CN104845488A - 一种耐冲击防火涂料及其制备方法 - Google Patents
一种耐冲击防火涂料及其制备方法 Download PDFInfo
- Publication number
- CN104845488A CN104845488A CN201510198496.2A CN201510198496A CN104845488A CN 104845488 A CN104845488 A CN 104845488A CN 201510198496 A CN201510198496 A CN 201510198496A CN 104845488 A CN104845488 A CN 104845488A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- dickite
- preparation
- starch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种耐冲击防火涂料及其制备方法,由下列重量份原料制成:改性地开石粉5-8份、软质粘土15-30份、玻璃粉3-5份、膨胀蛭石5-6份、氢化蓖麻油3-4份、脲醛树脂10-15份、氯化橡胶2-4份、聚磷酸铵5-6份、钛酸酯偶联剂1-3份、季戊四醇5-6份、淀粉6-7份、硼酸锌2-3份、丁基胶乳6-8份、氟硅酸钠3-5份、乙基纤维素5-7份。制备方法:(1)将脲醛树脂、氯化橡胶、聚磷酸铵、钛酸酯偶联剂、季戊四醇、淀粉、丁基胶乳、氟硅酸钠混合;(2)加入改性地开石粉、软质粘土、膨胀蛭石、氢化蓖麻油、硼酸锌,混合均匀后研制细度至50-60um;(3)加入玻璃粉、乙基纤维素,分散搅匀后即得。本发明的防火涂料防火隔热性能好、粘接力好、涂料膜面附着力强、不易脱落、耐冲击。
Description
技术领域
本发明涉及消防材料技术领域,尤其涉及一种耐冲击防火涂料及其制备方法。
背景技术
目前,防火涂料在石油化工、电力、工业及民用建筑、机械等行业应用越来越广泛。防火涂料是用于可燃性基材表面、能降低被涂材料表面的可燃性、阻滞火灾的迅速蔓延,用以提高被涂材料耐火极限的一种特种涂料。但是现有的防火涂料存在涂料膜面附着力、耐冲击性差的问题。
发明内容
本发明的目的是克服现有技术的不足,提供一种防火隔热性能好、粘接力好、涂料膜面附着力强、不易脱落、耐冲击的防火涂料。
为了实现上述目的本发明采用如下技术方案:
一种耐冲击防火涂料,由下列重量份的原料制成:改性地开石粉5-8份、软质粘土15-30份、玻璃粉3-5份、膨胀蛭石5-6份、氢化蓖麻油3-4份、脲醛树脂10-15份、氯化橡胶2-4份、聚磷酸铵5-6份、钛酸酯偶联剂1-3份、季戊四醇5-6份、淀粉6-7份、硼酸锌2-3份、丁基胶乳6-8份、氟硅酸钠3-5份、乙基纤维素5-7份。
所述的改性地开石粉由以下方法制备:将地开石在300-500℃下煅烧3-5小时,冷却后,用8-12%双氧水溶液浸泡3-4小时,去离子水洗涤至中性,烘干,然后在其中加入相当于其重量1-2%的月桂酸醇酸钠、2-3%的六偏磷酸钠、1-2%的交联剂TAC,高速3500-3800转/分搅拌,30-40分钟后,烘干研磨成纳米粉末,即得。
所述的耐冲击防火涂料的制备方法,包括以下制备步骤:
(1)按上述重量份比例将脲醛树脂、氯化橡胶、聚磷酸铵、钛酸酯偶联剂、季戊四醇、淀粉、丁基胶乳、氟硅酸钠在1500-1600转/分下搅拌5-8min,混合均匀;
(2)再按上述重量份比例向步骤(1)的混料中依次加入改性地开石粉、软质粘土、膨胀蛭石、氢化蓖麻油、硼酸锌,在1800-2000转/分下搅拌20-25min,混合均匀后研制细度至50-60um;
(3)最后向步骤(2)的混料中依次加入玻璃粉、乙基纤维素,在600-800转/分下搅拌20-25min,分散搅匀后即得。
与已有技术相比,本发明的有益效果如下:
本发明通过添加改性地开石粉、软质粘土、玻璃粉等成分到防火涂料中,调整配方,解决现有的防火涂料膜面附着力、耐冲击性差的问题。本发明的防火涂料防火隔热性能好、粘接力好、涂料膜面附着力强、不易脱落、耐冲击,制备的防火涂料在重量为1kg,高度为150-200cm情况下冲击涂料,涂料没有异常现象发生。
