CN103526597A - 一种阻燃印花粘合剂及其制备方法 - Google Patents

一种阻燃印花粘合剂及其制备方法 Download PDF

Info

Publication number
CN103526597A
CN103526597A CN201310502203.6A CN201310502203A CN103526597A CN 103526597 A CN103526597 A CN 103526597A CN 201310502203 A CN201310502203 A CN 201310502203A CN 103526597 A CN103526597 A CN 103526597A
Authority
CN
China
Prior art keywords
parts
minute
adhesive
printing adhesive
retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310502203.6A
Other languages
English (en)
Inventor
朱亮
杨明虎
朱守玉
张祖豪
吴昊天
丁虎
唐红涛
王俊
李曼莉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI POLYMERIZATION CONVERGENCE TECHNOLOGY Co Ltd
Original Assignee
HEFEI POLYMERIZATION CONVERGENCE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI POLYMERIZATION CONVERGENCE TECHNOLOGY Co Ltd filed Critical HEFEI POLYMERIZATION CONVERGENCE TECHNOLOGY Co Ltd
Priority to CN201310502203.6A priority Critical patent/CN103526597A/zh
Publication of CN103526597A publication Critical patent/CN103526597A/zh
Pending legal-status Critical Current

Abstract

一种阻燃印花粘合剂，由下列重量份的原料制成：甲基丙烯酸缩水甘油酯12-14、丙烯酸甲酯9-12、三氯乙基磷酸酯6-8、聚丁烯3-4、十溴二苯醚7-9、环氧丙烯酸脂5-8、聚氨酯丙烯酸脂20-30、三乙二醇3-4、聚乙烯醇10-12、钛酸酯偶联剂TMC-TTS1-2、苄基二甲基酚聚氧乙烯醚1-2、过硫酸铵1-2、助剂4-5、水80-85。本发明使用三氯乙基磷酸酯、十溴二苯醚，使得粘合剂具有优异的阻燃效果；还具有耐水、固化膜收缩率低、耐气候、耐寒、抗静电的特点；还保留了聚氨酯树脂手感柔软的特点。

