CN103525096A - 一种改性纳米碳的甲基乙烯基硅橡胶电缆护套料及其制备方法 - Google Patents
一种改性纳米碳的甲基乙烯基硅橡胶电缆护套料及其制备方法 Download PDFInfo
- Publication number
- CN103525096A CN103525096A CN201310464980.6A CN201310464980A CN103525096A CN 103525096 A CN103525096 A CN 103525096A CN 201310464980 A CN201310464980 A CN 201310464980A CN 103525096 A CN103525096 A CN 103525096A
- Authority
- CN
- China
- Prior art keywords
- silicone rubber
- methyl vinyl
- vinyl silicone
- modified nano
- nano carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种改性纳米碳的甲基乙烯基硅橡胶电缆护套料及其制备方法，其组成原料为：甲基乙烯基硅橡胶、低密度聚乙烯、纳米陶土、改性纳米碳、三氧化锑、促进剂DM、2-硫醇基苯骈咪唑、乙烯基三(β-甲氧基乙氧基)硅烷、稀土稳定剂、间苯二酚、脂肪醇聚氧乙烯醚和磷酸三甲苯酯；本发明采用甲基乙烯基硅橡胶作为主料，电缆护套的抗拉强度、断裂伸长率、老化后的断裂伸长率和绝缘率具有优异的性能，而且通过对填料纳米碳的改性处理，增强电缆护套内部的连接，可以有效防止电缆护套的断裂，延迟使用寿命。
Description
技术领域
本发明涉及一种改性纳米碳的甲基乙烯基硅橡胶电缆护套料及其制备方法，属于电缆护套料制造领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视，电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，对电缆护套料的质量要求日益增加，本发明提供一种改性纳米碳的甲基乙烯基硅橡胶电缆护套料及其制备方法。
发明内容
本发明的目的在于提供一种改性纳米碳的甲基乙烯基硅橡胶电缆护套料及其制备方法。
为了实现上述目的，本发明采用如下技术方案：
改性纳米碳的甲基乙烯基硅橡胶电缆护套料，其组成原料的重量份为：甲基乙烯基硅橡胶60-65、低密度聚乙烯28-32、纳米陶土2.8-3.5、改性纳米碳13-15、三氧化锑17-23、促进剂DM3.5-4.0、2-硫醇基苯骈咪唑1.8-2.2、乙烯基三(β-甲氧基乙氧基)硅烷5.0-7.0、稀土稳定剂2.5-3.0、间苯二酚1.1-1.3、脂肪醇聚氧乙烯醚0.5-0.7和磷酸三甲苯酯1.3-1.8。
改性纳米碳的甲基乙烯基硅橡胶电缆护套料，其组成原料的重量份为：甲基乙烯基硅橡胶62、低密度聚乙烯30、纳米陶土3.2、改性纳米碳14、三氧化锑20、促进剂DM3.8、2-硫醇基苯骈咪唑2.0、乙烯基三(β-甲氧基乙氧基)硅烷6.0、稀土稳定剂2.8、间苯二酚1.2、脂肪醇聚氧乙烯醚0.6和磷酸三甲苯酯1.5。
改性纳米碳的甲基乙烯基硅橡胶电缆护套料的制备方法，包括以下步骤：
（1）改性纳米碳的制备：按组成原料的重量份称取纳米碳，然后加入8-10%大豆油，搅拌20-30分钟，然后加入纳米碳总质量0.5-0.7%的十二烷基苯磺酸钠和1.0-1.2%的铝酸酯偶联剂DL-411，搅拌1-2h后得到改性纳米碳；
