CN103540201A - Water-based heat-insulating waterproof coating - Google Patents
Water-based heat-insulating waterproof coating Download PDFInfo
- Publication number
- CN103540201A CN103540201A CN201310444630.3A CN201310444630A CN103540201A CN 103540201 A CN103540201 A CN 103540201A CN 201310444630 A CN201310444630 A CN 201310444630A CN 103540201 A CN103540201 A CN 103540201A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- raw material
- adhesive aid
- waterproof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based heat-insulating waterproof coating, which is composed of the following raw materials in parts by weight: 40-50 parts of a styrene-acrylic emulsion, 2-3 parts of rutile titanium dioxide, 2-5 parts of 1,2-benzisothiazolin-3-ketone and antimonous oxide, 1-4 parts of barium stearate, 1-2 parts of tetrapropylammonium bromide, 2-4 parts of 3-pyrroline, 2-3 parts of sodium metasilicate, 4-6 parts of slaked lime, 2-4 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 9-15 parts of actinolite powder, 10-20 parts of a bonding aid, and 5-20 parts of deionized water. According to the invention, through the reasonable collocation of various raw materials, the mechanical properties and gas-water barrier properties of products are significantly improved, so that the water-based heat-insulating waterproof coating has excellent mechanical properties and waterproof properties, the reflectivity of the coating can also be improved, and the heat-insulating effect of the coating is good.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of aquosity heat insulating heat preserving waterproof paint.
Background technology
Existing waterproof paint has multiple, some constructing operation complexity and poor performance; Some waterproof effects are poor, and weather resistance is poor; What have needs not only construct trouble but also exist batching to be forbidden to cause degradation to affect waterproof effect of field mix; The easy generation bubble having, surface gloss is bad, and it is necessary therefore producing a kind of high performance waterproof paint.
Summary of the invention
The object of the invention is just to provide a kind of aquosity heat insulating heat preserving waterproof paint.
The present invention is achieved by the following technical solutions:
A waterproof paint, it is comprised of the raw material of following weight parts:
Benzene emulsion 40-50, Rutile type Titanium Dioxide 2-3,1,2-benzisothiazole-3-ketone, antimonous oxide 2-5, barium stearate 1-4,4-propyl bromide 1-2,3-pyrroline 2-4, Starso 2-3, white lime 4-6,2,2,4-trimethylammonium-1,3-pentanediol mono isobutyrate 2-4, Tremoliteor Tremoliteasbestos powder 9-15, adhesive aid 10-20, deionized water 5-20;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 30-40, polyvinyl alcohol 6-10, Radix Notoginseng powder 2-3, carbomer 4-6, N-ethyl-neighbour, para toluene sulfonamide 0.5-1, sodium silicoaluminate 2-3, water are appropriate;
Above-mentioned sodium silicoaluminate is mixed with polyvinyl alcohol, be preheating to 30-40 ℃, ball milling 10-15 minute, joins in this compound weight 3-5 water doubly, be heated to 75-85 ℃, fully stir, add Radix Notoginseng powder, carbomer, rising temperature is 100-120 ℃, being stirred to temperature is 25-30 ℃, add each raw material of residue, fully ball milling, obtains described adhesive aid.
A preparation method for aquosity heat insulating heat preserving waterproof paint, comprises the following steps:
Under stirring, the speed of 500-800r/min first deionized water, Rutile type Titanium Dioxide, Tremoliteor Tremoliteasbestos powder, adhesive aid are fully mixed, add again 1,2-benzisothiazole-3-ketone, antimonous oxide, barium stearate, 4-propyl bromide, on multi-functional dispersion machine, with the high-speed stirring 2-4h of 4000-6000r/min, by high speed shear, be uniformly dispersed, then added each raw material of residue, be uniformly mixed 2-4 hour, obtain described aquosity heat insulating heat preserving waterproof paint.
