CN103554542A - 一种乳胶手套的涂层工艺 - Google Patents

一种乳胶手套的涂层工艺 Download PDF

Info

Publication number
CN103554542A
CN103554542A CN201310557628.7A CN201310557628A CN103554542A CN 103554542 A CN103554542 A CN 103554542A CN 201310557628 A CN201310557628 A CN 201310557628A CN 103554542 A CN103554542 A CN 103554542A
Authority
CN
China
Prior art keywords
emgloves
minutes
latex gloves
mixed
vinyl acetate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310557628.7A
Other languages
English (en)
Inventor
王学斌
高尚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHENJIANG SUHUI LATEX PRODUCT CO Ltd
Original Assignee
ZHENJIANG SUHUI LATEX PRODUCT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHENJIANG SUHUI LATEX PRODUCT CO Ltd filed Critical ZHENJIANG SUHUI LATEX PRODUCT CO Ltd
Priority to CN201310557628.7A priority Critical patent/CN103554542A/zh
Publication of CN103554542A publication Critical patent/CN103554542A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种乳胶手套的涂层工艺，其方法如下：（1）将乙烯-醋酸乙烯共聚物与聚氨酯混合，加入适量水，顺时针进行搅拌20—25分钟，使其混合均匀；（2）将混合后的液体加热，使其温度达到20～30；℃，（3）将乳胶手套放进步骤（2）中的混合液中，持续浸泡8—10分钟；（4）将乳胶手套取出，放进明胶中持续浸泡2～5分钟；（5）对进行步骤（4）后的乳胶手套喷涂聚脲弹性体，使其均匀涂覆在乳胶手套表面上；（6）将进行步骤（5）后的乳胶手套取出翻边并进行烘干，烘干温度为80-160℃、烘干时间为5—10分钟；（7）重复步骤（5）与步骤（6）2—5遍后，自然冷却至常温、脱模最终得到成品，该工艺操作简单，涂层效果好。

