CN103538137A - 一种沙柳木丝复合板及其制备方法 - Google Patents

一种沙柳木丝复合板及其制备方法 Download PDF

Info

Publication number
CN103538137A
CN103538137A CN201310490343.6A CN201310490343A CN103538137A CN 103538137 A CN103538137 A CN 103538137A CN 201310490343 A CN201310490343 A CN 201310490343A CN 103538137 A CN103538137 A CN 103538137A
Authority
CN
China
Prior art keywords
wood wool
excelsior
salix monogolica
layer
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310490343.6A
Other languages
English (en)
Inventor
姚利宏
王喜明
王欣
相广东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia Agricultural University
Original Assignee
Inner Mongolia Agricultural University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia Agricultural University filed Critical Inner Mongolia Agricultural University
Priority to CN201310490343.6A priority Critical patent/CN103538137A/zh
Publication of CN103538137A publication Critical patent/CN103538137A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种沙柳木丝复合板及其制备方法，该方法为：将沙柳置于木丝机中，获得木丝长度4cm～10cm，宽度2mm～10mm，厚度1.0mm～3.0mm，木丝含水率为8%～12%；施加胶黏剂，在浸胶槽中将木丝浸渍30分钟，使施胶木束的含水率为8%～12％；将木丝根据需要的形状模具进行组坯；热压成型，热压温度120℃～170℃，热压压力0.6Mpa～1.8Mpa，热压时间0.5min/mm～2.5min/mm；该沙柳木丝复合板包括：第一木丝层、第二木丝层、第三木丝层。本发明通过以沙柳为原料，采取刨切的方式获得沙柳木丝，对沙柳木丝进行施胶，获得沙柳木丝板材或者方材；通过沙柳木丝与硅酸盐水泥进行混合，制备阻燃墙体材料，染色获得轻质木丝装饰材料。本发明提高了沙柳的加工利用率和加工利用附加值，拓展了木结构的发展。