Description

一种阻燃印花粘合剂及其制备方法
技术领域
本发明属于纺织印染助剂技术领域，尤其涉及一种阻燃印花粘合剂及其制备方法。
背景技术
所谓涂料印花是借助粘合剂的作用，将不溶于水、对织物没有亲和性和反应性的颜料固着在织物上，从而达到着色的目的。据最新资料介绍，目前世界上大约有一半产量的印花织物为涂料印花。涂料印花粘合剂是涂料印花浆的主要成分，涂料印花成品质量的优劣直接受印花粘合剂性能的影响。
    目前印花粘合剂的品质不一，因粘合剂质量问题引起的印花次品率在3%以上，造成了巨大的经济损失，且印花粘合剂的质量直接影响到印花的质量、精细度、面料的档次，因此，需要研发更优质的粘合剂。
发明内容
本发明的目的在于提供一种阻燃印花粘合剂及其制备方法，该粘合剂具有阻燃的特点。
本发明的技术方案如下：
一种阻燃印花粘合剂，其特征在于由下列重量份的原料制成：甲基丙烯酸缩水甘油酯12-14、丙烯酸甲酯9-12、三氯乙基磷酸酯6-8、聚丁烯3-4、十溴二苯醚7-9、环氧丙烯酸脂5-8、聚氨酯丙烯酸脂20-30、三乙二醇3-4、聚乙烯醇10-12、钛酸酯偶联剂TMC-TTS 1-2、苄基二甲基酚聚氧乙烯醚1-2、过硫酸铵1-2、助剂4-5、水80-85；所述助剂由下列重量份的原料制成：硅烷偶联剂KH-570 2-3、交联剂 TAC1-2、苯乙烯3-4、肌醇六磷酸酯9-12、2- 氨基-2-甲基-1-丙醇1-2、新戊二醇3-4、抗氧剂1035 1-2、二甘醇7-9、乙醇12-15；制备方法是将交联剂 TAC、苯乙烯、2- 氨基-2-甲基-1-丙醇、新戊二醇、乙醇混合，加热至65-75℃，搅拌反应45-60分钟，继续升温至85-95℃，加入其它剩余成分，搅拌反应40-60分钟即得。
所述阻燃印花粘合剂的制备方法，其特征在于包括以下步骤：将甲基丙烯酸缩水甘油酯、丙烯酸甲酯、三氯乙基磷酸酯、聚丁烯、环氧丙烯酸脂、聚氨酯丙烯酸脂、三乙二醇、聚乙烯醇、钛酸酯偶联剂TMC-TTS 、苄基二甲基酚聚氧乙烯醚混合，在1000-1400转/分搅拌下，以7-9℃/分的速率加热到60-70℃；加入十溴二苯醚，以6-8℃/分的速率加热到80-90℃，加入过硫酸铵、水及其他剩余成分的混合液，继续搅拌反应2-3小时,即得。
本发明的有益效果
本发明使用三氯乙基磷酸酯、十溴二苯醚，使得粘合剂具有优异的阻燃效果；还具有耐水、固化膜收缩率低、耐气候、耐寒、抗静电的特点；还保留了聚氨酯树脂手感柔软的特点。
具体实施方式
一种阻燃印花粘合剂，由下列重量份（公斤）的原料制成：甲基丙烯酸缩水甘油酯13、丙烯酸甲酯11、三氯乙基磷酸酯7、聚丁烯3.6、十溴二苯醚8、环氧丙烯酸脂7、聚氨酯丙烯酸脂25、三乙二醇3.5、聚乙烯醇11、钛酸酯偶联剂TMC-TTS 1.5、苄基二甲基酚聚氧乙烯醚1.5、过硫酸铵1.5、助剂4.5、水83；所述助剂由下列重量份（公斤）的原料制成：硅烷偶联剂KH-570 3、交联剂 TAC1、苯乙烯3、肌醇六磷酸酯9、2- 氨基-2-甲基-1-丙醇2、新戊二醇4、抗氧剂1035 1、二甘醇7、乙醇12；制备方法是将交联剂 TAC、苯乙烯、2- 氨基-2-甲基-1-丙醇、新戊二醇、乙醇混合，加热至65-75℃，搅拌反应45-60分钟，继续升温至85-95℃，加入其它剩余成分，搅拌反应40-60分钟即得。
所述阻燃印花粘合剂的制备方法，包括以下步骤：将甲基丙烯酸缩水甘油酯、丙烯酸甲酯、三氯乙基磷酸酯、聚丁烯、环氧丙烯酸脂、聚氨酯丙烯酸脂、三乙二醇、聚乙烯醇、钛酸酯偶联剂TMC-TTS 、苄基二甲基酚聚氧乙烯醚混合，在1200转/分搅拌下，以8℃/分的速率加热到65℃；加入十溴二苯醚，以7℃/分的速率加热到85℃，加入过硫酸铵、水及其他剩余成分的混合液，继续搅拌反应2.5小时,即得。
该阻燃印花粘合剂用于印花织物，按GB标准检测，干摩擦牢度3-4级，湿摩擦牢度在3级，刷洗牢度4级，粘色牢度4级，皂洗后褪色牢度3-4级。

Claims (2)

1.一种阻燃印花粘合剂，其特征在于由下列重量份的原料制成：甲基丙烯酸缩水甘油酯12-14、丙烯酸甲酯9-12、三氯乙基磷酸酯6-8、聚丁烯3-4、十溴二苯醚7-9、环氧丙烯酸脂5-8、聚氨酯丙烯酸脂20-30、三乙二醇3-4、聚乙烯醇10-12、钛酸酯偶联剂TMC-TTS 1-2、苄基二甲基酚聚氧乙烯醚1-2、过硫酸铵1-2、助剂4-5、水80-85；所述助剂由下列重量份的原料制成：硅烷偶联剂KH-570 2-3、交联剂 TAC1-2、苯乙烯3-4、肌醇六磷酸酯9-12、2- 氨基-2-甲基-1-丙醇1-2、新戊二醇3-4、抗氧剂1035 1-2、二甘醇7-9、乙醇12-15；制备方法是将交联剂 TAC、苯乙烯、2- 氨基-2-甲基-1-丙醇、新戊二醇、乙醇混合，加热至65-75℃，搅拌反应45-60分钟，继续升温至85-95℃，加入其它剩余成分，搅拌反应40-60分钟即得。
2.根据权利要求1所述阻燃印花粘合剂的制备方法，其特征在于包括以下步骤：将甲基丙烯酸缩水甘油酯、丙烯酸甲酯、三氯乙基磷酸酯、聚丁烯、环氧丙烯酸脂、聚氨酯丙烯酸脂、三乙二醇、聚乙烯醇、钛酸酯偶联剂TMC-TTS 、苄基二甲基酚聚氧乙烯醚混合，在1000-1400转/分搅拌下，以7-9℃/分的速率加热到60-70℃；加入十溴二苯醚，以6-8℃/分的速率加热到80-90℃，加入过硫酸铵、水及其他剩余成分的混合液，继续搅拌反应2-3小时,即得。
CN201310502203.6A 2013-10-23 2013-10-23 一种阻燃印花粘合剂及其制备方法 Pending CN103526597A (zh)