（2）按组成原料的重量份称取步骤（1）的改性纳米碳和其他剩余各原料，常温下低速搅拌5-8分钟，使得混合均匀，然后在温度50-70℃混炼35-45分钟，出料。
本发明的有益效果：
本发明采用甲基乙烯基硅橡胶作为主料，电缆护套的抗拉强度、断裂伸长率、老化后的断裂伸长率和绝缘率具有优异的性能，而且通过对填料纳米碳的改性处理，增强电缆护套内部的连接，可以有效防止电缆护套的断裂，延迟使用寿命。
具体实施方式
实施例1：改性纳米碳的甲基乙烯基硅橡胶电缆护套料，其组成原料的重量份（kg）为：甲基乙烯基硅橡胶62、低密度聚乙烯30、纳米陶土3.2、改性纳米碳14、三氧化锑20、促进剂DM3.8、2-硫醇基苯骈咪唑2.0、乙烯基三(β-甲氧基乙氧基)硅烷6.0、稀土稳定剂2.8、间苯二酚1.2、脂肪醇聚氧乙烯醚0.6和磷酸三甲苯酯1.5。
改性纳米碳的甲基乙烯基硅橡胶电缆护套料的制备方法，包括以下步骤：
（1）改性纳米碳的制备：按组成原料的重量份称取纳米碳，然后加入8-10%大豆油，搅拌25分钟，然后加入纳米碳总质量0.6%的十二烷基苯磺酸钠和1.1%的铝酸酯偶联剂DL-411，搅拌1-2h后得到改性纳米碳；
（2）按组成原料的重量份称取步骤（1）的改性纳米碳和其他剩余各原料，常温下低速搅拌5-8分钟，使得混合均匀，然后在温度60℃混炼40分钟，出料。
通过本发明的实施例1制得的电缆料性能数据：
| 序号 | 项目名称 | 单位 | 测试值 |
| 1 | 抗张强度 | Mpa | 8.1 |
| 2 | 断裂伸长率 | % | 558 |
| 3 | 200℃，,240h老化后抗张强度 | Mpa | 7.24 |
| 4 | 200℃，,240h老化后断裂伸长率 | % | 518 |
| 5 | 20℃体积电阻率 | Ω·m | 8.87×1012 |
| 6 | 相对介电常数 | / | 3.17 |
| 7 | 1000℃×90min高温下绝缘电阻 | MΩ | 1.25 |
Claims (3)
1.一种改性纳米碳的甲基乙烯基硅橡胶电缆护套料，其特征在于其组成原料的重量份为：甲基乙烯基硅橡胶60-65、低密度聚乙烯28-32、纳米陶土2.8-3.5、改性纳米碳13-15、三氧化锑17-23、促进剂DM 3.5-4.0、2-硫醇基苯骈咪唑1.8-2.2、乙烯基三(β-甲氧基乙氧基)硅烷5.0-7.0、稀土稳定剂2.5-3.0、间苯二酚1.1-1.3、脂肪醇聚氧乙烯醚0.5-0.7和磷酸三甲苯酯1.3-1.8。
2.根据权利要求1所述的改性纳米碳的甲基乙烯基硅橡胶电缆护套料，其特征在于其组成原料的重量份为：甲基乙烯基硅橡胶62、低密度聚乙烯30、纳米陶土3.2、改性纳米碳14、三氧化锑20、促进剂DM 3.8、2-硫醇基苯骈咪唑2.0、乙烯基三(β-甲氧基乙氧基)硅烷6.0、稀土稳定剂2.8、间苯二酚1.2、脂肪醇聚氧乙烯醚0.6和磷酸三甲苯酯1.5。
3.一种如权利要求1所述的改性纳米碳的甲基乙烯基硅橡胶电缆护套料的制备方法，其特征在于包括以下步骤：
（1）改性纳米碳的制备：按组成原料的重量份称取纳米碳，然后加入8-10%大豆油，搅拌20-30分钟，然后加入纳米碳总质量0.5-0.7%的十二烷基苯磺酸钠和1.0-1.2%的铝酸酯偶联剂DL-411，搅拌1-2h后得到改性纳米碳；
（2）按组成原料的重量份称取步骤（1）的改性纳米碳和其他剩余各原料，常温下低速搅拌5-8分钟，使得混合均匀，然后在温度50-70℃混炼35-45分钟，出料。