CN103525072A - 一种无卤阻燃聚苯醚电缆料 - Google Patents

一种无卤阻燃聚苯醚电缆料 Download PDF

Info

Publication number
CN103525072A
CN103525072A CN201310459808.1A CN201310459808A CN103525072A CN 103525072 A CN103525072 A CN 103525072A CN 201310459808 A CN201310459808 A CN 201310459808A CN 103525072 A CN103525072 A CN 103525072A
Authority
CN
China
Prior art keywords
parts
halogen
hour
powder
retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310459808.1A
Other languages
English (en)
Other versions
CN103525072B (zh
Inventor
何成龙
何源
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Handan City Xin peak new Mstar Technology Ltd
Original Assignee
Wuhu Spaceflight Special Cable Factory Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Spaceflight Special Cable Factory Co Ltd filed Critical Wuhu Spaceflight Special Cable Factory Co Ltd
Priority to CN201310459808.1A priority Critical patent/CN103525072B/zh
Publication of CN103525072A publication Critical patent/CN103525072A/zh
Application granted granted Critical
Publication of CN103525072B publication Critical patent/CN103525072B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种无卤阻燃聚苯醚电缆料，由下列重量份的原料制成：聚苯醚40-50、POE弹性体10-15、聚丙烯10-12、三氧化钼10-15、钼酸铵8-10、抗氧剂10100.2-1、环氧大豆油10-15、甘油5-7、纳米碳化硅0.2-1、聚磷酸铵1-2、4-甲基愈创木酚1-2、PE蜡1.0-3.0、乙酰丙酮硒1-2、改性填料10-15。本发明的电缆料生产成本低，具有加工性能好、无卤、阻燃、拉伸强度高等优良性能，可广泛应用于电子线绝缘料。

Description

一种无卤阻燃聚苯醚电缆料
技术领域
本发明涉及电缆料领域，具体涉及一种无卤阻燃聚苯醚电缆料。
背景技术
随着全球经济的迅猛发展，及人类环保意识的增强，各领域对电线电缆的质量和性能的要求越来越高，因电线、电缆的老化而引发的火灾也越来越多，如何降低火灾的发生率及发生火灾的时的死亡率，低烟、无卤、阻燃、环保也成为电线电缆行业的发展方向。其中无卤低烟阻燃电缆料的需求量越来越大，目前无卤低烟阻燃电缆料的生产大多是在聚烯烃基材中加入大量的氢氧化镁或氢氧化铝来达到阻燃效果，然而，大量无机材料的加入，影响了电缆料的物理机械性能和加工工艺性能，其在常温下柔软性能、耐气候性差、耐油性、耐低温性能都不是很好。
发明内容
本发明提供了一种无卤阻燃聚苯醚电缆料。
本发明采用的技术方案为：
一种无卤阻燃聚苯醚电缆料，其特征在于：由下列重量份的原料制成：聚苯醚40-50、POE弹性体10-15、聚丙烯10-12、三氧化钼10-15、钼酸铵8-10、抗氧剂10100.2-1、环氧大豆油10-15、甘油5-7、纳米碳化硅0.2-1、聚磷酸铵1-2、4-甲基愈创木酚1-2、PE蜡1.0-3.0、乙酰丙酮硒1-2、改性填料10-15。
所述的无卤阻燃聚苯醚电缆料，其特征在于，由下列重量份的组分原料制备而得：聚苯醚45、POE弹性体12、聚丙烯11、三氧化钼13、钼酸铵9、抗氧剂10100.6、环氧大豆油13、甘油6、纳米碳化硅0.6、聚磷酸铵1、4-甲基愈创木酚1、PE蜡1.5、乙酰丙酮硒1、改性填料13。
所述的无卤阻燃聚苯醚电缆料，其特征在于，所述的改性填料是通过下列方法制备而得：
将凹凸棒土在540-580℃下煅烧3-4小时，取出后，加入3-4%的氢氧化钠溶液中研磨1-2小时，然后，加入12-15%的盐酸溶液，调节PH值为4-5，陈化10-15小时，再加氢氧化钠溶液调节研磨液pH为中性，过滤，烘干得到填料粉末，然后向所得粉末中加入相当于粉末重量1-2%的茶树精油、1-2%的氧化锌、1-2%的季戊四醇、2-3%纳米玉石粉，共同研磨1-2小时后，再加入相当于粉末重量2-3%的氨丙基三乙氧基硅烷、4-5%聚乙二醇6000、2-3%的吗啉，以11000-12000转/分的高速分散均匀，即得。
按配方比例称取各组分原料，将称取的组分原料，在高速混合机中搅拌均匀，再在130-165℃的温度区间下经密炼机密炼，双螺杆挤出，磨面热切造粒，旋风分离机送料，振动筛筛分然后包装，即制得电缆料成品。
有益效果
本发明采用聚丙烯和弹性体对聚苯醚进行改性，并且没有使用官能化聚苯醚作为相容剂，简化了材料的配比和制备，同时对填料进行改性，增加了填料的添加量，降低了生产成本，具有加工性能好、无卤、阻燃、拉伸强度高等优良性能，可广泛应用于电子线绝缘料。
具体实施方式
无卤阻燃聚苯醚电缆料，由下列重量（kg）的原料制成：
聚苯醚45、POE弹性体12、聚丙烯11、三氧化钼13、钼酸铵9、抗氧剂10100.6、环氧大豆油13、甘油6、纳米碳化硅0.6、聚磷酸铵1、4-甲基愈创木酚1、PE蜡1.5、乙酰丙酮硒1、改性填料13，
其中，改性填料是通过下列方法制备而得：
将凹凸棒土在540-580℃下煅烧3-4小时，取出后，加入3-4%的氢氧化钠溶液中研磨1-2小时，然后，加入12-15%的盐酸溶液，调节PH值为4-5，陈化10-15小时，再加氢氧化钠溶液调节研磨液pH为中性，过滤，烘干得到填料粉末，然后向所得粉末中加入相当于粉末重量1-2%的茶树精油、1-2%的氧化锌、1-2%的季戊四醇、2-3%纳米玉石粉，共同研磨1-2小时后，再加入相当于粉末重量2-3%的氨丙基三乙氧基硅烷、4-5%聚乙二醇6000、2-3%的吗啉，以11000-12000转/分的高速分散均匀，即得。
成品电缆料的制备方法：
按配方比例称取各组分原料，将称取的组分原料，在高速混合机中搅拌均匀，再在130-165℃的温度区间下经密炼机密炼，双螺杆挤出，磨面热切造粒，旋风分离机送料，振动筛筛分然后包装，即制得电缆料成品。
本实施例制得的电缆料的性能测试结果如下表：
Figure BDA0000391123470000031

