CN103554883A - 一种水杯壳体用abs改性聚碳酸酯材料及其制备方法 - Google Patents
一种水杯壳体用abs改性聚碳酸酯材料及其制备方法 Download PDFInfo
- Publication number
- CN103554883A CN103554883A CN201310510395.5A CN201310510395A CN103554883A CN 103554883 A CN103554883 A CN 103554883A CN 201310510395 A CN201310510395 A CN 201310510395A CN 103554883 A CN103554883 A CN 103554883A
- Authority
- CN
- China
- Prior art keywords
- abs
- modified polycarbonate
- parts
- diatomite
- polycarbonate material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水杯壳体用ABS改性聚碳酸酯材料，其特征在于，由下列重量份的原料制成：聚碳酸酯500-520、ABS30-35、聚乙烯蜡粉12-15、异丙基二硬脂酰氧基铝酸酯1-2、硅藻土8-10、三氧化三锑7-9、助剂10-12；本发明通过ABS改性，是本发明聚碳酸酯材料具有很好的力学性能，韧性增强，从而利于工业化大生产，而且具有高强度及弹性系数、高冲击强度、使用温度范围广，成形收缩率低、尺寸安定性良好，无味无臭对人体无害符合卫生安全。
Description
技术领域
本发明涉及塑料领域，特别是一种水杯壳体用ABS改性聚碳酸酯材料及其制备方法。
背景技术
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物，由于聚碳酸酯结构上的特殊性，现已成为五大工程塑料中增长速度最快的通用工程塑料。由于聚碳酸酯制品具有质量轻，抗冲击和透明性好，用热水和腐蚀性溶液洗涤处理时不变形且保持透明的优点，一些领域PC瓶已完全取代玻璃瓶。据预测，随着人们对饮用水质量重视程度的不断提高，聚碳酸酯在这方面的用量增长速度将保持在10%以上，因此研发一种聚碳酸酯材料的水杯壳体是大势所趋。
发明内容
本发明的目的是提供一种水杯壳体用ABS改性聚碳酸酯材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种水杯壳体用ABS改性聚碳酸酯材料，由下列重量份的原料制成：聚碳酸酯500-520、ABS30-35、聚乙烯蜡粉12-15、异丙基二硬脂酰氧基铝酸酯1-2、硅藻土8-10、三氧化三锑7-9、助剂10-12；
所述助剂由下列重量份的原料制成：硅藻土40-45、二缩三丙二醇二丙烯酸酯3-4、双季戊四醇六丙烯酸酯2-3、三聚磷酸钠5-6、玉石4-5、硅烷偶联剂KH-550 1-2、交联剂TAC1-2、碳化硅4-5、聚异丁烯1-2；制备方法是将硅藻土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
本发明所述水杯壳体用ABS改性聚碳酸酯材料，由以下具体步骤制成：
（1）将ABS加热至熔融状态，加入聚乙烯蜡粉、异丙基二硬脂酰氧基铝酸酯、硅藻土、助剂，搅拌捏合15-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将干燥后的聚碳酸酯加热至245-285℃，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。
本发明具有以下优点：本发明通过ABS改性，是本发明聚碳酸酯材料具有很好的力学性能，韧性增强，从而利于工业化大生产，而且具有高强度及弹性系数、高冲击强度、使用温度范围广，成形收缩率低、尺寸安定性良好，无味无臭对人体无害符合卫生安全。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种水杯壳体用ABS改性聚碳酸酯材料，由下列重量份（公斤）的原料制成：聚碳酸酯500、ABS30、聚乙烯蜡粉12、异丙基二硬脂酰氧基铝酸酯1、硅藻土8、三氧化三锑7、助剂10；
所述助剂由下列重量份（公斤）的原料制成：硅藻土40、二缩三丙二醇二丙烯酸酯3、双季戊四醇六丙烯酸酯2、三聚磷酸钠6、玉石5、硅烷偶联剂KH-550 1、交联剂TAC1、碳化硅5、聚异丁烯1；制备方法是将硅藻土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
本发明所述水杯壳体用ABS改性聚碳酸酯材料，由以下具体步骤制成：
（1）将ABS加热至熔融状态，加入聚乙烯蜡粉、异丙基二硬脂酰氧基铝酸酯、硅藻土、助剂，搅拌捏合15-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将干燥后的聚碳酸酯加热至245-285℃，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。
本发明材料拉伸强度为50-55MPa, 伸长率10-15%，弯曲强度70-80MPA，缺口冲击强度370J/M。
Claims (2)
1.一种水杯壳体用ABS改性聚碳酸酯材料，其特征在于，由下列重量份的原料制成：聚碳酸酯500-520、ABS30-35、聚乙烯蜡粉12-15、异丙基二硬脂酰氧基铝酸酯1-2、硅藻土8-10、三氧化三锑7-9、助剂10-12；
所述助剂由下列重量份的原料制成：硅藻土40-45、二缩三丙二醇二丙烯酸酯3-4、双季戊四醇六丙烯酸酯2-3、三聚磷酸钠5-6、玉石4-5、硅烷偶联剂KH-550 1-2、交联剂TAC1-2、碳化硅4-5、聚异丁烯1-2；制备方法是将硅藻土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-400目粉末，与其它剩余成分混合，研磨分散均匀，即得。
2.根据权利要求1所述水杯壳体用ABS改性聚碳酸酯材料，其特征在于，由以下具体步骤制成：
（1）将ABS加热至熔融状态，加入聚乙烯蜡粉、异丙基二硬脂酰氧基铝酸酯、硅藻土、助剂，搅拌捏合15-25分钟，送入双螺杆挤出机造粒，得到A料；
（2）将干燥后的聚碳酸酯加热至245-285℃，加入其它剩余成分，搅拌6-10分钟，送入双螺杆挤出机上熔融挤出造粒，得到B料；
（3）将A、B料混合均匀后，在双螺杆挤出机上熔融挤出造粒，即得。