Description

一种乳胶手套的涂层工艺
技术领域
本发明涉及乳胶制品技术领域，具体涉及一种乳胶手套的涂层工艺。
背景技术
乳胶手套是手套中的一种，它不同于一般的手套，由乳胶加工而成，可以作为家庭、工业、医疗美容等行业使用，是必备的手部防护用品。采用天然乳胶，配以其他的精细主机加工而成的乳胶手套，产品经过特殊表面处理，穿戴舒适，在工农业生产，医疗，日常生活中都有广泛应用。乳胶手套的内外表面会涂有一层防水的涂层膜，传统的用于涂层膜的浸渍液是将凝固剂与涂层膜的主要原料等一起进行混合，这样浸渍效果差，组分较多，工艺繁琐。
发明内容
本发明所要解决的技术问题是针对以上弊端提供一种乳胶手套的涂层工艺，该工艺操作简单，涂层效果好。
为解决上述技术问题，本发明的技术方案是：
一种乳胶手套的涂层工艺，其方法如下：
（1）将乙烯-醋酸乙烯共聚物与聚氨酯混合，加入适量水，顺时针进行搅拌20—25分钟，使其混合均匀；
（2）将混合后的液体加热，使其温度达到20～30℃；
（3）将乳胶手套放进步骤（2）中的混合液中，持续浸泡8—10分钟；
（4）将乳胶手套取出，放进明胶中持续浸泡2～5分钟；
（5）对进行步骤（4）后的乳胶手套喷涂聚脲弹性体，使其均匀涂覆在乳胶手套表面上；
（6）将进行步骤（5）后的乳胶手套取出翻边并进行烘干，烘干温度为80-160℃、烘干时间为5—10分钟；
（7）重复步骤（5）与步骤（6）2—5遍后，自然冷却至常温、脱模最终得到成品。
上述一种乳胶手套的涂层工艺，其中，所述的乙烯-醋酸乙烯共聚物、聚氨酯与水的重量比为100:8—45:10—30。
本发明的有益效果为：本发明工艺操作简单，组分少，但是涂层防水效果好；聚脲是由半预聚体、端氨基聚醚、胺扩链剂等原料现场喷涂而成。它疏水性极强，对环境湿度不敏感，表现特别突出，聚脲涂层柔韧有余、刚性十足、色彩丰富，它致密、连续、无接缝，完全隔绝空气中水分和氧气的渗入，防腐和防护性能无与伦比。它同时具有耐磨、防水、抗冲击、抗疲劳、耐老化、耐高温、耐核辐射等多种功能。
具体实施方式
以下通过具体实施例对本发明的具体实施方式作进一步详细的说明。
实例一：
一种乳胶手套的涂层工艺，其方法如下：
（1）将10kg乙烯-醋酸乙烯共聚物与3.5kg聚氨酯混合，加入2.5kg水，顺时针进行搅拌20—25分钟，使其混合均匀；
（2）将混合后的液体加热，使其温度达到20～30℃；
（3）将乳胶手套放进步骤（2）中的混合液中，持续浸泡8—10分钟；
（4）将乳胶手套取出，放进明胶中持续浸泡2～5分钟；
（5）对进行步骤（4）后的乳胶手套喷涂聚脲弹性体，使其均匀涂覆在乳胶手套表面上；
（6）将进行步骤（5）后的乳胶手套取出翻边并进行烘干，烘干温度为80-160℃、烘干时间为5—10分钟；
（7）重复步骤（5）与步骤（6）两次后，自然冷却至常温、脱模最终得到成品。
实例二：
一种乳胶手套的涂层工艺，其方法如下：
（1）将10kg乙烯-醋酸乙烯共聚物与2kg聚氨酯混合，加入2kg水，顺时针进行搅拌20—25分钟，使其混合均匀；
（2）将混合后的液体加热，使其温度达到20～30℃；
（3）将乳胶手套放进步骤（2）中的混合液中，持续浸泡8—10分钟；
（4）将乳胶手套取出，放进明胶中持续浸泡2～5分钟；
（5）对进行步骤（4）后的乳胶手套喷涂聚脲弹性体，使其均匀涂覆在乳胶手套表面上；
（6）将进行步骤（5）后的乳胶手套取出翻边并进行烘干，烘干温度为80-160℃、烘干时间为5—10分钟；
（7）重复步骤（5）与步骤（6）四次后，自然冷却至常温、脱模最终得到成品。
本发明工艺操作简单，组分少，但是涂层防水效果好；聚脲是由半预聚体、端氨基聚醚、胺扩链剂等原料现场喷涂而成。它疏水性极强，对环境湿度不敏感，表现特别突出，聚脲涂层柔韧有余、刚性十足、色彩丰富，它致密、连续、无接缝，完全隔绝空气中水分和氧气的渗入，防腐和防护性能无与伦比。它同时具有耐磨、防水、抗冲击、抗疲劳、耐老化、耐高温、耐核辐射等多种功能。
这里本发明的描述和应用是说明性的，并非想将本发明的范围限制在上述实施例中，因此，本发明不受本实施例的限制，任何采用等效替换取得的技术方案均在本发明保护的范围内。

Claims (2)

1.一种乳胶手套的涂层工艺，其特征为，其方法如下：
（1）将乙烯-醋酸乙烯共聚物与聚氨酯混合，加入适量水，顺时针进行搅拌20—25分钟，使其混合均匀； 
（2）将混合后的液体加热，使其温度达到20～30℃； 
（3）将乳胶手套放进步骤（2）中的混合液中，持续浸泡8—10分钟；
（4）将乳胶手套取出，放进明胶中持续浸泡2～5分钟； 
（5）对进行步骤（4）后的乳胶手套喷涂聚脲弹性体，使其均匀涂覆在乳胶手套表面上；
（6）将进行步骤（5）后的乳胶手套取出翻边并进行烘干，烘干温度为80-160℃、烘干时间为5—10分钟；
（7）重复步骤（5）与步骤（6）2—5遍后，自然冷却至常温、脱模最终得到成品。
2.如权利要求1所述的一种乳胶手套的涂层工艺，其特征为，所述的乙烯-醋酸乙烯共聚物、聚氨酯与水的重量比为100:8—45:10—30。
CN201310557628.7A 2013-11-11 2013-11-11 一种乳胶手套的涂层工艺 Pending CN103554542A (zh)