CN103525066A - 一种水杯壳体用pet树脂改性聚碳酸酯材料及其制备方法 - Google Patents

一种水杯壳体用pet树脂改性聚碳酸酯材料及其制备方法 Download PDF

Info

Publication number
CN103525066A
CN103525066A CN201310510393.6A CN201310510393A CN103525066A CN 103525066 A CN103525066 A CN 103525066A CN 201310510393 A CN201310510393 A CN 201310510393A CN 103525066 A CN103525066 A CN 103525066A
Authority
CN
China
Prior art keywords
parts
pet
resin
polycarbonate
polycarbonate material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310510393.6A
Other languages
English (en)
Inventor
吴秀杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI FUGUANG INDUSTRIAL CO LTD
Original Assignee
ANHUI FUGUANG INDUSTRIAL CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI FUGUANG INDUSTRIAL CO LTD filed Critical ANHUI FUGUANG INDUSTRIAL CO LTD
Priority to CN201310510393.6A priority Critical patent/CN103525066A/zh
Publication of CN103525066A publication Critical patent/CN103525066A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种水杯壳体用PET树脂改性聚碳酸酯材料,其特征在于,由下列重量份的原料制成:聚碳酸酯500-520、PET树脂40-45、高密度聚乙烯20-25、环己烷-1,2-二羧酸二异壬基酯12-15、偏苯三酸三辛酯2.5-3.0、羧甲基纤维素3-5、2.4.6-三(二甲胺基甲基)苯酚1-2、助剂10-12;本发明添加PET改性,增加了聚碳酸酯不开裂以及耐磨的特性,又保留了聚碳酸酯原有的高强度及弹性系数、高冲击强度、使用温度范围广等特点,生产简单,成本低,成形收缩率低、尺寸安定性良好,无味无臭对人体无害符合卫生安全,适合制作水杯壳体。

Description

一种水杯壳体用PET树脂改性聚碳酸酯材料及其制备方法
技术领域
本发明涉及塑料领域,特别是一种水杯壳体用PET树脂改性聚碳酸酯材料及其制备方法。
背景技术
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物,由于聚碳酸酯结构上的特殊性,现已成为五大工程塑料中增长速度最快的通用工程塑料。由于聚碳酸酯制品具有质量轻,抗冲击和透明性好,用热水和腐蚀性溶液洗涤处理时不变形且保持透明的优点,一些领域PC瓶已完全取代玻璃瓶。据预测,随着人们对饮用水质量重视程度的不断提高,聚碳酸酯在这方面的用量增长速度将保持在10%以上,因此研发一种聚碳酸酯材料的水杯壳体是大势所趋。
发明内容
本发明的目的是提供一种水杯壳体用PET树脂改性聚碳酸酯材料及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种水杯壳体用PET树脂改性聚碳酸酯材料,由下列重量份的原料制成:聚碳酸酯500-520、PET树脂40-45、高密度聚乙烯20-25、环己烷-1,2-二羧酸二异壬基酯12-15、偏苯三酸三辛酯2.5-3.0、羧甲基纤维素3-5、2.4.6-三(二甲胺基甲基)苯酚1-2、助剂10-12;
所述助剂由下列重量份的原料制成:硅藻土40-45、二缩三丙二醇二丙烯酸酯3-4、双季戊四醇六丙烯酸酯2-3、三聚磷酸钠5-6、玉石4-5、硅烷偶联剂KH-550 1-2、交联剂TAC1-2、碳化硅4-5、聚异丁烯1-2;制备方法是将硅藻土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时,冷却,放入10-12%盐酸溶液中浸泡1-2小时,过滤取出,用清水洗净烘干,粉碎成200-400目粉末,与其它剩余成分混合,研磨分散均匀,即得。
本发明所述水杯壳体用PET树脂改性聚碳酸酯材料,由以下具体步骤制成:
(1)将高密度聚乙烯加热至熔融状态,加入环己烷-1,2-二羧酸二异壬基酯、偏苯三酸三辛酯、羧甲基纤维素、助剂,搅拌捏合15-25分钟,送入双螺杆挤出机造粒,得到A料;
(2)将干燥后的聚碳酸酯加热至240-280℃,加入其它剩余成分,搅拌7-10分钟,送入双螺杆挤出机上熔融挤出造粒,得到B料;
(3)将A、B料混合均匀后,在双螺杆挤出机上熔融挤出造粒,即得。
本发明具有以下优点:本发明添加PET改性,增加了聚碳酸酯不开裂以及耐磨的特性,又保留了聚碳酸酯原有的高强度及弹性系数、高冲击强度、使用温度范围广等特点,生产简单,成本低,成形收缩率低、尺寸安定性良好,无味无臭对人体无害符合卫生安全,适合制作水杯壳体。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种水杯壳体用PET树脂改性聚碳酸酯材料,由下列重量份(公斤)的原料制成:聚碳酸酯500、PET树脂40、高密度聚乙烯20、环己烷-1,2-二羧酸二异壬基酯12、偏苯三酸三辛酯2.5、羧甲基纤维素3、2.4.6-三(二甲胺基甲基)苯酚1、助剂10;
所述助剂由下列重量份(公斤)的原料制成:硅藻土40、二缩三丙二醇二丙烯酸酯3、双季戊四醇六丙烯酸酯2、三聚磷酸钠6、玉石5、硅烷偶联剂KH-550 1、交联剂TAC1、碳化硅5、聚异丁烯1;制备方法是将硅藻土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时,冷却,放入10-12%盐酸溶液中浸泡1-2小时,过滤取出,用清水洗净烘干,粉碎成200-400目粉末,与其它剩余成分混合,研磨分散均匀,即得。
本发明所述水杯壳体用PET树脂改性聚碳酸酯材料,由以下具体步骤制成:
(1)将高密度聚乙烯加热至熔融状态,加入环己烷-1,2-二羧酸二异壬基酯、偏苯三酸三辛酯、羧甲基纤维素、助剂,搅拌捏合15-25分钟,送入双螺杆挤出机造粒,得到A料;
(2)将干燥后的聚碳酸酯加热至240-280℃,加入其它剩余成分,搅拌7-10分钟,送入双螺杆挤出机上熔融挤出造粒,得到B料;
(3)将A、B料混合均匀后,在双螺杆挤出机上熔融挤出造粒,即得。
本发明材料拉伸强度为50-55MPa, 伸长率10-15%,弯曲强度70-80MPA,缺口冲击强度370J/M。