Claims (3)

1.一种无卤阻燃聚苯醚电缆料，其特征在于：由下列重量份的原料制成：聚苯醚40-50、POE弹性体10-15、聚丙烯10-12、三氧化钼10-15、钼酸铵8-10、抗氧剂1010 0.2-1、环氧大豆油10-15、甘油5-7、纳米碳化硅0.2-1、 聚磷酸铵1-2、4-甲基愈创木酚1-2、PE蜡1.0-3.0、乙酰丙酮硒1-2、改性填料10-15。
2.根据权利要求1所述的无卤阻燃聚苯醚电缆料，其特征在于，由下列重量份的组分原料制备而得：聚苯醚45、POE弹性体12、聚丙烯11、三氧化钼13、钼酸铵9、抗氧剂1010  0.6、环氧大豆油13、甘油6、纳米碳化硅0.6、 聚磷酸铵1、4-甲基愈创木酚1、PE蜡1.5、乙酰丙酮硒1、改性填料13。
3.  根据权利要求1或2所述的无卤阻燃聚苯醚电缆料，其特征在于，所述的改性填料是通过下列方法制备而得： 
将凹凸棒土在540-580℃下煅烧3-4小时，取出后，加入3-4%的氢氧化钠溶液中研磨1-2小时，然后，加入12-15%的盐酸溶液，调节PH值为4-5，陈化10-15小时，再加氢氧化钠溶液调节研磨液pH为中性，过滤，烘干得到填料粉末，然后向所得粉末中加入相当于粉末重量1-2%的茶树精油、1-2%的氧化锌、1-2%的季戊四醇、2-3%纳米玉石粉，共同研磨1-2小时后，再加入相当于粉末重量2-3%的氨丙基三乙氧基硅烷、4-5%聚乙二醇6000、2-3%的吗啉，以11000-12000转/分的高速分散均匀，即得。
CN201310459808.1A 2013-09-30 2013-09-30 一种无卤阻燃聚苯醚电缆料 Active CN103525072B (zh)