CN103554668A - 一种新型聚丙烯双壁波纹管 - Google Patents
一种新型聚丙烯双壁波纹管 Download PDFInfo
- Publication number
- CN103554668A CN103554668A CN201310528737.6A CN201310528737A CN103554668A CN 103554668 A CN103554668 A CN 103554668A CN 201310528737 A CN201310528737 A CN 201310528737A CN 103554668 A CN103554668 A CN 103554668A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrugated pipe
- wall corrugated
- raw material
- novel polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型聚丙烯双壁波纹管,其特征在于它是由下述重量份的原料组成的:聚丙烯T30S80-90、桔红色粉0.2-1、二硫氰基甲烷1-3、2,4,5-三氯苯磺酸钠1-2、聚乳酸2-3、四丁基溴化铵1-2、铸石粉1-2、妥尔油2-3、抗氧剂10100.8-2、乙烯基双硬脂酸酰胺1-2、水滑石粉3-5、复合填料5-10,本发明的波纹管管提高了管道的整体质量及保证了系统的安全性,散热性好,耐磨性强,保护性强,综合性能优越。
Description
技术领域
本发明主要涉及一种管材,尤其涉及一种新型聚丙烯双壁波纹管。
背景技术
PVC管(UPVC管) 硬聚氯乙烯管,是由聚氯乙烯树脂与稳定剂、润滑剂等配合后用热压法挤压成型,是最早得到开发应用的塑料管材。UPVC管抗腐蚀能力强、易于粘接、价格低、质地坚硬,但是由于有UPVC单体和添加剂渗出,只适用于输送温度不超过45℃的给水系统中。塑料管道用于输送饮用水,废水,化学品,加热液和冷却液,食品,超纯液体,泥浆,气体,压缩空气和真空系统的应用。
PE管有中密度聚乙烯管和高密度聚乙烯管。前者适用于输送气态的人工煤气、天然气、液化石油气,后者主要用于输送天然气。和钢管比较,施工工艺简单,有一定的柔韧性,更主要的是不用作防腐处理,将节省大量的工序。缺点就器械性不如钢管,施工中特别的注意热力供暖的安全间距,并且不能裸露于空气中阳光下,并且对化学物品敏感,防止污水管道的泄露造成伤害。
发明内容
本发明目的就是提供一种新型聚丙烯双壁波纹管。
本发明是通过以下技术方案实现的:
一种新型聚丙烯双壁波纹管,它是由下述重量份的原料组成的:
聚丙烯T30S 80-90、桔红色粉0.2-1、二硫氰基甲烷1-3、2,4,5- 三氯苯磺酸钠1-2、聚乳酸2-3、四丁基溴化铵1-2、铸石粉1-2、妥尔油2-3、抗氧剂1010 0.8-2、乙烯基双硬脂酸酰胺1-2、水滑石粉3-5、复合填料5-10;
所述的复合填料是由下述重量份的原料组成的:
红土32-40、黑沙4-5、石墨粉10-12、轻质碳酸钙6-8、聚乙烯醇2-3、氨丙基三乙氧基硅烷0.6-1、辣椒油树脂0.1-0.3;
将上述红土和黑沙混合,600-700℃下煅烧2-3小时,出料冷却后与轻质碳酸钙混合,研磨成粉;将上述石墨粉与聚乙烯醇混合,球磨均匀,加热到75-85℃,保温搅拌3-6分钟,降低温度为50-60℃,加入氨丙基三乙氧基硅烷,1000-1200转/分搅拌分散10-14分钟;将上述处理后的各原料与剩余各原料混合,球磨充分,过100-120目筛,即得所述复合填料。
一种新型聚丙烯双壁波纹管的制备方法,包括以下步骤:
将上述各原料混合,进行高速捏合混炼,混炼时间为10-14分钟,升高温度为130-140℃,搅拌至温度为40-50℃,熔融挤出,冷却、成型,即得所述新型聚丙烯双壁波纹管。
本发明的优点是:
本发明的波纹管管提高了管道的整体质量及保证了系统的安全性,散热性好,耐磨性强,保护性强,综合性能优越。
具体实施方式
实施例1
一种新型聚丙烯双壁波纹管,它是由下述重量份(公斤)的原料组成的:
聚丙烯T30S 80、桔红色粉0.7、二硫氰基甲烷3、2,4,5- 三氯苯磺酸钠1、聚乳酸2、四丁基溴化铵1、铸石粉1、妥尔油3、抗氧剂1010 0.8、乙烯基双硬脂酸酰胺1、水滑石粉5、复合填料10;
所述的复合填料是由下述重量份的原料组成的:
红土40、黑沙4、石墨粉12、轻质碳酸钙6、聚乙烯醇3、氨丙基三乙氧基硅烷0.6、辣椒油树脂0.3;
将上述红土和黑沙混合,700℃下煅烧2小时,出料冷却后与轻质碳酸钙混合,研磨成粉;将上述石墨粉与聚乙烯醇混合,球磨均匀,加热到85℃,保温搅拌6分钟,降低温度为60℃,加入氨丙基三乙氧基硅烷,1200转/分搅拌分散14分钟;将上述处理后的各原料与剩余各原料混合,球磨充分,过120目筛,即得所述复合填料。
一种新型聚丙烯双壁波纹管的制备方法,包括以下步骤:
将上述各原料混合,进行高速捏合混炼,混炼时间为14分钟,升高温度为140℃,搅拌至温度为50℃,熔融挤出,冷却、成型,即得所述新型聚丙烯双壁波纹管。
性能测试:
冲击性能(TIR):≤10%;
环刚度(KN/m2):13.23;
环柔性:试样圆滑,无破裂,两壁无脱开,无反向弯曲;
烘箱实验(110℃,30min):无分层,无开裂、无气泡。
Claims (2)
1.一种新型聚丙烯双壁波纹管,其特征在于它是由下述重量份的原料组成的
聚丙烯T30S 80-90、桔红色粉0.2-1、二硫氰基甲烷1-3、2,4,5- 三氯苯磺酸钠1-2、聚乳酸2-3、四丁基溴化铵1-2、铸石粉1-2、妥尔油2-3、抗氧剂1010 0.8-2、乙烯基双硬脂酸酰胺1-2、水滑石粉3-5、复合填料5-10;
所述的复合填料是由下述重量份的原料组成的:
红土32-40、黑沙4-5、石墨粉10-12、轻质碳酸钙6-8、聚乙烯醇2-3、氨丙基三乙氧基硅烷0.6-1、辣椒油树脂0.1-0.3;
将上述红土和黑沙混合,600-700℃下煅烧2-3小时,出料冷却后与轻质碳酸钙混合,研磨成粉;将上述石墨粉与聚乙烯醇混合,球磨均匀,加热到75-85℃,保温搅拌3-6分钟,降低温度为50-60℃,加入氨丙基三乙氧基硅烷,1000-1200转/分搅拌分散10-14分钟;将上述处理后的各原料与剩余各原料混合,球磨充分,过100-120目筛,即得所述复合填料。
2.一种如权利要求1所述的新型聚丙烯双壁波纹管的制备方法,其特征在于包括以下步骤:
将上述各原料混合,进行高速捏合混炼,混炼时间为10-14分钟,升高温度为130-140℃,搅拌至温度为40-50℃,熔融挤出,冷却、成型,即得所述新型聚丙烯双壁波纹管。