CN103509282B - 一种具有优异性能的聚氯乙烯电缆料 - Google Patents

一种具有优异性能的聚氯乙烯电缆料 Download PDF

Info

Publication number
CN103509282B
CN103509282B CN201310405067.9A CN201310405067A CN103509282B CN 103509282 B CN103509282 B CN 103509282B CN 201310405067 A CN201310405067 A CN 201310405067A CN 103509282 B CN103509282 B CN 103509282B
Authority
CN
China
Prior art keywords
polyvinyl chloride
oxide
powder
excellent properties
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310405067.9A
Other languages
English (en)
Other versions
CN103509282A (zh
Inventor
李小康
陶天宝
吴中东
陈国林
王敏
方刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huatong Cable Group Co Ltd
Original Assignee
Anhui Huatong Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huatong Cable Group Co Ltd filed Critical Anhui Huatong Cable Group Co Ltd
Priority to CN201310405067.9A priority Critical patent/CN103509282B/zh
Publication of CN103509282A publication Critical patent/CN103509282A/zh
Application granted granted Critical
Publication of CN103509282B publication Critical patent/CN103509282B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种具有优异性能的聚氯乙烯电缆料，其是由下述重量份的原料制得：SG-4聚氯乙烯130-150、中密度聚乙烯10-15、海泡石粉10-15、磷酸三苯酯2.3-3.2、环氧油酸丁酯1-2、白炭黑0.5-1.2，氢氧化铝8-12、三氧化钼2-4、纳米碳酸钙10-20、邻苯二甲酸酯0.1-0.2、对苯二甲酸酯2-4、氧化镁1.5-3，填充料20-35。

Description

一种具有优异性能的聚氯乙烯电缆料
技术领域
本发明涉及电缆料领域，确切地说是一种具有优异性能的聚氯乙烯电缆料。
背景技术
聚氯乙烯电缆料即PVC电缆料品质的优劣，根本上是由PVC电缆料配方以及所选用的原料来决定的。随着PVC的各种助剂和填充物的不断更新和发展，也使得PVC电缆料的配方不断完善和提高。
发明内容
本发明的目的在于提供一种具有优异性能的聚氯乙烯电缆料
上述目的通过以下方案实现：
一种具有优异性能的聚氯乙烯电缆料，其特征在于：其是由下述重量份的原料制得：SG-4聚氯乙烯130-150、中密度聚乙烯10-15、海泡石粉10-15、磷酸三苯酯2.3-3.2、环氧油酸丁酯1-2、白炭黑0.5-1.2，氢氧化铝8-12、三氧化钼2-4、纳米碳酸钙10-20、邻苯二甲酸酯0.1-0.2、对苯二甲酸酯2-4、氧化镁1.5-3，填充料20-35；
所述的填充料由下列重量份的原料制成：
硅藻土20-26、石英粉2-3、纳米二氧化硅1-2，乙酰柠檬酸三乙酯2-3、氧化铝0.2-0.3，氧化镁1.3-2.5、氢氧化镁10-12、环氧亚麻油1-2、硼酸锌1-3；
所述的填充料的制备方法是将硅藻土、石英粉混匀后，在600-650℃下煅烧1-3小时，取出，与氢氧化铝一并加入适量水中研磨，加浓度为9-12％的盐酸溶液调PH为4-5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其余原料混合，三辊研磨机研磨1-2小时，混合均匀即得。,所述的一种具有优异性能的聚氯乙烯电缆料，其特征在于：
制备方法为：
(1)取SG-4聚氯乙烯、中密度聚乙烯、海泡石粉、磷酸三苯酯、环氧油酸丁酯、白炭黑、氢氧化铝、三氧化钼、纳米碳酸钙按重量份混匀，于捏合机中150-160℃下捏合6-12分钟后，取出冷却；
(2)将步骤(1)所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度在165-175℃，得到成品。
本发明的有益效果为：该电缆料具有优异的耐候性、耐寒性、耐老化性以及优异的抗氧化性。
具体实施方式
一种具有优异性能的聚氯乙烯电缆料，其是由下述重量份(kg)的原料制得：SG-4聚氯乙烯139、中密度聚乙烯15、海泡石粉15、磷酸三苯酯2.3、环氧油酸丁酯1、白炭黑0.8，氢氧化铝12、三氧化钼2、纳米碳酸钙20、邻苯二甲酸酯0.2、对苯二甲酸酯2、氧化镁3，填充料20；
所述的填充料由下列重量份的原料制成：
硅藻土25、石英粉2.3、纳米二氧化硅2，乙酰柠檬酸三乙酯3、氧化铝0.3，氧化镁1.8、氢氧化镁12、环氧亚麻油1.2、硼酸锌3；
所述的填充料的制备方法是将硅藻土、石英粉混匀后，在630℃下煅烧2小时，取出，与氢氧化铝一并加入适量水中研磨，加浓度为12％的盐酸溶液调PH为4，研磨浆料至500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其余原料混合，三辊研磨机研磨2小时，混合均匀即得。
所述的一种具有优异性能的聚氯乙烯电缆料，制备方法为：
(1)取SG-4聚氯乙烯、中密度聚乙烯、海泡石粉、磷酸三苯酯、环氧油酸丁酯、白炭黑、氢氧化铝、三氧化钼、纳米碳酸钙按重量份混匀，于捏合机中158℃下捏合8分钟后，取出冷却；
(2)将步骤(1)所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度在168℃，得到成品。
将本实施例进行性能测试，所得数据如下：
从本实施例测试结果可见，本发明的产品经过100℃×168h的老化和80℃×6h高温压力试验，其机械物理性能变化符合相应标注要求，具有良好的物理机械性能，满足不同温度环境变化的需求。

Claims (2)

1.一种具有优异性能的聚氯乙烯电缆料，其特征在于：其是由下述重量份的原料制得：SG-4聚氯乙烯130-150、中密度聚乙烯10-15、海泡石粉10-15、磷酸三苯酯2.3-3.2、环氧油酸丁酯1-2、白炭黑0.5-1.2，氢氧化铝8-12、三氧化钼2-4、纳米碳酸钙10-20、邻苯二甲酸酯0.1-0.2、对苯二甲酸酯2-4、氧化镁1.5-3，填充料20-35；所述的填充料由下列重量份的原料制成：硅藻土20-26、石英粉2-3、纳米二氧化硅1-2，乙酰柠檬酸三乙酯2-3、氧化铝0.2-0.3，氧化镁1.3-2.5、氢氧化镁10-12、环氧亚麻油1-2、硼酸锌1-3；所述的填充料的制备方法是将硅藻土、石英粉混匀后，在600-650℃下煅烧1-3小时，取出，与氢氧化铝一并加入适量水中研磨，加浓度为9-12%的盐酸溶液调pH为4-5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其余原料混合，三辊研磨机研磨1-2小时，混合均匀即得。
2.根据权利要求1所述的一种具有优异性能的聚氯乙烯电缆料，其特征在于：制备方法为：
（1）取SG-4聚氯乙烯、中密度聚乙烯、海泡石粉、磷酸三苯酯、环氧油酸丁酯、白炭黑、氢氧化铝、三氧化钼、纳米碳酸钙按重量份混匀，于捏合机中150-160℃下捏合6-12分钟后，取出冷却；
（2）将步骤（1）所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度在165-175℃，得到成品。
CN201310405067.9A 2013-09-06 2013-09-06 一种具有优异性能的聚氯乙烯电缆料 Active CN103509282B (zh)