CN103554854B - 一种ttr混合基用bopet - Google Patents

一种ttr混合基用bopet Download PDF

Info

Publication number
CN103554854B
CN103554854B CN201310550219.4A CN201310550219A CN103554854B CN 103554854 B CN103554854 B CN 103554854B CN 201310550219 A CN201310550219 A CN 201310550219A CN 103554854 B CN103554854 B CN 103554854B
Authority
CN
China
Prior art keywords
bopet
ttr
nano
mixed base
microns
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310550219.4A
Other languages
English (en)
Other versions
CN103554854A (zh
Inventor
李东升
韩冰冰
李加坤
李娟�
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiaozuo Zhuoli Film Material Co ltd
Original Assignee
Zhuoli Imaging Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhuoli Imaging Technology Co ltd filed Critical Zhuoli Imaging Technology Co ltd
Priority to CN201310550219.4A priority Critical patent/CN103554854B/zh
Publication of CN103554854A publication Critical patent/CN103554854A/zh
Application granted granted Critical
Publication of CN103554854B publication Critical patent/CN103554854B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于BOPET领域，具体涉及一种TTR混合基用BOPET。该BOPET产品，厚度为4.3微米，由基料和纳米硅母料制备而成；其中基料含量为50%~65%。本发明相较于现有技术中使用的4.5微米过渡产品，通过纳米硅添加剂的使用，降低了薄膜的粗糙度，使TTR打印噪音大幅降低，可低于89分贝；所制备的BOPET产品的热稳定性、剥离性、洁净度及对涂布溶剂的表面适应性等各项性能更适于TTR混合基高速涂布专用。

