CN103553384A - 大型琉璃石膏模具脱蜡方法 - Google Patents

大型琉璃石膏模具脱蜡方法 Download PDF

Info

Publication number
CN103553384A
CN103553384A CN201310468691.3A CN201310468691A CN103553384A CN 103553384 A CN103553384 A CN 103553384A CN 201310468691 A CN201310468691 A CN 201310468691A CN 103553384 A CN103553384 A CN 103553384A
Authority
CN
China
Prior art keywords
wax
mold
gypsum
pattern
plaster mold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310468691.3A
Other languages
English (en)
Other versions
CN103553384B (zh
Inventor
蔡平忠
张晓娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGHUANGDAO JUNDING TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
QINGHUANGDAO JUNDING TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGHUANGDAO JUNDING TECHNOLOGY DEVELOPMENT Co Ltd filed Critical QINGHUANGDAO JUNDING TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN201310468691.3A priority Critical patent/CN103553384B/zh
Publication of CN103553384A publication Critical patent/CN103553384A/zh
Application granted granted Critical
Publication of CN103553384B publication Critical patent/CN103553384B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种大型琉璃石膏模具脱蜡方法，经泥塑造型、制作硅胶模具、制作树脂或石膏外壳、浇蜡、制作石膏模具、将石膏模具贴近地面部分钻排气孔、将树脂或石膏保护外壳包裹的石膏模具和蜡模直接入窑炉，用热风装置吹注蜡模熔化，再用加热器放入到一定深度的蜡模中，并利用胶管外引蜡液，未熔化部分的蜡模，在窑炉烧制升温时或升温至200℃以前，蜡液顺排气孔自然流尽。因本发明在石膏模具外部采用了保护外壳，具有安全、快捷，成品率达100%。解决了传统石膏模具在脱蜡完成后，将石膏模具翻和往炉里吊运过程中，由于石膏模具本体太大，容易引起石膏模具的受损，甚至破裂，造成成品率低的问题。

Description

大型琉璃石膏模具脱蜡方法
技术领域
本发明涉及一种大型琉璃石膏模具脱蜡方法。保证了石膏模具的安全可靠性，有效提高了成品率。
背景技术
传统琉璃的脱蜡方法依据于青铜器的脱蜡铸造技法。它是以水蒸气脱蜡，先用一容器，盛上一些水，把模具口朝下，放一支架上，然后密封容器，待水煮开沸腾时产生水蒸气，在一定的时间内将蜡熔化成液体，流出石膏模具。待蜡脱尽后，再把模具翻过来口朝上放置，由于模具太大，在脱蜡过程中或是进行模具翻转和往炉里吊运时，都会引起石膏模具受损，甚至破裂，导致成品率极低。
发明内容
鉴于上述现状，本发明提供了一种大型琉璃石膏模具脱蜡方法，克服了传统在脱蜡过程中或是进行模具翻转和往炉里吊运时，引起的石膏模具受损及破裂问题。
本发明的大型琉璃石膏模具脱蜡方法，包括如下步骤：
1、根据图纸要求，制作泥塑造型；
2、制作硅胶模具，按配比选用硅胶：固化剂=100︰2-5，在泥塑整体上进行涂刷，涂刷至厚度为5-10mm，定型后去除泥塑；
3、制作树脂或石膏外壳，选用树脂或石膏材料将硅胶模具包裹形成保护外壳，保护外壳可以制成多块组合拼装；
4、浇蜡，把蜡加热至110℃—125℃成液态，浇灌入硅胶模具中，冷却至固化状态成蜡模；
5、制作石膏模具，去掉硅胶模具，按石膏︰水=100㎏︰15-18㎏的比例调制，浇灌在蜡模与保护外壳之间形成的夹层内，将蜡模整体包裹并且石膏最薄处不得低于30mm厚，放置4-8小时，将石膏模具贴近地面部分用金属丝粘蜡钻排气孔；
6、将树脂或石膏保护外壳包裹的石膏模具和蜡模直接入窑炉，使用热风装置吹注蜡模，使其熔化，再用加热器放入到一定深度的蜡模中，使其加热，并利用胶管往外引蜡液，未熔化部分的蜡模，在窑炉烧制升温时或升温至200C°以前，蜡液顺排气孔自然流尽。
本发明中，所涉及的金属丝直径为5mm。
进一步地，所述的排气孔为2-3个。
进一步地，所述的胶管直径为8—12mm。
本发明中，所涉及的热风装置是电热风机，或是电热吹风机。
本发明因采用了在石膏模具外部增设了强化保护作用的树脂或石膏保护外壳包裹住石膏模具，和蜡模构成整体入窑炉，这样，无论如何吊运都不会伤及石膏模具，该方法安全、快捷，并且要一气呵成，成品率达100﹪。
具体实施例
本发明的大型琉璃石膏模具脱蜡方法，包括如下步骤：
1、泥塑雕刻，根据图纸要求，将图纸上的视图作品制作三维立体泥塑造型；
2、制作硅胶模具，选用硅胶：固化剂=100︰2-5进行配比，在泥塑整体上进行涂刷，涂刷至厚度达到5-10mm，定型后去除泥塑；
3、制作树脂外壳或石膏外壳，选用树脂或石膏材料将硅胶模具包裹形成外壳，外壳可以制成两块或多块组合拼装，方便拆卸；
4、制作蜡模，先去除硅胶模具内的泥塑，把蜡加热至110℃—125℃成液态，浇灌入硅胶模具里，冷却至固化状态成形蜡模；
5、制作石膏模具，去掉硅胶模具，按石膏︰水＝100㎏︰15-18㎏的比例调制，浇灌在蜡模（与保护外壳之间），将蜡模整体包裹并且石膏最薄处不得低于30mm厚，放置4—8小时，制作石膏模具时，石膏模具贴近地面部分用直径为5mm金属丝粘蜡钻排气孔2-3个；
6、将树脂或石膏保护外壳包裹的石膏模具和蜡模直接入窑炉，待石膏模具入窑炉定位后，使用电热吹风机吹注料口部位的蜡模，使其熔化成液体，再用加热器放入蜡模中，使其加热，待加热到一定深度时，用直径8—12mm的胶管往外引蜡液，同时加热器不断的移动至到底部，未熔化部分的蜡模，在窑炉烧制升温时或升温至200C°以前，蜡液顺排气孔自然流尽。
待蜡脱尽后，再把模具翻过来口朝上放置玻璃熔料送入窑炉烧制产品或是备用。