具体实施方式
以下结合实施例对本发明作进一步的说明,但本发明不仅限于这些实施例,在未脱离本发明宗旨的前提下,所作的任何改进均落在本发明的保护范围之内。
实施例1:
一种耐冲击防火涂料,由下列重量份的原料制成:改性地开石粉5份、软质粘土30份、玻璃粉3份、膨胀蛭石6份、氢化蓖麻油3份、脲醛树脂10份、氯化橡胶2份、聚磷酸铵6份、钛酸酯偶联剂1份、季戊四醇6份、淀粉6份、硼酸锌2份、丁基胶乳8份、氟硅酸钠3份、乙基纤维素7份。
所述的改性地开石粉由以下方法制备:将地开石在300℃下煅烧5小时,冷却后,用8%双氧水溶液浸泡4小时,去离子水洗涤至中性,烘干,然后在其中加入相当于其重量1%的月桂酸醇酸钠、3%的六偏磷酸钠、1%的交联剂TAC,高速3500转/分搅拌,40分钟后,烘干研磨成纳米粉末,即得。
所述的耐冲击防火涂料的制备方法,包括以下制备步骤:
(1)按上述重量份比例将脲醛树脂、氯化橡胶、聚磷酸铵、钛酸酯偶联剂、季戊四醇、淀粉、丁基胶乳、氟硅酸钠在1500转/分下搅拌8min,混合均匀;
(2)再按上述重量份比例向步骤(1)的混料中依次加入改性地开石粉、软质粘土、膨胀蛭石、氢化蓖麻油、硼酸锌,在1800转/分下搅拌25min,混合均匀后研制细度至50um;
(3)最后向步骤(2)的混料中依次加入玻璃粉、乙基纤维素,在600转/分下搅拌25min,分散搅匀后即得。
实施例2:
一种耐冲击防火涂料,由下列重量份的原料制成:改性地开石粉8份、软质粘土15份、玻璃粉5份、膨胀蛭石5份、氢化蓖麻油4份、脲醛树脂10份、氯化橡胶3份、聚磷酸铵6份、钛酸酯偶联剂2份、季戊四醇6份、淀粉7份、硼酸锌3份、丁基胶乳7份、氟硅酸钠4份、乙基纤维素6份。
所述的改性地开石粉由以下方法制备:将地开石在500℃下煅烧3小时,冷却后,用12%双氧水溶液浸泡3小时,去离子水洗涤至中性,烘干,然后在其中加入相当于其重量2%的月桂酸醇酸钠、2%的六偏磷酸钠、2%的交联剂TAC,高速3500转/分搅拌,30分钟后,烘干研磨成纳米粉末,即得。
所述的耐冲击防火涂料的制备方法,包括以下制备步骤:
(1)按上述重量份比例将脲醛树脂、氯化橡胶、聚磷酸铵、钛酸酯偶联剂、季戊四醇、淀粉、丁基胶乳、氟硅酸钠在1600转/分下搅拌5min,混合均匀;
(2)再按上述重量份比例向步骤(1)的混料中依次加入改性地开石粉、软质粘土、膨胀蛭石、氢化蓖麻油、硼酸锌,在2000转/分下搅拌20min,混合均匀后研制细度至60um;
(3)最后向步骤(2)的混料中依次加入玻璃粉、乙基纤维素,在800转/分下搅拌20min,分散搅匀后即得。
Claims (3)
1.一种耐冲击防火涂料,其特征在于:由下列重量份的原料制成:改性地开石粉5-8份、软质粘土15-30份、玻璃粉3-5份、膨胀蛭石5-6份、氢化蓖麻油3-4份、脲醛树脂10-15份、氯化橡胶2-4份、聚磷酸铵5-6份、钛酸酯偶联剂1-3份、季戊四醇5-6份、淀粉6-7份、硼酸锌2-3份、丁基胶乳6-8份、氟硅酸钠3-5份、乙基纤维素5-7份。
2.根据权利要求1所述的耐冲击防火涂料,其特征在于:所述的改性地开石粉由以下方法制备:将地开石在300-500℃下煅烧3-5小时,冷却后,用8-12%双氧水溶液浸泡3-4小时,去离子水洗涤至中性,烘干,然后在其中加入相当于其重量1-2%的月桂酸醇酸钠、2-3%的六偏磷酸钠、1-2%的交联剂TAC,高速3500-3800转/分搅拌,30-40分钟后,烘干研磨成纳米粉末,即得。
3.一种如权利要求1或2所述的耐冲击防火涂料的制备方法,其特征在于:包括以下制备步骤:
(1)按上述重量份比例将脲醛树脂、氯化橡胶、聚磷酸铵、钛酸酯偶联剂、季戊四醇、淀粉、丁基胶乳、氟硅酸钠在1500-1600转/分下搅拌5-8min,混合均匀;
(2)再按上述重量份比例向步骤(1)的混料中依次加入改性地开石粉、软质粘土、膨胀蛭石、氢化蓖麻油、硼酸锌,在1800-2000转/分下搅拌20-25min,混合均匀后研制细度至50-60um;
(3)最后向步骤(2)的混料中依次加入玻璃粉、乙基纤维素,在600-800转/分下搅拌20-25min,分散搅匀后即得。