CN103540259A - High-hardness, anti-steam and waterproof coating - Google Patents
High-hardness, anti-steam and waterproof coating Download PDFInfo
- Publication number
- CN103540259A CN103540259A CN201310444511.8A CN201310444511A CN103540259A CN 103540259 A CN103540259 A CN 103540259A CN 201310444511 A CN201310444511 A CN 201310444511A CN 103540259 A CN103540259 A CN 103540259A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- hardness
- good
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a high-hardness, anti-steam and waterproof coating. The high-hardness, anti-steam and waterproof coating comprises the following raw materials in parts by weight: 60-70 parts of fluorosilicone emulsion with the solid content being not less than 25%, 7-9 parts of talcum powder, 15-20 parts of actinolite powder, 1-2 parts of calcined kaolin, 2-3 parts of ultrafine aluminum silicate, 2-4 parts of soy protein powder, 10-20 parts of polyvinyl acetate emulsion, 1-2 parts of sodium starch phosphate, 2-3 parts of perfluorooctyl methacrylate, 0.3-0.4 part of ammonium metavanadate, 2-4 parts of anhydrous ethanol, 10-20 parts of binding aid and 10-30 parts of deionized water. The waterproof coating disclosed by the invention has the advantages of waterproofness, anti-steam property, strong adhesion, good hardness of a formed film, low blistering probability, good anti-aging property, high hardness, good mechanical properties, good adhesion and good compactness.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of high rigidity, vapor-proof waterproof paint.
Background technology
Existing waterproof paint has multiple, some constructing operation complexity and poor performance; Some waterproof effects are poor, and weather resistance is poor; What have needs not only construct trouble but also exist batching to be forbidden to cause degradation to affect waterproof effect of field mix; The easy generation bubble having, surface gloss is bad, and it is necessary therefore producing a kind of high performance waterproof paint.
Summary of the invention
The object of the invention is just to provide a kind of high rigidity, vapor-proof waterproof paint.
The present invention is achieved by the following technical solutions:
, a vapor-proof waterproof paint, it is comprised of the raw material of following weight parts:
The fluoro-silicone emulsion 60-70 of solid content >=25%, talcum powder 7-9, Tremoliteor Tremoliteasbestos powder 15-20, calcined kaolin 1-2, superfine alumina silicate 2-3, soybean protein powder 2-4, polyvinyl acetate emulsion 10-20, sodium starch phosphate 1-2, methacrylic acid ten trifluoro monooctyl ester 2-3, ammonium meta-vanadate 0.3-0.4, dehydrated alcohol 2-4, adhesive aid 10-20, deionized water 10-30;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 30-40, polyvinyl alcohol 6-10, Radix Notoginseng powder 2-3, carbomer 4-6, N-ethyl-neighbour, para toluene sulfonamide 0.5-1, sodium silicoaluminate 2-3, water are appropriate;
Above-mentioned sodium silicoaluminate is mixed with polyvinyl alcohol, be preheating to 30-40 ℃, ball milling 10-15 minute, joins in this compound weight 3-5 water doubly, be heated to 75-85 ℃, fully stir, add Radix Notoginseng powder, carbomer, rising temperature is 100-120 ℃, being stirred to temperature is 25-30 ℃, add each raw material of residue, fully ball milling, obtains described adhesive aid.
A preparation method for high rigidity, vapor-proof waterproof paint, comprises the following steps:
Above-mentioned talcum powder, Tremoliteor Tremoliteasbestos powder, soybean protein powder, sodium starch phosphate, deionized water are mixed, after stirring, add polyvinyl acetate emulsion, 400-500 rev/min of dispersed with stirring 10-15 minute, add again each raw material of residue, high-speed stirring, to mixing, obtains described high rigidity, vapor-proof waterproof paint.
Advantage of the present invention is:
Waterproof paint waterproof of the present invention, vapor-proof, strong adhesion, becomes film hardness good, not easy to foaming, and resistance to deterioration is good, and hardness is high, good mechanical property, cementability is good, and compactness is good.
Embodiment
Embodiment 1
, a vapor-proof waterproof paint, it by following weight parts (kilogram) raw material form:
The fluoro-silicone emulsion 70 of solid content >=25%, talcum powder 7, Tremoliteor Tremoliteasbestos powder 20, calcined kaolin 2, superfine alumina silicate 3, soybean protein powder 2, polyvinyl acetate emulsion 20, sodium starch phosphate 2, methacrylic acid ten trifluoro monooctyl esters 3, ammonium meta-vanadate 0.4, dehydrated alcohol 2, adhesive aid 20, deionized water 30;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 40, polyvinyl alcohol 10, Radix Notoginseng powder 3, carbomer 6, N-ethyl-neighbour, para toluene sulfonamide 0.5, sodium silicoaluminate 2, water are appropriate;
Above-mentioned sodium silicoaluminate is mixed with polyvinyl alcohol, be preheating to 40 ℃, ball milling 15 minutes, joins in the water of 5 times of this compound weight, be heated to 85 ℃, fully stir, add Radix Notoginseng powder, carbomer, rising temperature is 120 ℃, being stirred to temperature is 30 ℃, add each raw material of residue, fully ball milling, obtains described adhesive aid.
A preparation method for high rigidity, vapor-proof waterproof paint, comprises the following steps:
Above-mentioned talcum powder, Tremoliteor Tremoliteasbestos powder, soybean protein powder, sodium starch phosphate, deionized water are mixed, after stirring, add polyvinyl acetate emulsion, 500 revs/min of dispersed with stirring 15 minutes, add again each raw material of residue, high-speed stirring, to mixing, obtains described high rigidity, vapor-proof waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. high rigidity, a vapor-proof waterproof paint, is characterized in that what it was comprised of the raw material of following weight parts:
The fluoro-silicone emulsion 60-70 of solid content >=25%, talcum powder 7-9, Tremoliteor Tremoliteasbestos powder 15-20, calcined kaolin 1-2, superfine alumina silicate 2-3, soybean protein powder 2-4, polyvinyl acetate emulsion 10-20, sodium starch phosphate 1-2, methacrylic acid ten trifluoro monooctyl ester 2-3, ammonium meta-vanadate 0.3-0.4, dehydrated alcohol 2-4, adhesive aid 10-20, deionized water 10-30;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 30-40, polyvinyl alcohol 6-10, Radix Notoginseng powder 2-3, carbomer 4-6, N-ethyl-neighbour, para toluene sulfonamide 0.5-1, sodium silicoaluminate 2-3, water are appropriate;
Above-mentioned sodium silicoaluminate is mixed with polyvinyl alcohol, be preheating to 30-40 ℃, ball milling 10-15 minute, joins in this compound weight 3-5 water doubly, be heated to 75-85 ℃, fully stir, add Radix Notoginseng powder, carbomer, rising temperature is 100-120 ℃, being stirred to temperature is 25-30 ℃, add each raw material of residue, fully ball milling, obtains described adhesive aid.
2. a preparation method for high rigidity as claimed in claim 1, vapor-proof waterproof paint, is characterized in that comprising the following steps:
Above-mentioned talcum powder, Tremoliteor Tremoliteasbestos powder, soybean protein powder, sodium starch phosphate, deionized water are mixed, after stirring, add polyvinyl acetate emulsion, 400-500 rev/min of dispersed with stirring 10-15 minute, add again each raw material of residue, high-speed stirring, to mixing, obtains described high rigidity, vapor-proof waterproof paint.