分数达到3.0%，加入丙酮制得预聚体，将扩链剂DE201和成盐剂TEA加入到去离子水中混合后，再加入到预聚体中充分搅拌，分散得A组分。
B组分制备：将聚醚多元醇B，聚醚多元醇C，异氰酸酯TDI和IPDI加入容器中，65℃反应1.5小时，测定NCO质量分数5.5%，加入丙酮冷却出料备用。
A和B组份按照质量比100：11混合，用转速高于2000r/min强力搅拌器搅拌4min。
混合液呈乳白色，密度为1.06g/ml，可用于涂布和粘结。改变配方中NCO的含量可进一步提高胶黏剂的初粘性。
实施例3
本发明实施例水性聚氨酯胶黏剂，由A和B两种组分按照以下重量份数比配制而成：
A组分：
B组分：
所述水性聚氨酯胶黏剂的制备方步骤如下：
A组分制备：将TDI-80与聚醚多元醇A按照配方比例混合，在90℃条件下，搅拌反应0.5小时后，加入DMPA继续反应，使NCO质量分数达到2.9%，加入丙酮制得预聚体，将扩链剂DE201和成盐剂TEA加入到去离子水中混合后，再加入到预聚体中充分搅拌，分散得A组分。
B组分制备：将聚醚多元醇B，聚醚多元醇C，聚醚多元醇D、异氰酸酯TDI和IPDI加入容器中，75℃反应0.8小时，测定NCO质量分数6.5%，加入丙酮冷却出料备用。
A和B组份按照质量比100：12混合，用转速高于2500r/min强力搅拌器搅拌5min。
混合液呈乳白色，密度为1.07g/ml，可用于涂布和粘结。改变配方中NCO的含量以及扩链剂DE201的量，可进一步提高胶黏剂后期的固化及粘结性能。

Claims (5)

1.一种水性聚氨酯胶黏剂，其特征在于，由A和B两种组分按照以下重量份数比的原料组成：
A组分：
TDI-8010-12份；
聚醚多元醇A33-37份；
DMPA3-4份；
TEA1-2份；
扩链剂0.05-0.3份；
溶剂8.0-9.0份；
B组分
TDI-8016-17份；
IPDI15-17份；
聚醚多元醇B10-15份；
聚醚多元醇C8-9份；
溶剂30.0-40.0份；
聚醚多元醇A为DMN-1000，聚醚多元醇B为DDL-4000D，聚醚多元醇C为DEP-303B。
2.根据权利要求1所述的水性聚氨酯胶黏剂，其特征在于，扩链剂为DE201，官能度为2，聚氧乙烯链段60-85％、分子量为1000。
3.根据权利要求1所述的水性聚氨酯胶黏剂，其特征在于，A与B组份的溶剂为丙酮。
4.一种权利要求1所述的水性聚氨酯胶黏剂的制备方法，其特征在于，步骤如下：
A组分制备：将TDI-80与聚醚多元醇A混合，在70-90℃条件下，搅拌反应0.5-1.5小时后，加入DMPA继续反应，使NCO质量分数达到2.6-3.0%，加入丙酮制得预聚体，将扩链剂DE201和成盐剂TEA的，加入到去离子水中，再加入预聚体中充分搅拌，分散得A组分；
B组分制备：将聚醚多元醇B，聚醚多元醇C，异氰酸酯TDI-80和IPDI加入容器中，65-75℃反应0.5-1.5小时，测定NCO质量分数为5.5-6.5%，加入溶剂冷却出料备用。
5.根据权利要求4所述的水性聚氨酯胶黏剂的制备方法，其特征在于，使用时，A与B组份按照质量比100：8-12混合，用转速高于1800-2500r/min强力搅拌器搅拌3-5min。
CN201310529931.6A 2013-10-31 2013-10-31 水性聚氨酯胶黏剂及其制备方法 Active CN103555259B (zh)