Claims (5)

1.大型琉璃石膏模具脱蜡方法，其特征是，包括如下步骤：
（1）根据图纸要求，制作泥塑造型；
（2）制作硅胶模具，按配比选用硅胶：固化剂=100︰2-5，在泥塑整体上进行涂刷，涂刷至厚度为5-10mm，定型后去除泥塑；
（3）制作树脂或石膏外壳，选用树脂或石膏材料将硅胶模具包裹形成保护外壳，保护外壳可以制成多块组合拼装；
（4）浇蜡，把蜡加热至110℃—125℃成液态，浇灌入硅胶模具里，冷却至固化状态成蜡模；
（5）制作石膏模具，去掉硅胶模具，按石膏︰水=100㎏︰15-18㎏的比例调制，浇灌在蜡模与保护外壳之间形成的夹层内，将蜡模整体包裹并且石膏最薄处不得低于30mm厚，放置4-8小时，将石膏模具贴近地面部分用金属丝粘蜡钻排气孔；
（6）将树脂或石膏保护外壳包裹的石膏模具和蜡模直接入窑炉，使用热风装置吹注蜡模，使其熔化，再用加热器放入到一定深度的蜡模中，使其加热，并利用胶管往外引蜡液，未熔化部分的蜡模，在窑炉烧制升温时或升温至200C°以前，蜡液顺排气孔自然流尽。
2.根据权利要求1所述的大型琉璃石膏模具脱蜡方法，其特征是，所述的金属丝直径为5mm。
3.根据权利要求1所述的大型琉璃石膏模具脱蜡方法，其特征是，所述的排气孔为2-3个。
4.根据权利要求1所述的大型琉璃石膏模具脱蜡方法，其特征是，所述的胶管直径为8—12mm。
5.根据权利要求1所述的大型琉璃石膏模具脱蜡方法，其特征是，所述的热风装置是电热风机，或是电热吹风机。
CN201310468691.3A 2013-10-10 2013-10-10 大型琉璃石膏模具脱蜡方法 Active CN103553384B (zh)