Description

一种沙柳木丝复合板及其制备方法
技术领域
本发明属于沙柳复合板制造技术领域，尤其涉及一种沙柳木丝复合板及其制备方法。
背景技术
木结构建筑在我国的快速发展，极大地推动了木结构结构材料及装饰材料的发展和应用。沙柳是西部一种特有的灌木资源，传统的利用沙柳多为制造纤维板和刨花板，利用方式能源消耗大、生产工艺复杂、且利用附加值低。
发明内容
本发明实施例的目的在于提供一种沙柳木丝复合板及其制备方法，旨在解决传统的利用沙柳多为制造纤维板和刨花板，利用方式能源消耗大、生产工艺复杂、且利用附加值低的问题，合理高效的将沙柳制备成木结构建筑墙体及装饰材料。
本发明实施例是这样实现的，一种沙柳木丝复合板的制备方法，该沙柳木丝复合板的制备方法包括以下步骤：
步骤一，沙柳木丝的制备，利用沙柳木丝机进行木丝制备，将沙柳置于木丝机中，获得木丝长度4cm～10cm，宽度2mm～10mm，厚度1.0mm～3.0mm，木丝含水率为8%～12%；
步骤二，施加胶黏剂，在浸胶槽中将木丝浸渍30分钟，使施胶木束的含水率控制在8%～12％；
步骤三，木丝板成型，将木丝根据需要的形状模具进行组坯；
步骤四，热压成型，热压温度120℃～170℃，热压压力0.6Mpa～1.8Mpa，热压时间0.5min/mm～2.5min/mm。
进一步，在步骤三中，组坯可以制成板状、方材状、也可以和硅酸盐材料混合制成轻质保温隔热材料。
本发明的另一目的在于提供沙柳木丝复合板，该沙柳木丝复合板包括：第一木丝层、第二木丝层、第三木丝层；
第一木丝层设置在沙柳木丝复合板的上面，第三木丝层设置在沙柳木丝复合板的下面，第二木丝层设置在第一木丝层和第三木丝层之间。
进一步，第一木丝层和第三木丝层为顺纹放置，第二木丝层为横纹放置。
本发明提供的沙柳木丝复合板及其制备方法，通过以沙柳为原料，采取刨切的方式获得沙柳木丝，对沙柳木丝进行施胶，获得沙柳木丝板材或者方材；通过沙柳木丝与硅酸盐水泥进行混合，制备阻燃墙体材料，染色获得轻质木丝装饰材料。本发明扩大了沙柳木丝板的加工利用原料，提高了沙柳的加工利用率和加工利用附加值，拓展了木结构的发展。本发明高效的利用沙生灌木，同时制备的木丝板为轻质材料，板材中有空隙，提高板材的保温、隔声效果；对木丝进行阻燃处理，可以提高材料的阻燃性能，制备阻燃墙体材料，为木结构建筑在西部的发展提供了很好的墙体装饰材料。
附图说明
图1是本发明实施例提供的沙柳木丝复合板的制备方法流程图；
图2是本发明实施例提供的沙柳木丝复合板的结构示意图；
图中：1、第一木丝层；2、第二木丝层；3、第三木丝层。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
下面结合附图及具体实施例对本发明的应用原理作进一步描述。
如图1所示，本发明实施例的沙柳木丝复合板的制备方法包括以下步骤：
S101：沙柳木丝的制备
利用沙柳木丝机进行木丝制备，将沙柳置于木丝机中，获得木丝长度4cm～10cm，宽度2mm～10mm，厚度1.0mm～3.0mm，木丝含水率为8%～12%；
S102：施加胶黏剂
在浸胶槽中将木丝浸渍30分钟，因施胶后的木束含水率较高，常温下陈化不能满足要求，使施胶木束的含水率控制在8%～12％；
S103：木丝板成型
将木丝根据需要的形状模具进行组坯，可以制成板状、方材状、也可以和硅酸盐等材料混合制成轻质保温隔热材料；
S104：热压成型
热压温度120℃～170℃，热压压力0.6Mpa～1.8Mpa，热压时间0.5min/mm～2.5min/mm。
如图2所示，本发明实施例的沙柳木丝复合板主要由第一木丝层1、第二木丝层2、第三木丝层3组成；
第一木丝层1和第三木丝层3为顺纹放置，第二木丝层2为横纹放置。
本发明高效的利用沙生灌木，同时制备的木丝板为轻质材料，板材中有空隙，提高板材的保温、隔声效果；对木丝进行阻燃处理，可以提高材料的阻燃性能，制备阻燃墙体材料，为木结构建筑在西部的发展提供了很好的墙体装饰材料。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.一种沙柳木丝复合板的制备方法，其特征在于，该沙柳木丝复合板的制备方法包括以下步骤：
步骤一，沙柳木丝的制备，利用沙柳木丝机进行木丝制备，将沙柳置于木丝机中，获得木丝长度4cm～10cm，宽度2mm～10mm，厚度1.0mm～3.0mm，木丝含水率为8%～12%；
步骤二，施加胶黏剂，在浸胶槽中将木丝浸渍30分钟，使施胶木丝的含水率为8%～12％；
步骤三，木丝板成型，将木丝根据需要的形状模具进行组坯；
步骤四，热压成型，热压温度120℃～170℃，热压压力0.6Mpa～1.8Mpa，热压时间0.5min/mm～2.5min/mm。
2.如权利要求1所述的沙柳木丝复合板的制备方法，其特征在于，在步骤三中，组坯可以制成板状、方材状、也可以和硅酸盐材料混合制成轻质保温隔热材料。
3.一种沙柳木丝复合板，其特征在于，该沙柳木丝复合板包括：第一木丝层、第二木丝层、第三木丝层；
第一木丝层设置在沙柳木丝复合板的上面，第三木丝层设置在沙柳木丝复合板的下面，第二木丝层设置在第一木丝层和第三木丝层之间。
4.如权利要求3所述的沙柳木丝复合板，其特征在于，第一木丝层和第三木丝层为顺纹放置，第二木丝层为横纹放置。
CN201310490343.6A 2013-10-14 2013-10-14 一种沙柳木丝复合板及其制备方法 Pending CN103538137A (zh)