CN103555075A - 一种防火涂料 - Google Patents

一种防火涂料 Download PDF

Info

Publication number
CN103555075A
CN103555075A CN201310512826.1A CN201310512826A CN103555075A CN 103555075 A CN103555075 A CN 103555075A CN 201310512826 A CN201310512826 A CN 201310512826A CN 103555075 A CN103555075 A CN 103555075A
Authority
CN
China
Prior art keywords
parts
weight
raw material
retardant coating
frie retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201310512826.1A
Other languages
English (en)
Inventor
卢逸凡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310512826.1A priority Critical patent/CN103555075A/zh
Publication of CN103555075A publication Critical patent/CN103555075A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种防火涂料，由下述重量份数的原料制成：：合成树脂10～25份，聚磷酸铵12～20份，季戊四醇5～15份，三聚氰胺5～10份，柔性乳液10～20份，填料5～10份，颜料5～10份，混合溶剂15～35份。其制作步骤如下：(1)按重量份数取原料；(2)将合成树脂溶解后加入其它组分，搅拌均匀，经砂磨机或球磨机研磨分散；(3)经检验合格后，出料包装。本发明具有涂层薄、装饰性强、施工方便、防火性能高，应用范围广等优点。

Description

一种防火涂料
技术领域
本发明涉及一种建筑涂料，具体涉及一种防火涂料。
背景技术
防火涂料是用于可燃性基材表面，能降低被涂材料表面的可燃性、阻滞火灾的迅速蔓延，用以提高被涂材料耐火极限的一种特种涂料。目前，市场上提供的防火涂料涂层较厚、装饰性不强、施工不便，无法满足各种客户的需求。
发明内容
发明目的：为了克服现有技术中存在的不足，本发明提供一种涂层薄、装饰性强、施工方便、防火性能高，应用范围广的防火涂料。
技术方案：为解决上述技术问题，本发明的采用的技术方案为：一种防火涂料，由下述重量份数的原料制成：：合成树脂10～25份，聚磷酸铵12～20份，季戊四醇5～15份，三聚氰胺5～10份，柔性乳液10～20份，填料5～10份，颜料5～10份，混合溶剂15～35份；其制作步骤如下：
(1)按重量份数取原料；
(2)将合成树脂溶解后加入其它组分，搅拌均匀，经砂磨机或球磨机研磨分散；
(3)经检验合格后，出料包装。
作为优选，所述的柔性乳液包括氨丁胶乳或者丁基胶乳。
作为优选，所述的防火涂料由下述重量份数的原料制成：合成树脂15份，聚磷酸铵20份，季戊四醇10份，三聚氰胺5份，氨丁胶乳20份，填料5份，颜料5份，混合溶剂20份。
作为优选，所述的防火涂料由下述重量份数的原料制成：合成树脂20份，聚磷酸铵15份，季戊四醇8份，三聚氰胺10份，丁基胶乳15份，填料8份，颜料8份，混合溶剂25份。
有益效果：本发明提供的防火涂料为油性配方，具有很好的防火隔热性能、附着力好、强度高，能经受高低温循环的影响，涂层的耐水性、耐酸性、耐盐腐蚀性良好，不易脱落，储存稳定，装饰性能好且施工方便，适用于室外输水输油管道的防火处理，具有显著的防火效果。
具体实施方式
实施例一：
采用下述重量份数的原料：合成树脂15份，聚磷酸铵20份，季戊四醇10份，三聚氰胺5份，氨丁胶乳20份，填料5份，颜料5份，混合溶剂20份。
(1)按重量份数取原料；
(2)将合成树脂溶解后加入其它组分，搅拌均匀，经砂磨机或球磨机研磨分散；
(3)经检验合格后，出料包装。
实施例二：
采用下述重量份数的原料：合成树脂20份，聚磷酸铵15份，季戊四醇8份，三聚氰胺10份，丁基胶乳15份，填料8份，颜料8份，混合溶剂25份。
(1)按重量份数取原料；
(2)将合成树脂溶解后加入其它组分，搅拌均匀，经砂磨机或球磨机研磨分散；
(3)经检验合格后，出料包装。
以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (5)

1.一种防火涂料，其特征在于：该涂料由下述重量份数的原料制成：：合成树脂10～25份，聚磷酸铵12～20份，季戊四醇5～15份，三聚氰胺5～10份，柔性乳液10～20份，填料5～10份，颜料5～10份，混合溶剂15～35份。
2.根据权利要求1所述的防火涂料，其特征在于：所述的柔性乳液包括氨丁胶乳或者丁基胶乳。
3.根据权利要求1所述的防火涂料，其特征在于：由下述重量份数的原料制成：合成树脂15份，聚磷酸铵20份，季戊四醇10份，三聚氰胺5份，氨丁胶乳20份，填料5份，颜料5份，混合溶剂20份。
4.根据权利要求1所述的防火涂料，其特征在于：由下述重量份数的原料制成：合成树脂20份，聚磷酸铵15份，季戊四醇8份，三聚氰胺10份，丁基胶乳15份，填料8份，颜料8份，混合溶剂25份。
5.由权利要求1所述原料制作防火涂料的方法，其特征在于：包括如下步骤：
(1)按重量份数取原料；
(2)将合成树脂溶解后加入其它组分，搅拌均匀，经砂磨机或球磨机研磨分散；
(3)经检验合格后，出料包装。
CN201310512826.1A 2013-10-25 2013-10-25 一种防火涂料 Withdrawn CN103555075A (zh)