CN103554701A - 一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料 - Google Patents

一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料 Download PDF

Info

Publication number
CN103554701A
CN103554701A CN201310525713.5A CN201310525713A CN103554701A CN 103554701 A CN103554701 A CN 103554701A CN 201310525713 A CN201310525713 A CN 201310525713A CN 103554701 A CN103554701 A CN 103554701A
Authority
CN
China
Prior art keywords
parts
polystyrene
insulating material
wire harness
oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310525713.5A
Other languages
English (en)
Inventor
柳彬盛
琚克刚
琚一雄
郜海文
周玉献
张燕
刘鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Deren Electronic Devices Co Ltd
Original Assignee
Hefei Deren Electronic Devices Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Deren Electronic Devices Co Ltd filed Critical Hefei Deren Electronic Devices Co Ltd
Priority to CN201310525713.5A priority Critical patent/CN103554701A/zh
Publication of CN103554701A publication Critical patent/CN103554701A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种线束用绝缘材料，具体涉及一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料，该材料包含以下重量份的原料：聚苯乙烯24-28，聚醋酸乙烯12-14，ABS高胶粉12-15，低密度聚乙烯20-23，三烯丙基异氰脲酸酯3-4，双叔丁基过氧化二异丙基苯4-5，三聚磷酸钠3-4，硅酸钠2-3，橘子油2-3，钛白粉20-23，N351炭黑10-12，二甲基二巯基乙酸异辛酯锡2-3，木质素磺酸钠2-3，羟基硅油15-18，四氧化三铁4-6，柠檬酸三乙酯20-23，助剂14-16；该绝缘材料结合了聚苯乙烯、聚醋酸乙烯、ABS高胶粉、低密度聚乙烯等原料的优点，提升了传统聚苯乙烯材料的性能，使其具有良好的加工性能和力学性能，制备的材料柔韧耐冲击，防水防潮，耐化学腐蚀，使用寿命长，能够广泛的用于制作家电各部位线束的绝缘护套、接线端子以及包扎材料等等，市场需求前景广阔。