Description

一种TTR混合基用BOPET
技术领域
本发明属于BOPET（双向拉伸聚酯薄膜）领域，具体涉及一种TTR（热转印色带）混合基用BOPET。
背景技术
目前，在TTR混合基高速涂布中使用的BOPET一般为电容器专用或为生产电容器专用BOPET的4.5微米过渡产品，没有TTR混合基高速涂布专用4.3微米BOPET。电容器用BOPET的4.5微米过渡产品从原料到工艺，全是针对电容器膜的耐击穿、绝缘等性能，无法满足TTR混合基高速涂布所需要的热稳定性、涂布后低噪音等性能要求。
发明内容
本发明目的在于提供一种TTR混合基高速涂布专用4.3微米BOPET。
本发明的技术方案如下：
一种TTR混合基用BOPET，厚度为4.3微米，由基料和纳米硅母料制备而成；
所述基料为PET，即聚对苯二甲酸乙二醇酯；
所述纳米硅母料为聚对苯二甲酸乙二醇酯与纳米SiO2的混合物，其中纳米SiO2的粒径为100nm~500nm，含量为3000~8000ppm。
所述TTR混合基用BOPET，以质量百分比计，基料含量为50%~65%。
所述TTR混合基用BOPET，以质量百分比计，基料含量为55%。
需要说明的是，为更好的制备4.3微米的BOPET，制备本发明TTR混合基高速涂布专用4.3微米的BOPET的生产线上的相关生产设备由奥地利安德里茨公司所生产，所引进的生产设备在MDO（纵向拉伸）、TDO（横向拉伸）区域相较于国内设备能够更好的满足生产所需。
本发明相较于现有技术中使用的4.5微米过渡产品，通过纳米硅添加剂的使用，降低了薄膜的粗糙度，使TTR打印噪音大幅降低，可低于89分贝；所制备的BOPET产品的热稳定性、剥离性、洁净度及对涂布溶剂的表面适应性等各项性能更适于TTR混合基高速涂布专用。
具体实施方式
下面结合实施例对本发明做进一步的介绍说明。
实施例1
按基料与纳米硅母料=5：5的质量比进行配制，所述基料为聚对苯二甲酸乙二醇酯；所述纳米硅母料为聚对苯二甲酸乙二醇酯与纳米SiO2的混合物，其中纳米SiO2的粒径为100nm~500nm，含量为5000ppm。
将配制好的原料经混合、干燥后，进入挤出机在280℃温度下进行原料熔融，首先将熔融后原料经过5μm高精度过滤器过滤后，在T型模头挤出并在急冷辊冷却，后经过MDO55℃~76℃的预热后，进行3.65倍纵拉和TDO的4.1倍横拉，在TDO横拉末段进行冷却结晶处理，然后再经过切边、收卷等工序收成半成品，最后经分切、包装后，成为TTR混合基高速涂布专用4.3微米BOPET成品。
对本实施例制备的BOPET成品进行分切，成品优等级品率可达89%，涂布A级品率可达83%。
对本实施例制备的TTR混合基高速涂布专用4.3微米BOPET成品的主要物化指标测定如下表所示：
实施例2
制备方法同实施例1，仅调整基料与纳米硅母料按5.5：4.5的质量比进行配制，所述基料为聚对苯二甲酸乙二醇酯；所述纳米硅母料为聚对苯二甲酸乙二醇酯与纳米SiO2的混合物，其中纳米SiO2的粒径为100nm~500nm，含量为5000ppm。
对本实施例制备的BOPET成品进行分切，成品优等级品率可达94%，涂布A级品率可达88%。
对本实施例制备的TTR混合基高速涂布专用4.3微米BOPET成品的主要物化指标测定如下表所示：
实施例3
制备方法同实施例1，仅调整基料与纳米硅母料按6：4的质量比进行配制，所述基料为聚对苯二甲酸乙二醇酯；所述纳米硅母料为聚对苯二甲酸乙二醇酯与纳米SiO2的混合物，其中纳米SiO2的粒径为100nm~500nm，含量为5000ppm。
对本实施例制备的BOPET成品进行分切，成品优等级品率可达88%，涂布A级品率可达82%。
对本实施例制备的TTR混合基高速涂布专用4.3微米BOPET成品的主要物化指标测定如下表所示：
实施例4
制备方法同实施例1，仅调整基料与纳米硅母料按6.5：3.5的质量比进行配制，所述基料为聚对苯二甲酸乙二醇酯；所述纳米硅母料为聚对苯二甲酸乙二醇酯与纳米SiO2的混合物，其中纳米SiO2的粒径为100nm~500nm，含量为5000ppm。
对本实施例制备的BOPET成品进行分切，成品优等级品率可达83%，涂布A级品率可达75%。
对本实施例制备的TTR混合基高速涂布专用4.3微米BOPET成品的主要物化指标测定如下表所示：
上述实施例为本发明的较佳实施例，从上述实施例所制备的TTR混合基高速涂布用BOPET产品性能来看，实施例2即基料与纳米硅母料=5.5：4.5的质量比制备的BOPET产品性能最好，故实施例2最本发明的最佳实施例。

Claims (1)

1.BOPET在TTR方面的应用，其特征在于，作为TTR混合基用BOPET；所述BOPET厚度为4.3微米，由基料和纳米硅母料制备而成；
所述基料为聚对苯二甲酸乙二醇酯；
所述纳米硅母料为聚对苯二甲酸乙二醇酯与纳米SiO2的混合物，其中纳米SiO2的粒径为100nm~500nm，含量为3000~8000ppm；
以质量百分比计，基料含量为50%~65%；
其制备过程为：
将配制好的原料经混合、干燥后，进入挤出机在280℃温度下进行原料熔融，首先将熔融后原料经过5μm高精度过滤器过滤后，在T型模头挤出并在急冷辊冷却，后经过MDO55℃~76℃的预热后，进行3.65倍纵拉和TDO的4.1倍横拉，在TDO横拉末段进行冷却结晶处理，然后再经过切边、收卷工序收成半成品，最后经分切、包装后，成为TTR混合基高速涂布专用4.3微米BOPET成品。
CN201310550219.4A 2013-11-08 2013-11-08 一种ttr混合基用bopet Active CN103554854B (zh)