Claims (2)

1.一种水杯壳体用PET树脂改性聚碳酸酯材料,其特征在于,由下列重量份的原料制成:聚碳酸酯500-520、PET树脂40-45、高密度聚乙烯20-25、环己烷-1,2-二羧酸二异壬基酯12-15、偏苯三酸三辛酯2.5-3.0、羧甲基纤维素3-5、2.4.6-三(二甲胺基甲基)苯酚1-2、助剂10-12;
所述助剂由下列重量份的原料制成:硅藻土40-45、二缩三丙二醇二丙烯酸酯3-4、双季戊四醇六丙烯酸酯2-3、三聚磷酸钠5-6、玉石4-5、硅烷偶联剂KH-550 1-2、交联剂TAC1-2、碳化硅4-5、聚异丁烯1-2;制备方法是将硅藻土、玉石混合放入煅烧炉中在700-720℃下煅烧3-4小时,冷却,放入10-12%盐酸溶液中浸泡1-2小时,过滤取出,用清水洗净烘干,粉碎成200-400目粉末,与其它剩余成分混合,研磨分散均匀,即得。
2.根据权利要求1所述水杯壳体用PET树脂改性聚碳酸酯材料,其特征在于,由以下具体步骤制成:
(1)将高密度聚乙烯加热至熔融状态,加入环己烷-1,2-二羧酸二异壬基酯、偏苯三酸三辛酯、羧甲基纤维素、助剂,搅拌捏合15-25分钟,送入双螺杆挤出机造粒,得到A料;
(2)将干燥后的聚碳酸酯加热至240-280℃,加入其它剩余成分,搅拌7-10分钟,送入双螺杆挤出机上熔融挤出造粒,得到B料;
(3)将A、B料混合均匀后,在双螺杆挤出机上熔融挤出造粒,即得。
CN201310510393.6A 2013-10-26 2013-10-26 一种水杯壳体用pet树脂改性聚碳酸酯材料及其制备方法 Pending CN103525066A (zh)