Description

一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料
技术领域
本发明涉及一种线束用绝缘材料，具体涉及一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料及其制备方法。
背景技术
家电线束是电器中连接各电器设备的接线部件，其作用至关重要，作为家电产业的基础连接部件，其市场需求量随着家电业的快速发展而增加，对其质量的要求也越来越高，尤其是安全环保问题，线束主要包括导线、绝缘护套、包扎材料等部件，在实际应用时，应根据线束的工作环境及性能要求，选择合适材质的部件，传统的线束用绝缘材料多存在阻燃性差、高温易变形、使用寿命短等问题，给实际使用带来很多不便，甚至威胁到人们的生命财产安全，因此，急需改变原有配方，改进材料性能，以适应家电电子器件市场多样的需求。
发明内容
本发明的目的在于，提供一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料，提升了传统聚苯乙烯材料的性能，使其具备良好的力学性能和加工性能，能够适应特定的使用环境条件，为了实现上述目的，本发明采用的技术方案如下：
一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料，其特征在于，该线束用高分子材料包含以下重量份的组分：聚苯乙烯24-28，聚醋酸乙烯12-14，ABS高胶粉12-15，低密度聚乙烯20-23，三烯丙基异氰脲酸酯3-4，双叔丁基过氧化二异丙基苯4-5，三聚磷酸钠3-4，硅酸钠2-3，橘子油2-3，钛白粉20-23，N351炭黑10-12，二甲基二巯基乙酸异辛酯锡2-3，木质素磺酸钠2-3，羟基硅油15-18，四氧化三铁4-6，柠檬酸三乙酯20-23，助剂14-16。
所述的助剂包含以下重量份的原料：天青石20-24，交联剂TAC 3-4，双季戊四醇六丙烯酸酯2-3，硼砂3-4，甲基三乙氧基硅烷2-3，三聚磷酸钠1-2，防老剂MB 1-2，丁香油2-3，抗坏血酸1-2，硫磺3-4，丙烯酸-2-羟基丙酯2-3，刚玉粉2-3，花椒籽油1-2；制备方法是将天青石放入煅烧炉中在550-570℃下煅烧3-4小时，冷却，粉碎成50-100目后放入12-15%盐酸溶液中浸泡2-3小时，过滤出天青石粉末，清水洗净、烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
所述的一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料，其制备方法为：将聚苯乙烯、聚醋酸乙烯、ABS高胶粉、低密度聚乙烯共混均匀后，加入其他剩余成分，送入高速捏合机中，在80-120℃下捏合4-5min，待捏合料冷却后，送入双螺杆挤出机造粒，即得本发明的绝缘材料。
本发明结合了聚苯乙烯、聚醋酸乙烯、ABS高胶粉、低密度聚乙烯等原料的优点，提升了传统聚苯乙烯材料的性能，使其具有良好的加工性能和力学性能，制备的材料柔韧耐冲击，防水防潮，耐化学腐蚀，使用寿命长，能够满足特定的使用环境条件，市场应用前景广阔。
具体实施方式
实施例
本实施例包含以下重量份的原料：聚苯乙烯28，聚醋酸乙烯14，ABS高胶粉15，低密度聚乙烯23，三烯丙基异氰脲酸酯4，双叔丁基过氧化二异丙基苯5，三聚磷酸钠4，硅酸钠3，橘子油3，钛白粉23，N351炭黑12，二甲基二巯基乙酸异辛酯锡3，木质素磺酸钠2，羟基硅油18，四氧化三铁6，柠檬酸三乙酯23，助剂15。
所述的助剂包含以下重量份的原料：天青石24，交联剂TAC 4，双季戊四醇六丙烯酸酯3，硼砂4，甲基三乙氧基硅烷3，三聚磷酸钠2，防老剂MB 2，丁香油3，抗坏血酸2，硫磺4，丙烯酸-2-羟基丙酯3，刚玉粉3，花椒籽油2；制备方法是将天青石放入煅烧炉中在570℃下煅烧4小时，冷却，粉碎成80目后放入15%盐酸溶液中浸泡3小时，过滤出天青石粉末，清水洗净、烘干，粉碎成300目粉末，与其它剩余成分混合，研磨分散2小时，即得。
所述的一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料，其制备方法为：将聚苯乙烯、聚醋酸乙烯、ABS高胶粉、低密度聚乙烯共混均匀后，加入其他剩余成分，送入高速捏合机中，在100℃下捏合4min，待捏合料冷却后，送入双螺杆挤出机造粒，即得本发明的绝缘材料。
本发明材料的性能测试结果为：拉伸强度为17.8Mpa，断裂伸长率为434%，经IRM902油90℃×70h处理后，拉伸强度和断裂伸长率分别为17.1Mpa、402%，经136℃×168h热空气老化后，拉伸强度保持率98.5%，断裂伸长率保持率为98.1%，20℃体积电阻率为1.8×1014Ω·m，经60℃的15%的NaCl溶液浸泡7天后，材料的吸液率为0.0031%，浸泡后体积电阻率变化率为0.003%，经过80℃甲苯溶剂浸泡7天后，无明显溶胀和开裂现象。

Claims (2)

1.一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料，其特征在于，该绝缘料由以下重量份的原料组成：聚苯乙烯24-28，聚醋酸乙烯12-14，ABS高胶粉12-15，低密度聚乙烯20-23，三烯丙基异氰脲酸酯3-4，双叔丁基过氧化二异丙基苯4-5，三聚磷酸钠3-4，硅酸钠2-3，橘子油2-3，钛白粉20-23，N351炭黑10-12，二甲基二巯基乙酸异辛酯锡2-3，木质素磺酸钠2-3，羟基硅油15-18，四氧化三铁4-6，柠檬酸三乙酯20-23，助剂14-16；
所述的助剂包含以下重量份的原料：天青石20-24，交联剂TAC 3-4，双季戊四醇六丙烯酸酯2-3，硼砂3-4，甲基三乙氧基硅烷2-3，三聚磷酸钠1-2，防老剂MB 1-2，丁香油2-3，抗坏血酸1-2，硫磺3-4，丙烯酸-2-羟基丙酯2-3，刚玉粉2-3，花椒籽油1-2；制备方法是将天青石放入煅烧炉中在550-570℃下煅烧3-4小时，冷却，粉碎成50-100目后放入12-15%盐酸溶液中浸泡2-3小时，过滤出天青石粉末，清水洗净、烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.如权利要求1所述的一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料，其制作工艺为：将聚苯乙烯、聚醋酸乙烯、ABS高胶粉、低密度聚乙烯共混均匀后，加入其他剩余成分，送入高速捏合机中，在80-120℃下捏合4-5min，待捏合料冷却后，送入双螺杆挤出机造粒，即得本发明的绝缘材料。
CN201310525713.5A 2013-10-31 2013-10-31 一种防水耐腐蚀家电线束用改性聚苯乙烯绝缘料 Pending CN103554701A (zh)