Advantage of the present invention is:
The present invention is reasonably combined by various raw materials, has significantly improved the gentle water barrier of mechanical property of product, makes it have excellent mechanical property and water resistance, can also improve the reflectivity of coating, by the heat insulating effect of coating.
Embodiment
Embodiment 1
A waterproof paint, it by following weight parts (kilogram) raw material form:
Benzene emulsion 50, Rutile type Titanium Dioxide 2,1,2-benzisothiazole-3-ketone, antimonous oxide 2, barium stearate 1,4-propyl bromide 1,3-pyrroline 2, Starso 2, white lime 6,2,2,4-trimethylammonium-1,3-pentanediol mono isobutyrate 4, Tremoliteor Tremoliteasbestos powder 15, adhesive aid 20, deionized water 20;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 40, polyvinyl alcohol 10, Radix Notoginseng powder 3, carbomer 6, N-ethyl-neighbour, para toluene sulfonamide 0.5, sodium silicoaluminate 2, water are appropriate;
Above-mentioned sodium silicoaluminate is mixed with polyvinyl alcohol, be preheating to 30 ℃, ball milling 15 minutes, joins in the water of 5 times of this compound weight, be heated to 85 ℃, fully stir, add Radix Notoginseng powder, carbomer, rising temperature is 120 ℃, being stirred to temperature is 30 ℃, add each raw material of residue, fully ball milling, obtains described adhesive aid.
A preparation method for aquosity heat insulating heat preserving waterproof paint, comprises the following steps:
Under stirring, the speed of 800r/min first deionized water, Rutile type Titanium Dioxide, Tremoliteor Tremoliteasbestos powder, adhesive aid are fully mixed, add again 1,2-benzisothiazole-3-ketone, antimonous oxide, barium stearate, 4-propyl bromide, on multi-functional dispersion machine, with the high-speed stirring 2h of 6000r/min, by high speed shear, be uniformly dispersed, then added each raw material of residue, be uniformly mixed 2-4 hour, obtain described aquosity heat insulating heat preserving waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an aquosity heat insulating heat preserving waterproof paint, is characterized in that what it was comprised of the raw material of following weight parts:
Benzene emulsion 40-50, Rutile type Titanium Dioxide 2-3,1,2-benzisothiazole-3-ketone, antimonous oxide 2-5, barium stearate 1-4,4-propyl bromide 1-2,3-pyrroline 2-4, Starso 2-3, white lime 4-6,2,2,4-trimethylammonium-1,3-pentanediol mono isobutyrate 2-4, Tremoliteor Tremoliteasbestos powder 9-15, adhesive aid 10-20, deionized water 5-20;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 30-40, polyvinyl alcohol 6-10, Radix Notoginseng powder 2-3, carbomer 4-6, N-ethyl-neighbour, para toluene sulfonamide 0.5-1, sodium silicoaluminate 2-3, water are appropriate;
Above-mentioned sodium silicoaluminate is mixed with polyvinyl alcohol, be preheating to 30-40 ℃, ball milling 10-15 minute, joins in this compound weight 3-5 water doubly, be heated to 75-85 ℃, fully stir, add Radix Notoginseng powder, carbomer, rising temperature is 100-120 ℃, being stirred to temperature is 25-30 ℃, add each raw material of residue, fully ball milling, obtains described adhesive aid.
2. a preparation method for aquosity heat insulating heat preserving waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
Under stirring, the speed of 500-800r/min first deionized water, Rutile type Titanium Dioxide, Tremoliteor Tremoliteasbestos powder, adhesive aid are fully mixed, add again 1,2-benzisothiazole-3-ketone, antimonous oxide, barium stearate, 4-propyl bromide, on multi-functional dispersion machine, with the high-speed stirring 2-4h of 4000-6000r/min, by high speed shear, be uniformly dispersed, then added each raw material of residue, be uniformly mixed 2-4 hour, obtain described aquosity heat insulating heat preserving waterproof paint.