CN103525067A - 一种sebs改性的聚碳酸酯水杯壳体材料及其制备方法 - Google Patents
一种sebs改性的聚碳酸酯水杯壳体材料及其制备方法 Download PDFInfo
- Publication number
- CN103525067A CN103525067A CN201310510399.3A CN201310510399A CN103525067A CN 103525067 A CN103525067 A CN 103525067A CN 201310510399 A CN201310510399 A CN 201310510399A CN 103525067 A CN103525067 A CN 103525067A
- Authority
- CN
- China
- Prior art keywords
- parts
- sebs
- polycarbonate
- water cup
- cup shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种SEBS改性的聚碳酸酯水杯壳体材料,其特征在于,由下列重量份的原料制成:聚碳酸酯500-520、SEBS30-35、聚-4-甲基-1-戊烯12-16、轻质碳酸钙15-20、二甲基二巯基乙酸异辛酯锡1-1.5、邻苯二甲酸二异丁酯6-9、麦饭石粉2.3-2.5、石英砂粉10-12、柠檬酸三乙酯3.6-3.8、助剂10-12;本发明添加SEBS,提高了聚碳酸酯的耐低温型以及抗应力开裂性能,而且该发明材料具高强度及弹性系数、高冲击强度、使用温度范围广,成形收缩率低、尺寸安定性良好,成型表面光洁度高,适合制作水杯壳体。
Description
技术领域
本发明涉及塑料领域,特别是一种SEBS改性的聚碳酸酯水杯壳体材料及其制备方法。
背景技术
聚碳酸酯(简称PC)是分子链中含有碳酸酯基的高分子聚合物,由于聚碳酸酯结构上的特殊性,现已成为五大工程塑料中增长速度最快的通用工程塑料。由于聚碳酸酯制品具有质量轻,抗冲击和透明性好,用热水和腐蚀性溶液洗涤处理时不变形且保持透明的优点,一些领域PC瓶已完全取代玻璃瓶。据预测,随着人们对饮用水质量重视程度的不断提高,聚碳酸酯在这方面的用量增长速度将保持在10%以上,因此研发一种聚碳酸酯材料的水杯壳体是大势所趋。
发明内容
本发明的目的是提供一种SEBS改性的聚碳酸酯水杯壳体材料及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种SEBS改性的聚碳酸酯水杯壳体材料,由下列重量份的原料制成:聚碳酸酯500-520、SEBS30-35、聚-4-甲基-1-戊烯12-16、轻质碳酸钙15-20、二甲基二巯基乙酸异辛酯锡1-1.5、邻苯二甲酸二异丁酯6-9、麦饭石粉2.3-2.5、石英砂粉10-12、柠檬酸三乙酯3.6-3.8、助剂10-12;
所述助剂由下列重量份的原料制成:硅藻土40-45、丙烯酸二甲基氨基乙酯4-5、二缩三丙二醇二丙烯酸酯2-3、氧化锌5-6、玉石4-5、3-氨丙基三甲氧基硅烷2-3、交联剂TAC1-2、葡萄糖酸锌1-2、硬脂酸锌1-2、玫瑰精油0.1-0.2;制备方法是将硅藻土、玉石混合放入煅烧炉中在710-740℃下煅烧3-4小时,冷却,放入10-12%盐酸溶液中浸泡1-2小时,过滤取出,用清水洗净烘干,粉碎成200-400目粉末,与其它剩余成分混合,研磨分散均匀,即得。
本发明所述SEBS改性的聚碳酸酯水杯壳体材料,由以下具体步骤制成:
(1)将聚-4-甲基-1-戊烯加热至熔融状态,加入轻质碳酸钙、二甲基二巯基乙酸异辛酯锡、邻苯二甲酸二异丁酯、麦饭石粉、助剂,搅拌捏合15-25分钟,送入双螺杆挤出机造粒,得到A料;
(2)将干燥后的聚碳酸酯加热至250-285℃,加入其它剩余成分,搅拌7-10分钟,送入双螺杆挤出机上熔融挤出造粒,得到B料;
(3)将A、B料混合均匀后,在双螺杆挤出机上熔融挤出造粒,即得。
本发明具有以下优点:本发明添加SEBS,提高了聚碳酸酯的耐低温型以及抗应力开裂性能,而且该发明材料具高强度及弹性系数、高冲击强度、使用温度范围广,成形收缩率低、尺寸安定性良好,成型表面光洁度高,适合制作水杯壳体。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种SEBS改性的聚碳酸酯水杯壳体材料,由下列重量份(公斤)的原料制成:聚碳酸酯500、SEBS30、聚-4-甲基-1-戊烯12、轻质碳酸钙15、二甲基二巯基乙酸异辛酯锡1、邻苯二甲酸二异丁酯6、麦饭石粉2.3、石英砂粉10、柠檬酸三乙酯3.6、助剂10;
所述助剂由下列重量份(公斤)的原料制成:硅藻土40、丙烯酸二甲基氨基乙酯5、二缩三丙二醇二丙烯酸酯3、氧化锌5、玉石4、3-氨丙基三甲氧基硅烷2、交联剂TAC2、葡萄糖酸锌2、硬脂酸锌2、玫瑰精油0.1;制备方法是将硅藻土、玉石混合放入煅烧炉中在710-740℃下煅烧3-4小时,冷却,放入10-12%盐酸溶液中浸泡1-2小时,过滤取出,用清水洗净烘干,粉碎成200-400目粉末,与其它剩余成分混合,研磨分散均匀,即得。
本发明所述SEBS改性的聚碳酸酯水杯壳体材料,由以下具体步骤制成:
(1)将聚-4-甲基-1-戊烯加热至熔融状态,加入轻质碳酸钙、二甲基二巯基乙酸异辛酯锡、邻苯二甲酸二异丁酯、麦饭石粉、助剂,搅拌捏合15-25分钟,送入双螺杆挤出机造粒,得到A料;
(2)将干燥后的聚碳酸酯加热至250-285℃,加入其它剩余成分,搅拌7-10分钟,送入双螺杆挤出机上熔融挤出造粒,得到B料;
(3)将A、B料混合均匀后,在双螺杆挤出机上熔融挤出造粒,即得。
本发明材料拉伸强度为50-55MPa, 伸长率10-15%,弯曲强度70-80MPA,缺口冲击强度370J/M。
Claims (2)
1.一种SEBS改性的聚碳酸酯水杯壳体材料,其特征在于,由下列重量份的原料制成:聚碳酸酯500-520、SEBS30-35、聚-4-甲基-1-戊烯12-16、轻质碳酸钙15-20、二甲基二巯基乙酸异辛酯锡1-1.5、邻苯二甲酸二异丁酯6-9、麦饭石粉2.3-2.5、石英砂粉10-12、柠檬酸三乙酯3.6-3.8、助剂10-12;
所述助剂由下列重量份的原料制成:硅藻土40-45、丙烯酸二甲基氨基乙酯4-5、二缩三丙二醇二丙烯酸酯2-3、氧化锌5-6、玉石4-5、3-氨丙基三甲氧基硅烷2-3、交联剂TAC1-2、葡萄糖酸锌1-2、硬脂酸锌1-2、玫瑰精油0.1-0.2;制备方法是将硅藻土、玉石混合放入煅烧炉中在710-740℃下煅烧3-4小时,冷却,放入10-12%盐酸溶液中浸泡1-2小时,过滤取出,用清水洗净烘干,粉碎成200-400目粉末,与其它剩余成分混合,研磨分散均匀,即得。
2.根据权利要求1所述SEBS改性的聚碳酸酯水杯壳体材料,其特征在于,由以下具体步骤制成:
(1)将聚-4-甲基-1-戊烯加热至熔融状态,加入轻质碳酸钙、二甲基二巯基乙酸异辛酯锡、邻苯二甲酸二异丁酯、麦饭石粉、助剂,搅拌捏合15-25分钟,送入双螺杆挤出机造粒,得到A料;
(2)将干燥后的聚碳酸酯加热至250-285℃,加入其它剩余成分,搅拌7-10分钟,送入双螺杆挤出机上熔融挤出造粒,得到B料;
(3)将A、B料混合均匀后,在双螺杆挤出机上熔融挤出造粒,即得。