CN103509497B - 一种高硬度的eva热熔胶 - Google Patents
一种高硬度的eva热熔胶 Download PDFInfo
- Publication number
- CN103509497B CN103509497B CN201310427196.8A CN201310427196A CN103509497B CN 103509497 B CN103509497 B CN 103509497B CN 201310427196 A CN201310427196 A CN 201310427196A CN 103509497 B CN103509497 B CN 103509497B
- Authority
- CN
- China
- Prior art keywords
- mixing
- composite nano
- nano powder
- melt adhesive
- high rigidity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种高硬度的EVA热熔胶,其是由下述重量份的原料制得:台聚UE630EVA 70-80,松香树脂10-15,阻燃聚酯多元醇 RAYNOLPF-1205 3-5,二异氰酸酯0.1-0.2,抗氧剂2046 0.5-1.0,光稳定剂HALS 0.4-0.6,复合纳米粉体2-4,三聚氰胺2-4、3-二乙氨基丙胺0.4-0.5,碳黑0.6-0.8,碳化硅2-6。
Description
技术领域
本发明涉及热熔胶领域,确切地说是一种高硬度的EVA热熔胶。
背景技术
热熔胶是一种可塑性的粘合剂,在一定温度范围内其物理状态随温度改变而改变,而化学特性不变,其无毒无味,属环保型化学产品。
通过掺混、接枝等办法对现有品种进行改性以提高热熔胶的性能。例如稳定剂用于防止氧化;增粘剂改善粘接强度;石蜡降低粘度改变表面性质;各种填料可提高粘度、熔点和粘接强度等。研究各种配合剂的品种、用量,并进行配方优化以满足不同需求。
发明内容
本发明的目的在于提供一种高硬度的EVA热熔胶。
上述目的通过以下方案实现:
一种高硬度的EVA热熔胶,其特征在于:其是由下述重量份的原料制得:台聚UE630EVA70-80,松香树脂10-15,阻燃聚酯多元醇RAYNOLPF-12053-5,二异氰酸酯0.1-0.2,抗氧剂20460.5-1.0,光稳定剂HALS0.4-0.6,复合纳米粉体2-4,三聚氰胺2-4、3-二乙氨基丙胺0.4-0.5,碳黑0.6-0.8,碳化硅2-6;
复合纳米粉体由下列重量份的原料制成:
凹凸棒土10-15、竹炭3-5、三氧化二锑4-7,环烷酸镁1-2,硅烷偶联剂KH5301-2,偏苯三酸三辛酯1.8-2.5、粉煤灰2-4;
复合纳米粉体的制备方法是将凹凸棒土、竹炭在800-850℃下煅烧1-2小时,取出,与粉煤灰混匀后,加入适量水中研磨,加10-15%盐酸溶液调PH为4-5,研磨浆料至600-800目后,再加氢氧化钠调为中性,喷雾干燥,所得粉末与其它剩余成分混合,研磨成纳米粉末后即得。
所述的一种高硬度的EVA热熔胶,其特征在于:
制备方法包括以下步骤:
(1)台聚UE630EVA、阻燃聚酯多元醇RAYNOLPF-1205、硅烷偶联剂KH570、三聚氰胺、抗氧剂2046按重量份混匀,于密炼机中170-185℃下混炼10-20分钟后取出冷却;
(2)再将冷却好的胶料与复合纳米粉体、松香树脂按重量份混匀,于密炼机中180-190℃下混炼10-20分钟后,取出,冷却;
(3)将步骤(2)所得冷却好的胶料与剩余原料混匀,在175-185℃下于双螺杆挤出机中,混炼、挤出、造粒,冷却后即得。
本发明的有益效果为:本发明硬度高,开放时间短,复合纳米粉体增加了本发明的强度。
具体实施方式
一种高硬度的EVA热熔胶,其是由下述重量kg的原料制得:台聚UE630EVA75,松香树脂15,阻燃聚酯多元醇RAYNOLPF-12055,二异氰酸酯0.2,抗氧剂20461.0,光稳定剂HALS0.6,复合纳米粉体2,三聚氰胺4、3-二乙氨基丙胺0.5,碳黑0.8,碳化硅4;
复合纳米粉体由下列重量kg的原料制成:
凹凸棒土15、竹炭5、三氧化二锑7,环烷酸镁2,硅烷偶联剂KH5301,偏苯三酸三辛酯2.5、粉煤灰2;
复合纳米粉体的制备方法是将凹凸棒土、竹炭在850℃下煅烧2小时,取出,与粉煤灰混匀后,加入适量水中研磨,加12%盐酸溶液调PH为4.5,研磨浆料至600目后,再加氢氧化钠调为中性,喷雾干燥,所得粉末与其它剩余成分混合,研磨成纳米粉末后即得。
所述的一种高硬度的EVA热熔胶,制备方法包括以下步骤:
(1)台聚UE630EVA、阻燃聚酯多元醇RAYNOLPF-1205、硅烷偶联剂KH570、三聚氰胺、抗氧剂2046按重量比例混匀,于密炼机中178℃下混炼20分钟后取出冷却;
(2)再将冷却好的胶料与复合纳米粉体、松香树脂按重量比例混匀,于密炼机中190℃下混炼20分钟后,取出,冷却;
(3)将步骤(2)所得冷却好的胶料与剩余原料混匀,在185℃下于双螺杆挤出机中,混炼、挤出、造粒,冷却后即得。
本实施例的粘结剂的表观粘度为5300MPa.s,剥离强度55N/2.5cm,初粘力达到5号钢球,开放时间44s,24小时热稳定性状稳定。
Claims (2)
1.一种高硬度的EVA热熔胶,其特征在于:其是由下述重量份的原料制得:台聚UE630EVA70-80,松香树脂10-15,阻燃聚酯多元醇RAYNOLPF-12053-5,二异氰酸酯0.1-0.2,抗氧剂22460.5-1.0,光稳定剂HALS0.4-0.6,复合纳米粉体2-4,三聚氰胺2-4,3-二乙氨基丙胺0.4-0.5,碳黑0.6-0.8,碳化硅2-6;
复合纳米粉体由下列重量份的原料制成:凹凸棒土10-15,竹炭3-5,三氧化二锑4-7,环烷酸镁1-2,硅烷偶联剂KH5301-2,偏苯三酸三辛酯1.8-2.5,粉煤灰2-4;
复合纳米粉体的制备方法是将凹凸棒土、竹炭在800-850℃下煅烧1-2小时,取出,与粉煤灰混匀后,加入适量水中研磨,加10-15%盐酸溶液调pH为4-5,研磨浆料至600-800目后,再加氢氧化钠调为中性,喷雾干燥,所得粉末与其它剩余成分混合,研磨成纳米粉末后即得。
2.根据权利要求1所述的一种高硬度的EVA热熔胶,其特征在于:制备方法包括以下步骤:
(1)台聚UE630EVA、阻燃聚酯多元醇RAYNOLPF-1205、硅烷偶联剂KH570、三聚氰胺、抗氧剂2246按重量份混匀,于密炼机中170-185℃下混炼10-20分钟后取出冷却;
(2)再将冷却好的胶料与复合纳米粉体、松香树脂按重量份混匀,于密炼机中180-190℃下混炼10-20分钟后,取出,冷却;
(3)将步骤(2)所得冷却好的胶料与剩余原料混匀,在175-185℃下于双螺杆挤出机中,混炼、挤出、造粒,冷却后即得。