CN103506564A - 一种高铝粉铸造涂料 - Google Patents
一种高铝粉铸造涂料 Download PDFInfo
- Publication number
- CN103506564A CN103506564A CN201310448762.3A CN201310448762A CN103506564A CN 103506564 A CN103506564 A CN 103506564A CN 201310448762 A CN201310448762 A CN 201310448762A CN 103506564 A CN103506564 A CN 103506564A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminum powder
- high aluminum
- casting coating
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高铝粉铸造涂料,包括有按重量份计的以下组分:甲醇25-30份,丙烯酸酯10-18份,高铝粉40-65份,铜粉5-8份,酚醛树脂1-2份,锂基膨润土1-2份,聚乙烯醇缩丁醛0.05-0.08份,脂肪醇聚氧乙烯醚0.3-0.5份。本发明的有益效果为:本发明提供的一种高铝粉铸造涂料,化学稳定性强,不易变性,同时,其粘度远低于现有产品,不会对物料产生沾粘,能够保证铸造型腔或砂芯的表面完整性,提高了产品的光滑程度。
Description
技术领域
本发明涉及铸造领域,具体涉及一种高铝粉铸造涂料。
背景技术
铸造用涂料是指用来涂敷在型腔或砂芯表面,以改变其表面耐火度、化学稳定性、抗金属冲刷性、抗粘砂性等性能的铸造辅助材料。传统的铸造涂料,其化学稳定性不强,粘度高,在生产中容易沾粘物料,不适于大规模的工业化生产。
发明内容
本发明的目的就是针对上述现有技术中的缺陷,提供了一种化学稳定性强,粘度低的高铝粉铸造涂料。
为了实现上述目的,本发明提供的技术方案为:一种高铝粉铸造涂料,包括有按重量份计的以下组分:甲醇25-30份,丙烯酸酯10-18份,高铝粉40-65份,铜粉5-8份,酚醛树脂1-2份,锂基膨润土1-2份,聚乙烯醇缩丁醛0.05-0.08份,脂肪醇聚氧乙烯醚0.3-0.5份。
进一步的,上述的一种高铝粉铸造涂料,包括有按重量份计的以下组分:甲醇28.5份,丙烯酸酯16.5份,高铝粉58.5份,铜粉7份,酚醛树脂1.6份,锂基膨润土1.6份,聚乙烯醇缩丁醛0.05份,脂肪醇聚氧乙烯醚0.4份。
本发明的有益效果为:本发明提供的一种高铝粉铸造涂料,化学稳定性强,不易变性,同时,其粘度远低于现有产品,不会对物料产生沾粘,能够保证铸造型腔或砂芯的表面完整性,提高了产品的光滑程度。
具体实施方式
实施例1:
一种高铝粉铸造涂料,包括有以下组分:甲醇25公斤,丙烯酸酯10公斤,高铝粉40公斤,铜粉5公斤,酚醛树脂1公斤,锂基膨润土1公斤,聚乙烯醇缩丁醛0.05公斤,脂肪醇聚氧乙烯醚0.3公斤。
实施例2:
一种高铝粉铸造涂料,包括有以下组分:甲醇30公斤,丙烯酸酯18公斤,高铝粉65公斤,铜粉8公斤,酚醛树脂2公斤,锂基膨润土2公斤,聚乙烯醇缩丁醛0.08公斤,脂肪醇聚氧乙烯醚0.5公斤。
实施例3:
一种高铝粉铸造涂料,包括有以下组分:甲醇28.5公斤,丙烯酸酯16.5公斤,高铝粉58.5公斤,铜粉7公斤,酚醛树脂1.6公斤,锂基膨润土1.6公斤,聚乙烯醇缩丁醛0.05公斤,脂肪醇聚氧乙烯醚0.4公斤。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (2)
1.一种高铝粉铸造涂料,其特征在于,包括有按重量份计的以下组分:甲醇25-30份,丙烯酸酯10-18份,高铝粉40-65份,铜粉5-8份,酚醛树脂1-2份,锂基膨润土1-2份,聚乙烯醇缩丁醛0.05-0.08份,脂肪醇聚氧乙烯醚0.3-0.5份。
2.根据权利要求1所述的一种高铝粉铸造涂料,其特征在于,包括有按重量份计的以下组分:甲醇28.5份,丙烯酸酯16.5份,高铝粉58.5份,铜粉7份,酚醛树脂1.6份,锂基膨润土1.6份,聚乙烯醇缩丁醛0.05份,脂肪醇聚氧乙烯醚0.4份。